Pengaruh Variasi Waktu Dan Suhu Pencampuran Serta Suhupengeringan Pada Lembar Katoda LiFePO4 Terhadap Kapasitasbaterai Ion Lithium

PENGARUH VARIASI WAKTU DAN SUHU PENCAMPURAN
SERTA SUHU PENGERINGAN PADA LEMBAR KATODA LiFePO 4
TERHADAP KAPASITAS BATERAI ION LITHIUM

ABSTRAK

Telah dilakukan penelitian pembuatan baterai coin dengan variasi suhu dan waku
pencampuran pada slurry katoda LiFePO 4 serta variasi suhu pengeringan lembar
katoda LiFePO 4 . Material katoda merupakan campuran dari LiFePO 4 : Super P :
PVDF dengan komposisi 85 : 10 : 5 dan DMAC 20 mL. Waktu dan suhu
pencampuran divariasikan yaitu 3, 5 dan 7 jam pada suhu 29˚C dan 29, 50 dan 60˚C
selama 3 jam dan variasi suhu pengeringan 80, 100 dan˚C120
selama 5 jam.
Lembaran katoda dibuat dengan menggunakan doctor blade. Pengujian
karakteristik serbuk LiFePO 4 dengan XRD, mikroskop optik dan SEM-EDX untuk
melihat morfologi lembaran katoda LiFePO 4 dan pengujian kapasitas discharge
dengan charge/discharge. Hasil analisis menunjukkan bahwa variasi waktu
pencampuran yang memiliki kapasitas tertinggi adalah sampel 7 jam yaitu 3,74
mAh/g. Sementara pada variasi suhu pencampuran, kapasitas tertinggi terdapat
pada sampel 50
˚C yaitu 5,81 mAh/g. Pada variasi suhu pengeringan kapasitas

tertinggi terdapat pada sampel 80˚C yaitu 5,70 mAh/g.
Kata kunci : Baterai ion lithium, Lembar katoda, LiFePO 4 , Kapasitas
discharge

Universitas Sumatera Utara

THE EFFECT OF TIME VARIATION, MIXING TEMPERATURE AND
DRYING TEMPERATURE ON LiFePO 4 CATHODE SHEETS OF
LITHIUM ION BATTERIES CAPACITY

ABSTRAC

A research on the fabrication of coin battery with the variation of mixing time and
temperature at slurry cathode LiFePO 4 and variation of drying temperature at
cathode sheets. The material of cathode was using a powder of LiFePO 4 : Super P :
PVDF with composition 85 : 10 : 5 and 20 mL of DMAC. The mixing time was
varied at 3, 5, 7 hour at 29˚C and the mixing temperature was varied at 29, 50, 60˚C
for 3 hour and the drying temperature was varied of 80, 100, 120˚C for 5 hour. The
sheets of cathode are made by using doctor blade process. The powder of LiFePO 4
was analyzed by XRD. Morphology of the LiFePO 4 cathode sheets was analyzed

by Microscope Optic and SEM. Discharge capacity was analyzed by
charge/discharge. The result of this research showed that the variation of mixing
time has the highest capacity at 7 hour-sampel is 3,75 mAh/g. Meanwhile, the
variation of mixing temperature has the highest capacity at˚C
50sampel is 5,81
mAh/g. The variation of drying temperature has the highest capacity at 80
˚C
sampel is 5,70 mAh/g.
Key word : Lithium ion battery, Cathode sheets, LiFePO 4 , Discharge capacity.

Universitas Sumatera Utara