Modifikasi Silika Gel dengan Tembaga(II) Klorida Sebagai Desikan - UNS Institutional Repository

  

MODIFIKASI SILIKA GEL

DENGAN TEMBAGA(II) KLORIDA SEBAGAI DESIKAN

Disusun oleh:

  

ALIKA NURAINTI

M0313007

SKRIPSI

Diajukan untuk memenuhi sebagian persyaratan mendapatkan gelar

Sarjana Sains dalam Bidang Ilmu Kimia

  

FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM

UNIVERSITAS SEBELAS MARET

SURAKARTA

Maret 2018

  

HALAMAN PENGESAHAN

SKRIPSI

MODIFIKASI SILIKA GEL

DENGAN TEMBAGA(II) KLORIDA SEBAGAI DESIKAN

ALIKA NURAINTI

  

M0313007

  Skripsi ini dibimbing oleh: Pembimbing I Pembimbing II

  Dr. Dian Maruto Widjonarko, M.Si. Dr. Sayekti Wahyuningsih, M.Si NIP. 19700330 200003 1001 NIP. 19711211 199702 2001

  Dipertahankan di depan Tim Penguji Skripsi pada: Hari : Rabu Tanggal : 28 Maret 2018

  Anggota Tim Penguji : 1. Dr. Khoirina Dwi Nugrahaningtyas,M.Si. 1. .................................

  NIP 19740419 200003 2001 2. Dr.rer.nat. Atmanto Heru Wibowo,M.Si. 2. ................................. NIP 19740813 200003 1001

  Disahkan Oleh Kepala Program Studi S1 Kimia

  Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Sebelas Maret Surakarta

  Dr. Triana Kusumaningsih, M.Si.

  NIP. 19730124 199903 2001

  

PERNYATAAN

  Dengan ini saya menyatakan bahwa skripsi saya yang berjudul “MODIFIKASI SILIKA GEL DENGAN TEMBAGA(II) KLORIDA SEBAGAI DESIKAN

  ” belum pernah diajukan untuk memperoleh gelar kesarjanaan di suatu perguruan tinggi dan sepanjang pengetahuan saya juga belum pernah ditulis atau dipublikasikan oleh orang lain, kecuali yang secara tertulis diacu dalam naskah ini dan disebutkan dalam daftar pustaka.

  Surakarta, 6 Maret 2018 ALIKA NURAINTI

  

MODIFIKASI SILIKA GEL

DENGAN TEMBAGA(II) KLORIDA SEBAGAI DESIKAN

ALIKA NURAINTI

  Program Studi Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam, Universitas Sebelas Maret, Jl. Ir. Sutami 36A, Surakarta 57126

  

ABSTRAK

  Telah dilakukan modifikasi silika gel dengan tembaga(II) klorida sebagai desikan. Penelitian ini bertujuan untuk mempelajari pengaruh tembaga(II) klorida pada karakter kimia dan fisik silika gel hasil modifikasi. Modifikasi dilakukan dengan merendam hidrogel pada larutan tembaga(II) klorida dengan konsentrasi 0,1M; 0,3M; 0,5M dan 0,8M kemudian dikeringkan pada suhu 105 ºC selama 6 jam. Material hasil modifikasi dikarakterisasi dengan X-Ray Diffraction (XRD),

  

Fourier Transform Infra Red (FTIR), Scanning Electron Microscopy-Energy

Dispersive X-ray (SEM-EDX), Surface Area Analyzer (SAA), Thermo

Gravimetry /Differential Thermal Analysis (TG/DTA), Spektrofotometer UV-

Visible dan kemampuan adsorpsinya terhadap kelembaban dengan metode

  gravimetri.

  Hasil penelitian menunjukkan bahwa modifikasi silika gel dengan tembaga(II) klorida berhasil dibuat. Silika bersifat amorf ditunjukkan dengan puncak difraksi utama pada 2θ: 23,715º. Kerangka silanol dan siloksan ditunjukkan oleh vibrasi Si-OH dan Si-O-Si pada bilangan gelombang 3443,08

• 1 -1

  cm dan 469,69 cm yang diperkuat dengan kandungan Si: 41,40% dan O: 58,60%. Penambahan tembaga(II) klorida menurunkan luas permukaan dan volume pori total serta meningkatkan nilai kapasitas adsorpsi kelembaban. Silika gel hasil modifikasi dengan konsentrasi tembaga(II) klorida 0,5M memiliki luas

  2

  permukaan sebesar 99,711 m /g, volume pori 0,292 cc/g serta nilai kapasitas adsorpsi kelembaban sebesar 110,86%. Kata kunci: silika gel, silika gel-Cu, indikator kelembaban

  

MODIFICATION OF SILICA GEL

WITH COPPER(II) CHLORIDE AS A DESSICANT

ALIKA NURAINTI

  Department of Chemsitry, Faculty of Mathematics and Natural Science, Sebelas Maret University, Jl. Ir. Sutami 36A, Surakarta 57126

  

ABSTRACT

  Modification of silica gel with copper(II) chloride as a dessicant has been conducted. This research aims to investigate the effect of indicator copper(II) chloride on chemical and physical character of modified silica gel. The modification was conducted by immersing the hydrogel in copper(II) chloride solution with concentration 0,1M; 0,3M; 0,5M and 0,8M then dried at 105 ºC for 6 hours. The modified materials was analyzed by X-Ray Diffraction (XRD), Fourier Transform Infra Red (FTIR), Scanning Electron Microscopy-Energy Dispersive X-ray (SEM-EDX), Surface Area Analyzer (SAA), Thermo Gravimetry / Differential Thermal Analysis TG / DTA), UV-Visible Spectrophotometer and adsorption ability against moisture by gravimetric method.

  The result shows that the modification of silica gel with copper(II) chloride was successfully made. Silica is amorphous with the main diffraction peak at (2θ) 23.715º. Silanol and siloxane structure is represented by Si-OH and

• 1 -1

  Si-O-Si vibration at the wave number of 3443.08 cm and 469.69 cm reinforced by Si content: 41.40% and O: 58.60%. The addition of copper(II) chloride decreases surface area and pore volume along increase. Modified silica gel with a

  2

  concentration of copper(II) chloride 0.5M have surface area 99.711 m /g, pore volume 0.292 cc/g and humidity adsorption capacity 110.86%. Keywords: silica gel, silica gel-Cu, humidity indicator

  

MOTTO

“ Dan apa yang disisi Allah adalah lebih baik”

  

(Q.S. Ali Imran : 198)

“Allah tidak membebani seseorang melainkan sesuai dengan kadar

kesanggupannya”

  (Q.S. Al-Baqarah: 286)

  PERSEMBAHAN Karya ini kupersembahkan untuk : Ayah yang telah meninggalkanku, Ibu dan Adikku yang telah memberikan do’a, kasih sayang dan motivasinya hingga saat ini Sahabat-sahabatku yang selalu mendukung dan mendengarkan segala keluh kesahku selama kuliah, Ika, Dwi, Intan, Khofifah, Fitri, Nana, Anis, Septi, Maya

Teman-teman Grup Riset, Intan, Maya, Arika, Yuli, Khilyatin, Salma, Yuliana, Vanani

  Teman-teman Kimia 2013

KATA PENGANTAR

  Puji syukur penulis panjatkan kehadirat Allah SWT atas nikmat iman, sehat, kesempatan, serta ilmu pengetahuan yang telah diberikan kepada penulis sehingga skripsi ini dapat terselesaikan. Penelitian skripsi yang berjudul “Modifikasi Silika Gel dengan Tembaga(II) Klorida Sebagai Desikan” ini tidak akan selesai tanpa bantuan dari berbagai pihak. Oleh sebab itu, penulis mengucapkan terimakasih sebesar-besarnya kepada: 1.

  Dr. Triana Kusumaningsih, M.Si selaku Kepala Prodi Kimia FMIPA UNS 2. Dr. Dian Maruto Widjonarko, M.Si selaku Pembimbing 1 3. Dr. Sayekti Wahyuningsih, M.Si selaku Pembimbing 2 4. Dr. Khoirina Dwi Nugrahaningtyas, M.Si selaku Pembimbing Akademik 5. Bapak dan Ibu dosen dan seluruh staf Program Studi Kimia FMIPA UNS 6. Ibu, Ayah, dan adikku yang selalu memberikan dukungan dan doa bagi penulis

7. Teman-teman Kimia 2013 8.

  Semua pihak yang penulis tidak bisa sebutkan satu persatu.

  Penulis menyadari bahwa banyak kekurangan dalam penulisan skripsi ini. Oleh karena itu, penulis mengharapkan kritik dan saran untuk menyempurnakannya. Namun demikian, penulis berharap semoga skripsi ini bermanfaat bagi pembaca.

  Surakarta, Maret 2018 Alika Nurainti

  

DAFTAR ISI

  

  BAB I

  

  

  

  

  

  BAB II

  

  

  

  

  BAB III

  

  

  

  

  

  

  

  

  BAB I

  

  

  

  

  BAB

  

DAFTAR TABEL

  

  

  

  

  

  

DAFTAR GAMBAR