ADSORPSI ZAT WARNA REMAZOL BRILLIANT BLUE R DENGAN MONTMORILLONIT TERMODIFIKASI AMINOSILAN

  

SKRIPSI

ADSORPSI ZAT WARNA REMAZOL BRILLIANT BLUE R

DENGAN MONTMORILLONIT TERMODIFIKASI

AMINOSILAN

Disusun Oleh :

BAGUS TAUFIQ ARDIANTO M0311016 SKRIPSI

  

Diajukan untuk memenuhi sebagian persyaratan mendapatkan gelar

Sarjana Sains dalam bidang ilmu kimia

FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM

UNIVERSITAS SEBELAS MARET

SURAKARTA

  

Agustus 2017

  

SKRIPSI

HALAMAN JUDUL

ADSORPSI ZAT WARNA REMAZOL BRILLIANT BLUE R

DEGAN MONTMORILLONIT TERMODIFIKASI

AMINOSILAN

Disusun Oleh :

BAGUS TAUFIQ ARDIANTO

  

M0311016

SKRIPSI

Diajukan untuk memenuhi sebagian persyaratan mendapatkan gelar

Sarjana Sains dalam bidang ilmu kimia

  

UNIVERSITAS SEBELAS MARET

SURAKARTA

2017

  PERNYATAAN

  Dengan ini saya menyatakan bahwa skripsi saya yang berjudul “ADSORPSI ZAT WARNA REMAZOL BRILLIANT BLUE R DENGAN MONTMORILLONIT TERMODIFIKASI AMINOSILAN ” belum pernah diajukan untuk memperoleh gelar kesarjanaan di suatu perguruan tinggi, dan sepanjang pengetahuan saya juga belum pernah ditulis atau dipublikasikan oleh orang lain, kecuali yang secara tertulis diacu dalam naskah ini dan disebutkan dalam daftar pustaka.

  Surakarta, Agustus 2017 BAGUS TAUFIQ ARDIANTO

  

ADSORPSI ZAT WARNA REMAZOL BRILLIANT BLUE R DENGAN

MONTMORILLONIT TERMODIFIKASI AMINOSILAN

BAGUS TAUFIQ ARDIANTO

  Program Studi Kimia, Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Sebelas Maret

  ABSTRAK

  Telah dilakukan modifikasi lempung montmorillonit dengan senyawa aminosilan sebagai adsorben zat warna Remazol brilliant blue r. Tujuan penelitian ini adalah mengetahui perubahan karakter montmorillonit termodifikasi aminosilan serta adsorpsinya terhadap zat warna Remazol brilliant blue r. Senyawa aminosilan disintesis melalui aminolisis GPTMS dengan etilen diamin dengan perbandingan 1:5 mol/mol. Modifikasi montmorillonit dilakukan dalam medium toluena selama 24 jam menggunakan proses refluks. Karakterisasi montmorillonit dan montmorillonit termodifikasi aminosilan dilakukan dengan

  XRD, FTIR, SAA, SEM-EDX dan TGA. Konsentrasi zat warna Remazol brilliant blue r diuji dengan spektrofotometer UV-Vis.

  Difraktogram XRD montmorillonit termodifikasi aminosilan menunjukkan perbedaan dengan difraktogram montmorillonit yang ditandai dengan munculnya puncak baru pada 2

  θ = 23,70° serta kenaikan intensitas pada 2θ = 26,36°. Analisis gugus fungsi montmorillonit termodifikasi aminosilan dengan FTIR menunjukkan adanya perbedaan serapan dengan serapan montmorillonit yang ditandai dengan

• 1

  munculnya serapan gugus –CH

  2 asimetris dan simetris pada 2937,71 cm dan

• 1

  2873,09 cm . Analisis luas permukaan dengan SAA menunjukkan adanya penurunan luas permukaan pada montmorillonit termodifikasi aminosilan, yaitu

  2

  2

  dari 208,4 m /g menjadi 26,54 m /g. Morfologi permukaan montmorillonit termodifikasi aminosilan lebih halus dari montmorillonit serta terdapatnya atom karbon (C) dan nitrogen (N) pada montmorillonit termodifikasi aminosilan. Hasil analisis dengan TGA menunjukkan bahwa montmorillonit termodifikasi aminosilan mempunyai suhu dekomposisi lebih tinggi dari pada montmorillonit. Kondisi optimum adsorpsi zat warna Remazol brilliant blue r oleh montmorillonit termodifikasi aminosilan adalah pada pH 3 dan waktu kontak 20 menit dengan kapasitas adsorpsi sebesar 57,40 (mg/g). Jenis isoterm adsorpsi zat warna Remazol oleh montmorillonit termodifikasi aminosilan mengikuti

  brilliant blue r persamaan isoterm adsorpsi Langmuir.

  Kata Kunci : Adsorpsi, Montmorillonit, Aminosilan, Remazol brilliant blue r

  ADSORPTION OF REMAZOL BRILLIANT BLUE R DYE ON

AMINOSILANE-MODIFIED MONTMORILLONITE

BAGUS TAUFIQ ARDIANTO

  Department of Chemistry, Faculty of Mathematics and Natural Science Sebelas Maret University

  ABSTRACT

  The modification of montmorillonite clay surface with aminosilane as

  

Remazol brilliant blue r dye's adsorbent has been conducted. This study aimed to

  deterimine the character changes of aminosilane-modified montmorillonite and its adsorption to Remazol brilliant blue r dye. The aminosilane compounds were synthesized through a GPTMS aminolysis process with ethylenediamine in the ratio of 1:5 mol/mol. The modification of montmorillonite was perfomed in toluene for 24 hours using reflux process. Montmorillonite and aminosilane- modified montmorillonite were characterized using XRD, FTIR, SAA, SEM-EDX and TGA. Remazol brilliant blue r concentration was examinated using UV-Vis spectrophotometer.

  Difractrogram of aminosilane-modified montmorillonite showed difference from difractrogram of montmorillonite by appearance of a new peak at

  o o

  and the increasing . Functional group analysis 2θ = 23.70 intensity at 2θ = 26.36 of aminosilane-modified montmorillonite using FTIR showed difference from montmorillonite, marked by appearance the asymmetry and symmetry –CH

  2

• 1 -1

  functional group at 2937,71 cm and 2873,09 cm . The result of SAA analysis revealed surface area of aminosilane-modified montmorillonite decreased from

  2

  2

  208,4 m /g to 26,54 m /g. Compared to montmorillonite, morphology of aminosilane-modified montmorillonite surface is smoother than montmorillite. Besides that, carbon and nitrogen atoms were found on aminosilane-modified montmorillonite surface. The result of TGA analysis revealed that aminosilane- modified montmorillonite has higher thermal decomposition than montmorillonite. The optimum adsorption of Remazol brilliant blue r dye using aminosilane-modified montmorillonit was obtained on pH 3 and contact time at 20 minutes with 57,40 (mg/g) adsorption capacity. The type of adsorption for

  

Remazol brilliant blue r by aminosilane-modified montmorillonit was obtained

using Langmuir isotherm.

  Keywords : Adsorption, Montmorillonite, Aminosilane, Remazol brilliant blue r

  

MOTTO

  “Sometimes life hits you in the head with a brick. Don’t lose faith” (Steve Jobs)

  “Tell me and I forget. Teach me and I remember. Involve me and I learn” (Benjamin Franklin)

  “Maka nikmat Tuhanmu yang manakah yang kau dustakan” (Q.S : Ar rahman ayat 13)

  “Hai orang-orang yang beriman, bersabarlah kamu dan kuatkanlah kesabaranmu dan tetaplah bersiap si aga dan bertaqwalah kepada ALLAH agar kamu menang”

  (Q.S : Ali Imraan ayat 200)

  

PERSEMBAHAN

  skripsi ini penulis persembahkan untuk : Ibu, bapak, kakak tercinta serta teman penulis ozi adi saputra yang tak pernah lelah mendoakan, memberikan motivasi dan semangat yang tak pernah luntur. Teman-teman kimia 2011

  Hamba-hamba Allah yang menjadikan ilmu sebagai sarana mendekatkan diri kepada Rabbnya. Alhamdulillah, puji syukur kehadirat Allah SWT yang telah memberikan rahmat dan hidayahNya, sehingga penulis dapat menyelesaikan penulisan skripsi yang berjudul “ADSORPSI ZAT WARNA REMAZOL BRILLIANT BLUE R DENGAN MONTMORILLONIT TERMODIFIKASI AMINOSILAN

  ”. Sholawat dan salam senantiasa penulis haturkan kepada Rasulullah SAW sebagai pembimbing seluruh umat manusia.

  Skripsi ini tidak akan selesai tanpa adanya bantuan dari banyak pihak, karena itu penulis menyampaikan terima kasih kepada :

  1. Ibu Dr.Triana Kusumaningsih, M.Si selaku Kepala Prodi Kimia Fakultas Matematika dan Ilmu Pengetahuan Alam UNS.

  2. Bapak Candra Purnawan, M.Sc selaku pembimbing I yang telah memberikan bimbingan, pengarahan dan ilmu yang bermanfaat.

  3. Ibu Dr.rer.nat Witri Wahyu Lestari, M.Sc selaku pembimbing II dan Pembimbing Akademik yang telah memberikan bimbingan, pengarahan dan ilmu yang bermanfaat.

  4. Bapak-Ibu dosen yang sabar memberikan ilmu.

  5. Ibu, Bapak dan Kakak yang telah memberikan doa, dukungan dan kasih sayang.

  6. Sahabat-sahabatku tercinta Ozi, Karima, Heri, Taufik, Ichsan, Ardian, Aji, Artha, Rahmat, Khusnan, Ferdinand yang selalu memberikan motivasi.

  7. Teman–teman kimia 2011 yang telah menorehkan kenangan indah semasa kuliah.

  8. Teman–teman BEM FMIPA Kabinet Optimis Mas Wachid, Mas Wawan, Sofi, Miki, Afi, Tyas, Istiqomah, Sefti, Linda, Pandu, Eka, Adam, Fafa, JES, Tito, Hanif dan lainnya yang telah memberikan pembelajaran dan pengalaman berharga selama berorganisasi.

  9. Teman–teman BEM FMIPA Kabinet Positif Bersatu Aisyah, Ayu, Fifi, Yulianto, Rara, Anggit, Jakiyah, Lau, Lila, Afifah, Barep, Fahri dan lainnya yang telah memberikan pembelajaran dan pengalaman berharga selama berorganisasi.

  10. Kakak dan adik tingkat atas semangat, dukungan dan doanya.

  11. Semua pihak yang tidak dapat penulis sebutkan satu persatu. Semoga Allah SWT membalas jerih payah dan pengorbanan yang telah diberikan dengan balasan yang lebih baik. Amin.

  Penulis menyadari bahwa penyusunan skripsi ini masih banyak terdapat kekurangan dan keterbatasan, sehingga hasilnya masih jauh dari sempurna, Untuk itu, demi kesempurnaan skripsi ini penulis mengharapkan kritikan dan saran yang bersifat membangun dari pembaca.

  Surakarta, Agustus 2017 Penulis

  DAFTAR ISI

  Halaman DAFTAR LAMPIRAN ........................................................................................ xvi DAFTAR SINGKATAN .................................................................................... xvii

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

  

DAFTAR TABEL

  Halaman

  

  

  DAFTAR GAMBAR

  Halaman