11
CHAPTER III
BASIC THEORY
3.1. Geopolymer Concrete
Geopolymer concrete is concrete which uses different materials and are environmental friendly during the production process. There are several
advantages of the materials; such as anti-fire, used as a cover material for the exterior of mechanical equipment, durable and environment friendly.
Geopolymer concrete was established by Joseph Davidovits in 1970. At that time, Davidovits investigated the materials which were in the pyramid. He found
that the cement used in the pyramid consist of several different materials. At that time it was called geopolymer, which was obtained from fly ash as a result of
geo-polymerization reaction mix with NaOH, KOH and so on. In the process of geopolymer, there is a chemical reaction between alumina-silicate oxide Si
2
O
5
, Al
2
O
2
with alkali poly-silicates which produces Si-O-Al bonds. Poly-silicate is generally in the form of sodium or potassium silicate obtained from the chemical
industry or fine silica powder as a byproduct of the process ferro-silicon metallurgy. From the reactions that mix together in the geopolymer, there will be
H
2
O or water that has been released.
12
From the equation, it can be shown that the chemical reaction of compound formation geopolymer also produces water that will be removed during the
curing process. Davidovits, 1999; Hardjito Rangan, 2005 Actually, geopolymer concrete can be produced no only from fly ash but
geopolymer can be also produced with silica and materials rich in alumina. Several studies have reported the use of geopolymer in concrete is beneficial.
Most of the studies investigated the use of alkali activators containing sodium hydroxide and sodium silicate; or potassium hydroxide and potassium silicate.
Different with the material that is used above, Cheng and Chiu 2003 reported the production of geopolymer concrete using slag and metakaolin with
potassium hydroxide and sodium silicate as the alkaline medium. Some of people using fly ash as a material in geopolymers with sodium hydroxide and sodium
silicate as well as with potassium hydroxide with potassium silicate combinations. The results from the studies show that the formation of
geopolymer is excellent. It can be noted that the presence of calcium content in fly ash, played a significant role in compressive strength development. The
addition of calcium ions, provide a faster reaction and thus produces good hardening of geopolymer in shorter curing time.
“Polymers a
re sensitive towards heat and can form a stronger chain due to polycondensation. It is noted from the basic chemical reaction when subjected to
heat causes silicon and aluminium hydroxide molecules to polycondense or
13
polymerizes, to form rigid chains or ne
ts of oxygen bonded tetrahedra.” Hindawi, 2013
Davidovits 1988 reported that geopolymer can harden rapidly at room temperature and can gain the compressive strength up to 20 MPa. Geopolymer
cement was discovered to be acid resistant, because, unlike the Portland cement, geopolymer cements does not depend on lime and are not dissolved by acidic
solutions.
3.2. Metakaolin