Variasi Kadar Perekat Phenol Formaldehida Terhadap Kualitas Papan Partikel Dari Campuran Partikel Kelapa Sawit dan Serutan Meranti
Lampiran 1. Perhitungan bahan baku papan partikel
Kadar perekat phenol formaldehida (PF) = 8%, 10%, 12%, 14%, dan 16%
Ukuran sampel = 25 x 25 x 1 cm
Kerapatan target = 0,7 g/cm3
Solid content phenol formaldehida = 43%
A. Kadar perekat phenol formaldehida (PF) = 8%
∑ partikel =(25 x 25 x 1)x 0,7 x
= 405,1 + 40,51 = 445,599
g (KA 0%)
KA 5% = 445,6 + 5% (445,6) = 467,88g (kebutuhan bahan baku
akhir)
Kadar perekat = 8% x 467,88 = 37,43 g
Kadar perekat akhir = 37,43 x
= 87,04 + (10% spilasi) = 95,74 g
B. Kadar perekat phenol formaldehida (PF) = 10%
∑ partikel = (25 x 25 x 1) x 0,7 x
= 397,727 + 39,77 = 437,497 g
KA 5% = 437,497 + 5% (437,497) = 459,37 g
Kadar perekat = 10% x 459,37 = 45,937 g
Kadar perekat akhir = 45,937 x
= 106,83 + 10,683 = 117,513 g
C. Kadar perekat phenol formaldehida (PF) = 12%
∑ partikel = (25 x 25 x 1)x 0,7 x
= 390,62 + 39,06 = 429,68 g
KA 5% = 429,68 + 5% (429,68) = 451,164 g
Kadar perekat = 12% x 451,164 = 54,139 g
Kadar perekat akhir = 54,139 x
= 125,904 + 12,59 = 138,494 g
D. Kadar perekat phenol formaldehida (PF) = 14%
∑ partikel =( 25 x 25 x 1) x 0,7 x
383,771 + 38,37 = 422,141
g
KA 5% = 422,141 + 5% (422,141) = 443,24 g
Kadar perekat = 14% x 443,24 = 62,053 g
iii
Universitas Sumatera Utara
Kadar perekat akhir = 62,053 x
= 144,31 + 14,431 = 158,741 g
E. Kadar perekat phenol formaldehida (PF) = 16%
∑ partikel =( 25 x 25 x 1) x 0,7 x
= 377,155 + 37,715 = 414,87 g
KA 5% = 414,87 + 5% (414,87) = 435,613 g
Kadar perekat = 16% x 435,613 = 69,69 g
= 162,08 + 16,208 = 178,296 g
Kadar perekat akhir = 69,69 x
iii
Universitas Sumatera Utara
Lampiran 2. Rekapitulasi nilai kerapatan dan kadar air papan partikel
Kadar
Perekat
PF (%)
8
10
12
14
16
Ulangan
P (cm)
L (cm)
T (cm)
Volume
(cm)
BKU
(g)
BKO
(g)
KA
(%)
Kerapatan
(g/cm3)
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
10,557
10,496
10,295
10,523
10,387
10,424
1,264
1,178
1,273
140,41
128,45
136,67
75,66
83
82,25
71,5
78,33
77,56
10,341
10,304
10,533
10,407
10,435
10,866
1,287
1,242
1,271
138,51
133,59
145,56
79,53
87,78
90,73
76
83,74
86,85
10,714
10,007
10,235
10,245
10,07
10,28
1,343
1,208
1,217
147,49
121,78
119,24
80,91
86,57
70
76,81
82,33
66,45
9,862
10,085
10,263
10,403
10,103
10,419
1,171
11,73
1,24
120,17
119,54
132,62
72,65
74,75
80,3
69
71,2
76,59
10,461
10,561
10,429
10,26
10,277
10,735
1,265
1,155
1,226
135,83
125,45
137,31
83,91
81
84,17
80,08
77,47
80,15
5,82
5,96
6,05
5,94
4,64
4,82
4,47
4,65
5,34
5,15
5,34
5,28
5,29
4,99
4,84
5,04
4,78
4,56
5,02
4,78
0,57
0,59
0,60
0,59
0,57
0,60
0,59
0,59
0,59
0,57
0,59
0,59
0,60
0,63
0,61
0,61
0,62
0,62
0,61
0,62
Keterangan:
P
: panjang contoh uji
L
: lebar contoh uji
T
: tebal contoh uji
BKU : berat kering udara contoh uji
BKO : berat kering oven contoh uji
KA
: kadar air contoh uji
iii
Universitas Sumatera Utara
Lampiran 3. Rekapitulasi nilai daya serap air papan partikel
Kadar
Perekat PF
(%)
8
10
12
14
16
Ulangan
Berat
Awal (g)
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
30,99
26,14
25,78
Berat Setelah
Perendaman (g)
2 Jam
24 Jam
54,37
60
45,83
51,12
45,84
50,59
23,49
17,42
18,8
39,74
29,91
31,37
43,48
39,89
34,85
22,63
19,89
17,5
35,77
32,49
28,74
39,45
39,57
33,29
18,97
18,55
22,2
31,08
28,2
36,55
36,68
30,13
35,12
21,99
25,78
19,78
31,92
36,06
29,76
35,56
40,08
32,83
Daya Serap Air (%)
2 Jam
75,44
75,33
77,81
76,19
69,18
71,7
66,86
69,25
66,68
63,35
64,23
64,75
63,84
52,02
64,64
60,17
45,16
39,88
50,46
45,16
24 Jam
93,61
95,56
96,24
95,14
85,10
83,15
85,37
84,54
79,84
75,87
75,67
77,13
59,27
67,2
60,81
62,43
61,71
55,47
65,98
61,05
iii
Universitas Sumatera Utara
Lampiran 4. Rekapitulasi hasil pengembangan tebal papan partikel
Kadar
Perekat
PF (%)
Ulangan
8
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
10
12
14
16
Tebal
sebelum
perendaman
(g)
1,28
1,38
1,39
Tebal setelah
Perendaman (g)
2 Jam
24 Jam
1,8
1,83
1,85
1,82
1,97
1,96
1,2
1,3
1,26
1,46
1,6
1,56
1,48
1,66
1,65
1,27
1,19
1,23
1,55
1,44
1,51
1,61
1,53
1,57
1,19
1,19
1,22
1,36
1,37
1,45
1,39
1,55
1,51
1,21
1,19
1,29
1,44
1,38
1,44
1,45
1,45
1,39
Pengembangan
Tebal (%)
2 Jam
24 Jam
39,93
32,59
32,82
35,11
21,94
23,06
24,28
23,1
21,82
20,62
22,57
21,67
14,71
15,51
19,08
16,43
19,45
15,99
12,29
15,91
47,74
42,37
40,78
43,63
23,55
28,21
31,43
27,73
26,29
24,6
26,31
25,73
20,37
20,82
23,87
21,68
20,72
20,21
16,98
19,31
iii
Universitas Sumatera Utara
Lampiran 5. Rekapitulasi nilai internal bond papan partikel
Kadar
Perekat PF
(%)
8
10
12
14
16
Ulangan
P max
(kg)
P
(cm)
L
(cm)
A
(cm)
IB
(kg/cm2)
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
50,63
34,48
35,33
5,35
5,09
5,24
5,77
5,72
5,58
30,87
29,08
29,26
57,18
50,02
22,81
5,39
5,29
5,46
5,22
4,85
5,57
28,15
25,66
30,41
34,21
31,08
82,56
5,19
5,1
5,12
5,12
5,04
5,33
26,53
25,74
27,26
77,21
62,21
51,45
5,57
5,01
5,45
5,25
5,23
5,04
29,27
26,2
27,46
91,22
61,85
31,16
5,17
5,53
5,59
5,76
5,57
5,03
29,75
30,79
28,08
1,64
1,19
1,21
1,34
2,03
1,95
0,75
1,57
1,29
1,21
3,03
1,84
2,64
2,37
1,87
2,29
3,07
2,01
1,11
2,06
Keterangan:
P
: panjang contoh uji
L
: lebar contoh uji
A
: luas penampang contoh uji
P Max : beban maksimum yang diberikan
IB
: internal bond (keteguhan rekat internal) contoh uji
iii
Universitas Sumatera Utara
Lampiran 6. Rekapitulasi nilai MOE papan partikel
Kadar
perekat
PF (%)
8
10
12
14
16
Ulangan
ΔP
(kg)
ΔY
(kg)
L
(cm)
b
(cm)
h
(cm)
MOE
(kg/cm2)
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
1
1
0,01301
0,00746
0,0081
16
16
16
5,48
5,56
5,52
1,18
1,34
1,33
1
1
1
0,01091
0,0116
0,01109
16
16
16
5,25
5,67
5,42
1,23
1,19
1,18
1
1
1
0,01006
0,0092
0,01207
16
16
16
5,39
5,2
5,36
1,2
1,19
1,18
1
1
1
0,00998
0,01255
0,00871
16
16
16
5,59
5,13
5,55
1,18
1,17
1,27
1
1
1
0,00983
0,0097
0,01086
16
16
16
5,68
5,43
5,55
1,18
1,16
1,15
8692,646
10161,93
9753,602
9536,06
9712,052
9249,817
10455,78
9805,88
10792,96
12660,05
9666,836
11039,95
11291,07
9848,013
10365,42
10501,50
11283
12560,59
11242,69
11695,42
Keterangan:
b
h
L
ΔP
ΔY
MOE
: lebar contoh uji
: tebal contoh uji
: jarak sanggah
: beban sebelum batas proporsi
: lenturan pada beban
: keteguhan lentur contoh uji
iii
Universitas Sumatera Utara
Lampiran 7. Rekapitulasi nilai MOR papan partikel
Kadar
perekat PF
(%)
Ulangan
P max
(kg)
L
(cm)
b
(cm)
h
(cm)
MOR
(kg/cm2)
8
1
2
3
Rata-rata
1
2
3
Rata-rata
1
3
5
Rata-rata
3
4
5
Rata-rata
1
2
3
Rata-rata
27,98
38,53
41,96
16
16
16
5,48
5,31
5,52
1,18
1,27
1,33
87,67
108,06
103,32
99,68
30,25
40,27
31,27
16
16
16
5,67
5,29
5,42
1,19
1,26
1,18
90,48
115,93
100,01
102,14
37,71
31,14
39,66
16
16
16
5,48
5,39
5,36
1,26
1,2
1,18
103,38
95,49
127,84
108,91
34,13
40,85
62,04
16
16
16
5,14
5,48
5,64
1,16
1,17
1,25
118,05
130,73
169,6
139,46
48,95
44,37
41,21
16
16
16
5,79
5,43
5,55
1,18
1,16
1,15
145,68
146,57
135,35
142,54
10
12
14
16
Keterangan:
b
h
L
P Max
MOR
: lebar contoh uji
: tebal contoh uji
: jarak sanggah
:beban maksimum yang diberikan
: keteguhan patah contoh uji
iii
Universitas Sumatera Utara
Lampiran 8. Analisis keragaman kerapatan dan hasil uji duncan papan
partikel
Sumber keragaman Jumlah kuadrat DB
0.003
4
Kadar Perekat
Galad
0.001
10
Total
0.004
14
Kuadrat tengah
0.001
F
5.299*
Sig
0.015
0.000
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar Perekat
(%)
12
8
10
14
16
Sig.
Subset for alpha = 0,05
N
1
3
3
3
3
3
0.5850
0.5877
0.5897
Notasi
2
a
a
a
b
b
0.6118
0.6181
0.512
0.644
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
Lampiran 9. Analisis keragaman kadar air dan hasil uji duncan papan
partikel
Sumber keragaman
Jumlah kuadrat DB
Kuadrat tengah
F
Sig
Kadar Perekat
3.129
4
0.782
24.167**
0.000
Galad
0.324
10
0.032
Total
3.453
14
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar Perekat
(%)
10
16
14
12
8
Sig.
Subset for alpha = 0,05
N
1
3
3
3
3
3
4.6456
4.7850
0.365
2
4.7850
5.0399
0.113
3
Notasi
4
5.0399
5.2767
0.138
5.9424
1.000
a
ab
bc
c
d
iii
Universitas Sumatera Utara
Lampiran 10. Analisis keragaman daya serap air 2 jam dan hasil uji duncan
papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat DB
1626.938
4
Kuadrat tengah F
406.735
22.928**
Galad
177.396
10
17.740
Total
1804.334
14
Sig
0.000
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar
perekat (%)
16
14
12
10
8
Sig.
N
1
3
3
3
3
3
45.1626
Subset for alpha = 0,05
2
3
60.1663
64.7528
1.000
64.7528
69.2464
1.212
1.221
Notasi
4
a
b
bc
cd
d
69.2464
76.1937
0.071
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
Lampiran 11. Analisis keragaman daya serap air 24 jam dan hasil uji duncan
papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat
2544.325
DB Kuadrat tengah
4 636.081
Galad
108.964
10
Total
2653.289
14
F
58.376**
Sig
0.000
10.896
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar perekat
(%)
16
14
12
10
8
Sig.
Subset for alpha = 0,05
N
1
3
3
3
3
61.0517
62.4265
2
3
Notasi
4
77.1262
84.5407
95.1369
3
0.621
1.000
1.000
a
a
b
c
d
1.000
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
iii
Universitas Sumatera Utara
Lampiran 12. Analisis keragaman pengembangan tebal 2 jam dan hasil uji
duncan papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat
720.986
DB
4
Kuadrat tengah
180.247
Galad
75.993
10
7.599
Total
796.979
14
F
23.719**
sig
0.000
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Subset for alpha = 0,05
Kadar Perekat
(%)
16
14
12
10
8
Sig.
N
1
2
3
3
3
3
3
15.9120
16.4340
Notasi
3
a
a
b
b
c
21.6702
23.0950
0.821
0.541
35.1136
1.000
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
Lampiran 13. Analisis keragaman pengembangan tebal 24 jam dan hasil uji
duncan papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat
1092.559
DB
4
Kuadrat tengah
273.140
Galad
75.464
10
7.546
Total
1168.023
14
F
36.195**
sig
0.000
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar perekat
(%)
16
14
10
12
8
Sig.
N
1
3
3
3
3
3
Subset for alpha = 0,05
2
3
19.3054
21.6848
0.314
21.6848
25.7330
0.101
Notasi
4
25.7330
27.7284
0.395
43.6280
1.000
a
ab
bc
c
d
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
iii
Universitas Sumatera Utara
Lampiran 14. Analisis keragaman internal bond (IB) dan hasil uji duncan
papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat DB
1.709
4
Kuadrat tengah
0.427
Galad
5.494
10
Total
7.203
14
F
sig
tn
0.564
0.778
0.549
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
tn = Tidak berpengaruh nyata
Lampiran 15. Analisis keragaman keteguhan lentur (MOE) dan hasil uji
duncan papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat
9390953.362
DB Kuadrat tengah
4
2347738.341
Galad
8654497.408
10
Total
1.805E7
14
F
tn
2.713
sig
0.091
865449.741
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
tn = Tidak berpengaruh nyata
Lampiran 16. Analisis keragaman keteguhan patah (MOR) dan hasil uji
duncan papan partikel
Sumber keragaman Jumlah kuadrat
5192.275
Kadar Perekat
DB
4
Galad
2648.360
10
Total
7840.635
14
Kuadrat tengah
1298.069
F
4.901*
sig
0.019
264.836
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
tn = Tidak berpengaruh nyata
Kadar Perekat
(%)
8
10
12
14
16
Sig.
Subset for alpha = 0,05
N
1
3
3
3
3
3
99.6871
1.0215E2
1.0891E2
0.523
Notasi
2
1.3947E2
1.4254E2
0.822
a
a
a
b
b
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
iii
Universitas Sumatera Utara
Kadar perekat phenol formaldehida (PF) = 8%, 10%, 12%, 14%, dan 16%
Ukuran sampel = 25 x 25 x 1 cm
Kerapatan target = 0,7 g/cm3
Solid content phenol formaldehida = 43%
A. Kadar perekat phenol formaldehida (PF) = 8%
∑ partikel =(25 x 25 x 1)x 0,7 x
= 405,1 + 40,51 = 445,599
g (KA 0%)
KA 5% = 445,6 + 5% (445,6) = 467,88g (kebutuhan bahan baku
akhir)
Kadar perekat = 8% x 467,88 = 37,43 g
Kadar perekat akhir = 37,43 x
= 87,04 + (10% spilasi) = 95,74 g
B. Kadar perekat phenol formaldehida (PF) = 10%
∑ partikel = (25 x 25 x 1) x 0,7 x
= 397,727 + 39,77 = 437,497 g
KA 5% = 437,497 + 5% (437,497) = 459,37 g
Kadar perekat = 10% x 459,37 = 45,937 g
Kadar perekat akhir = 45,937 x
= 106,83 + 10,683 = 117,513 g
C. Kadar perekat phenol formaldehida (PF) = 12%
∑ partikel = (25 x 25 x 1)x 0,7 x
= 390,62 + 39,06 = 429,68 g
KA 5% = 429,68 + 5% (429,68) = 451,164 g
Kadar perekat = 12% x 451,164 = 54,139 g
Kadar perekat akhir = 54,139 x
= 125,904 + 12,59 = 138,494 g
D. Kadar perekat phenol formaldehida (PF) = 14%
∑ partikel =( 25 x 25 x 1) x 0,7 x
383,771 + 38,37 = 422,141
g
KA 5% = 422,141 + 5% (422,141) = 443,24 g
Kadar perekat = 14% x 443,24 = 62,053 g
iii
Universitas Sumatera Utara
Kadar perekat akhir = 62,053 x
= 144,31 + 14,431 = 158,741 g
E. Kadar perekat phenol formaldehida (PF) = 16%
∑ partikel =( 25 x 25 x 1) x 0,7 x
= 377,155 + 37,715 = 414,87 g
KA 5% = 414,87 + 5% (414,87) = 435,613 g
Kadar perekat = 16% x 435,613 = 69,69 g
= 162,08 + 16,208 = 178,296 g
Kadar perekat akhir = 69,69 x
iii
Universitas Sumatera Utara
Lampiran 2. Rekapitulasi nilai kerapatan dan kadar air papan partikel
Kadar
Perekat
PF (%)
8
10
12
14
16
Ulangan
P (cm)
L (cm)
T (cm)
Volume
(cm)
BKU
(g)
BKO
(g)
KA
(%)
Kerapatan
(g/cm3)
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
10,557
10,496
10,295
10,523
10,387
10,424
1,264
1,178
1,273
140,41
128,45
136,67
75,66
83
82,25
71,5
78,33
77,56
10,341
10,304
10,533
10,407
10,435
10,866
1,287
1,242
1,271
138,51
133,59
145,56
79,53
87,78
90,73
76
83,74
86,85
10,714
10,007
10,235
10,245
10,07
10,28
1,343
1,208
1,217
147,49
121,78
119,24
80,91
86,57
70
76,81
82,33
66,45
9,862
10,085
10,263
10,403
10,103
10,419
1,171
11,73
1,24
120,17
119,54
132,62
72,65
74,75
80,3
69
71,2
76,59
10,461
10,561
10,429
10,26
10,277
10,735
1,265
1,155
1,226
135,83
125,45
137,31
83,91
81
84,17
80,08
77,47
80,15
5,82
5,96
6,05
5,94
4,64
4,82
4,47
4,65
5,34
5,15
5,34
5,28
5,29
4,99
4,84
5,04
4,78
4,56
5,02
4,78
0,57
0,59
0,60
0,59
0,57
0,60
0,59
0,59
0,59
0,57
0,59
0,59
0,60
0,63
0,61
0,61
0,62
0,62
0,61
0,62
Keterangan:
P
: panjang contoh uji
L
: lebar contoh uji
T
: tebal contoh uji
BKU : berat kering udara contoh uji
BKO : berat kering oven contoh uji
KA
: kadar air contoh uji
iii
Universitas Sumatera Utara
Lampiran 3. Rekapitulasi nilai daya serap air papan partikel
Kadar
Perekat PF
(%)
8
10
12
14
16
Ulangan
Berat
Awal (g)
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
30,99
26,14
25,78
Berat Setelah
Perendaman (g)
2 Jam
24 Jam
54,37
60
45,83
51,12
45,84
50,59
23,49
17,42
18,8
39,74
29,91
31,37
43,48
39,89
34,85
22,63
19,89
17,5
35,77
32,49
28,74
39,45
39,57
33,29
18,97
18,55
22,2
31,08
28,2
36,55
36,68
30,13
35,12
21,99
25,78
19,78
31,92
36,06
29,76
35,56
40,08
32,83
Daya Serap Air (%)
2 Jam
75,44
75,33
77,81
76,19
69,18
71,7
66,86
69,25
66,68
63,35
64,23
64,75
63,84
52,02
64,64
60,17
45,16
39,88
50,46
45,16
24 Jam
93,61
95,56
96,24
95,14
85,10
83,15
85,37
84,54
79,84
75,87
75,67
77,13
59,27
67,2
60,81
62,43
61,71
55,47
65,98
61,05
iii
Universitas Sumatera Utara
Lampiran 4. Rekapitulasi hasil pengembangan tebal papan partikel
Kadar
Perekat
PF (%)
Ulangan
8
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
10
12
14
16
Tebal
sebelum
perendaman
(g)
1,28
1,38
1,39
Tebal setelah
Perendaman (g)
2 Jam
24 Jam
1,8
1,83
1,85
1,82
1,97
1,96
1,2
1,3
1,26
1,46
1,6
1,56
1,48
1,66
1,65
1,27
1,19
1,23
1,55
1,44
1,51
1,61
1,53
1,57
1,19
1,19
1,22
1,36
1,37
1,45
1,39
1,55
1,51
1,21
1,19
1,29
1,44
1,38
1,44
1,45
1,45
1,39
Pengembangan
Tebal (%)
2 Jam
24 Jam
39,93
32,59
32,82
35,11
21,94
23,06
24,28
23,1
21,82
20,62
22,57
21,67
14,71
15,51
19,08
16,43
19,45
15,99
12,29
15,91
47,74
42,37
40,78
43,63
23,55
28,21
31,43
27,73
26,29
24,6
26,31
25,73
20,37
20,82
23,87
21,68
20,72
20,21
16,98
19,31
iii
Universitas Sumatera Utara
Lampiran 5. Rekapitulasi nilai internal bond papan partikel
Kadar
Perekat PF
(%)
8
10
12
14
16
Ulangan
P max
(kg)
P
(cm)
L
(cm)
A
(cm)
IB
(kg/cm2)
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
50,63
34,48
35,33
5,35
5,09
5,24
5,77
5,72
5,58
30,87
29,08
29,26
57,18
50,02
22,81
5,39
5,29
5,46
5,22
4,85
5,57
28,15
25,66
30,41
34,21
31,08
82,56
5,19
5,1
5,12
5,12
5,04
5,33
26,53
25,74
27,26
77,21
62,21
51,45
5,57
5,01
5,45
5,25
5,23
5,04
29,27
26,2
27,46
91,22
61,85
31,16
5,17
5,53
5,59
5,76
5,57
5,03
29,75
30,79
28,08
1,64
1,19
1,21
1,34
2,03
1,95
0,75
1,57
1,29
1,21
3,03
1,84
2,64
2,37
1,87
2,29
3,07
2,01
1,11
2,06
Keterangan:
P
: panjang contoh uji
L
: lebar contoh uji
A
: luas penampang contoh uji
P Max : beban maksimum yang diberikan
IB
: internal bond (keteguhan rekat internal) contoh uji
iii
Universitas Sumatera Utara
Lampiran 6. Rekapitulasi nilai MOE papan partikel
Kadar
perekat
PF (%)
8
10
12
14
16
Ulangan
ΔP
(kg)
ΔY
(kg)
L
(cm)
b
(cm)
h
(cm)
MOE
(kg/cm2)
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
2
3
Rata-rata
1
1
1
0,01301
0,00746
0,0081
16
16
16
5,48
5,56
5,52
1,18
1,34
1,33
1
1
1
0,01091
0,0116
0,01109
16
16
16
5,25
5,67
5,42
1,23
1,19
1,18
1
1
1
0,01006
0,0092
0,01207
16
16
16
5,39
5,2
5,36
1,2
1,19
1,18
1
1
1
0,00998
0,01255
0,00871
16
16
16
5,59
5,13
5,55
1,18
1,17
1,27
1
1
1
0,00983
0,0097
0,01086
16
16
16
5,68
5,43
5,55
1,18
1,16
1,15
8692,646
10161,93
9753,602
9536,06
9712,052
9249,817
10455,78
9805,88
10792,96
12660,05
9666,836
11039,95
11291,07
9848,013
10365,42
10501,50
11283
12560,59
11242,69
11695,42
Keterangan:
b
h
L
ΔP
ΔY
MOE
: lebar contoh uji
: tebal contoh uji
: jarak sanggah
: beban sebelum batas proporsi
: lenturan pada beban
: keteguhan lentur contoh uji
iii
Universitas Sumatera Utara
Lampiran 7. Rekapitulasi nilai MOR papan partikel
Kadar
perekat PF
(%)
Ulangan
P max
(kg)
L
(cm)
b
(cm)
h
(cm)
MOR
(kg/cm2)
8
1
2
3
Rata-rata
1
2
3
Rata-rata
1
3
5
Rata-rata
3
4
5
Rata-rata
1
2
3
Rata-rata
27,98
38,53
41,96
16
16
16
5,48
5,31
5,52
1,18
1,27
1,33
87,67
108,06
103,32
99,68
30,25
40,27
31,27
16
16
16
5,67
5,29
5,42
1,19
1,26
1,18
90,48
115,93
100,01
102,14
37,71
31,14
39,66
16
16
16
5,48
5,39
5,36
1,26
1,2
1,18
103,38
95,49
127,84
108,91
34,13
40,85
62,04
16
16
16
5,14
5,48
5,64
1,16
1,17
1,25
118,05
130,73
169,6
139,46
48,95
44,37
41,21
16
16
16
5,79
5,43
5,55
1,18
1,16
1,15
145,68
146,57
135,35
142,54
10
12
14
16
Keterangan:
b
h
L
P Max
MOR
: lebar contoh uji
: tebal contoh uji
: jarak sanggah
:beban maksimum yang diberikan
: keteguhan patah contoh uji
iii
Universitas Sumatera Utara
Lampiran 8. Analisis keragaman kerapatan dan hasil uji duncan papan
partikel
Sumber keragaman Jumlah kuadrat DB
0.003
4
Kadar Perekat
Galad
0.001
10
Total
0.004
14
Kuadrat tengah
0.001
F
5.299*
Sig
0.015
0.000
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar Perekat
(%)
12
8
10
14
16
Sig.
Subset for alpha = 0,05
N
1
3
3
3
3
3
0.5850
0.5877
0.5897
Notasi
2
a
a
a
b
b
0.6118
0.6181
0.512
0.644
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
Lampiran 9. Analisis keragaman kadar air dan hasil uji duncan papan
partikel
Sumber keragaman
Jumlah kuadrat DB
Kuadrat tengah
F
Sig
Kadar Perekat
3.129
4
0.782
24.167**
0.000
Galad
0.324
10
0.032
Total
3.453
14
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar Perekat
(%)
10
16
14
12
8
Sig.
Subset for alpha = 0,05
N
1
3
3
3
3
3
4.6456
4.7850
0.365
2
4.7850
5.0399
0.113
3
Notasi
4
5.0399
5.2767
0.138
5.9424
1.000
a
ab
bc
c
d
iii
Universitas Sumatera Utara
Lampiran 10. Analisis keragaman daya serap air 2 jam dan hasil uji duncan
papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat DB
1626.938
4
Kuadrat tengah F
406.735
22.928**
Galad
177.396
10
17.740
Total
1804.334
14
Sig
0.000
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar
perekat (%)
16
14
12
10
8
Sig.
N
1
3
3
3
3
3
45.1626
Subset for alpha = 0,05
2
3
60.1663
64.7528
1.000
64.7528
69.2464
1.212
1.221
Notasi
4
a
b
bc
cd
d
69.2464
76.1937
0.071
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
Lampiran 11. Analisis keragaman daya serap air 24 jam dan hasil uji duncan
papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat
2544.325
DB Kuadrat tengah
4 636.081
Galad
108.964
10
Total
2653.289
14
F
58.376**
Sig
0.000
10.896
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar perekat
(%)
16
14
12
10
8
Sig.
Subset for alpha = 0,05
N
1
3
3
3
3
61.0517
62.4265
2
3
Notasi
4
77.1262
84.5407
95.1369
3
0.621
1.000
1.000
a
a
b
c
d
1.000
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
iii
Universitas Sumatera Utara
Lampiran 12. Analisis keragaman pengembangan tebal 2 jam dan hasil uji
duncan papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat
720.986
DB
4
Kuadrat tengah
180.247
Galad
75.993
10
7.599
Total
796.979
14
F
23.719**
sig
0.000
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Subset for alpha = 0,05
Kadar Perekat
(%)
16
14
12
10
8
Sig.
N
1
2
3
3
3
3
3
15.9120
16.4340
Notasi
3
a
a
b
b
c
21.6702
23.0950
0.821
0.541
35.1136
1.000
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
Lampiran 13. Analisis keragaman pengembangan tebal 24 jam dan hasil uji
duncan papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat
1092.559
DB
4
Kuadrat tengah
273.140
Galad
75.464
10
7.546
Total
1168.023
14
F
36.195**
sig
0.000
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
Kadar perekat
(%)
16
14
10
12
8
Sig.
N
1
3
3
3
3
3
Subset for alpha = 0,05
2
3
19.3054
21.6848
0.314
21.6848
25.7330
0.101
Notasi
4
25.7330
27.7284
0.395
43.6280
1.000
a
ab
bc
c
d
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
iii
Universitas Sumatera Utara
Lampiran 14. Analisis keragaman internal bond (IB) dan hasil uji duncan
papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat DB
1.709
4
Kuadrat tengah
0.427
Galad
5.494
10
Total
7.203
14
F
sig
tn
0.564
0.778
0.549
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
tn = Tidak berpengaruh nyata
Lampiran 15. Analisis keragaman keteguhan lentur (MOE) dan hasil uji
duncan papan partikel
Sumber keragaman
Kadar Perekat
Jumlah kuadrat
9390953.362
DB Kuadrat tengah
4
2347738.341
Galad
8654497.408
10
Total
1.805E7
14
F
tn
2.713
sig
0.091
865449.741
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
tn = Tidak berpengaruh nyata
Lampiran 16. Analisis keragaman keteguhan patah (MOR) dan hasil uji
duncan papan partikel
Sumber keragaman Jumlah kuadrat
5192.275
Kadar Perekat
DB
4
Galad
2648.360
10
Total
7840.635
14
Kuadrat tengah
1298.069
F
4.901*
sig
0.019
264.836
* = Berpengaruh nyata
** = Sangat berpengaruh nyata
tn = Tidak berpengaruh nyata
Kadar Perekat
(%)
8
10
12
14
16
Sig.
Subset for alpha = 0,05
N
1
3
3
3
3
3
99.6871
1.0215E2
1.0891E2
0.523
Notasi
2
1.3947E2
1.4254E2
0.822
a
a
a
b
b
Ket: Notasi yang sama artinya tidak berbeda nyata
Notasi yang tidak sama artinya berbeda nyata
iii
Universitas Sumatera Utara