Ketahanan Fiber Plastic Composites Polipropilena Terhadap Pemaparan Cuaca
Susan Barbara Patricia S. M. Durability of Fiber Plastic Composites
Polyprophylene to Weathering Exposed. Under Supervised by Luthfi Hakim and
Ridwanti Batubara.
ABSTRACT
Fiber plastic composites (FPC) is one of expand biocomposites product to
substitute wood. In this research FPC made from recycle polyprophylene and old
corrugated paper fiber. The purpose of this research were to evaluate durability
of physical and mechanical properties of FPC after exposed to outdoor
weathering for six months. This research use completely randomized factorial
design, 2 factors: compositions polyprophylene and fiber (50:50, 60:40 and
70:30) and percentage of maleic anhydryd (5% and 7%) and the results compare
with JIS A 5905-2003 hardboard S20 and JIS A 5908-2003 particleboards type
13. The results showed that the physical properties of FPC fulfill standard JIS A
5905-2003 hardboard S20 and JIS A 5908-2003 particleboards type 13 after
exposed to outdoor weathering for six months except moisture content.
Mechanical properties testing showed that modulus of rapture fulfill standard JIS
A 5905-2003 hardboard S20 and JIS A 5908-2003 particleboards too. Physicly
FPC degradated too, such as board colour change and board broken.
Keywords: fiber plastic composites, polyprophylene, maleic anhydryd (MAH),
weathering expose and physical and mechanical properties durability.
Universitas Sumatera Utara
Susan Barbara Patricia S. M. Ketahanan Fiber Plastic Composites
Polipropilena Terhadap Pemaparan Cuaca. Dibimbing oleh Luthfi Hakim dan
Ridwanti Batubara.
ABSTRAK
Fiber plastic composites (FPC) adalah salah satu produk biokomposit
yang berkembang sebagai substitusi kayu solid. Pada penelitian ini FPC terbuat
dari polipropilena daur ulang dan serat kardus bekas. Tujuan dari penelitian ini
adalah untuk mengevaluasi ketahanan sifat fisis dan sifat mekanis dari FPC
setelah pemaparan cuaca di luar ruangan selama enam bulan. Penelitian ini
menggunakan rancangan acak lengkap (RAL) faktorial, 2 faktor: perbandingan
polipropilena dengan serat kardus (50:50, 60:40 dan 70:30) dan persentasi maleat
anhidrid (MAH) (5% dan 7%) dan hasilnya dibandingkan dengan standar JIS A
5905-2003 hardboard S20 dan JIS A 5908-2003 particleboards type 13. Hasil
penelitian menunjukkan bahwa sifat fisis FPC memenuhi standar JIS A 59052003 hardboard S20 dan JIS A 5908-2003 particleboards type 13 kecuali sifat
kadar air. Pengujian sifat mekanis keteguhan patah juga memenuhi standar JIS A
5905-2003 hardboard S20 dan JIS A 5908-2003 particleboards type 13. Secara
fisik FPC juga mengalami degradasi seperti perubahan warna papan dan
kerusakan papan.
Kata kunci: fiber plastic composites (FPC), polipropilena, maleat anhidrid
(MAH), pemaparan cuaca, ketahanan sifat fisis dan mekanis.
Universitas Sumatera Utara
Polyprophylene to Weathering Exposed. Under Supervised by Luthfi Hakim and
Ridwanti Batubara.
ABSTRACT
Fiber plastic composites (FPC) is one of expand biocomposites product to
substitute wood. In this research FPC made from recycle polyprophylene and old
corrugated paper fiber. The purpose of this research were to evaluate durability
of physical and mechanical properties of FPC after exposed to outdoor
weathering for six months. This research use completely randomized factorial
design, 2 factors: compositions polyprophylene and fiber (50:50, 60:40 and
70:30) and percentage of maleic anhydryd (5% and 7%) and the results compare
with JIS A 5905-2003 hardboard S20 and JIS A 5908-2003 particleboards type
13. The results showed that the physical properties of FPC fulfill standard JIS A
5905-2003 hardboard S20 and JIS A 5908-2003 particleboards type 13 after
exposed to outdoor weathering for six months except moisture content.
Mechanical properties testing showed that modulus of rapture fulfill standard JIS
A 5905-2003 hardboard S20 and JIS A 5908-2003 particleboards too. Physicly
FPC degradated too, such as board colour change and board broken.
Keywords: fiber plastic composites, polyprophylene, maleic anhydryd (MAH),
weathering expose and physical and mechanical properties durability.
Universitas Sumatera Utara
Susan Barbara Patricia S. M. Ketahanan Fiber Plastic Composites
Polipropilena Terhadap Pemaparan Cuaca. Dibimbing oleh Luthfi Hakim dan
Ridwanti Batubara.
ABSTRAK
Fiber plastic composites (FPC) adalah salah satu produk biokomposit
yang berkembang sebagai substitusi kayu solid. Pada penelitian ini FPC terbuat
dari polipropilena daur ulang dan serat kardus bekas. Tujuan dari penelitian ini
adalah untuk mengevaluasi ketahanan sifat fisis dan sifat mekanis dari FPC
setelah pemaparan cuaca di luar ruangan selama enam bulan. Penelitian ini
menggunakan rancangan acak lengkap (RAL) faktorial, 2 faktor: perbandingan
polipropilena dengan serat kardus (50:50, 60:40 dan 70:30) dan persentasi maleat
anhidrid (MAH) (5% dan 7%) dan hasilnya dibandingkan dengan standar JIS A
5905-2003 hardboard S20 dan JIS A 5908-2003 particleboards type 13. Hasil
penelitian menunjukkan bahwa sifat fisis FPC memenuhi standar JIS A 59052003 hardboard S20 dan JIS A 5908-2003 particleboards type 13 kecuali sifat
kadar air. Pengujian sifat mekanis keteguhan patah juga memenuhi standar JIS A
5905-2003 hardboard S20 dan JIS A 5908-2003 particleboards type 13. Secara
fisik FPC juga mengalami degradasi seperti perubahan warna papan dan
kerusakan papan.
Kata kunci: fiber plastic composites (FPC), polipropilena, maleat anhidrid
(MAH), pemaparan cuaca, ketahanan sifat fisis dan mekanis.