Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003
STUDI KOMPARASI SNI 03-2105-2006 DENGANJIS A 59082003
HASIL PENELITIAN
Oleh Jevlen Joel Simarmata 071203035/Teknologi Hasil Hutan
DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN
UNIVERSITAS SUMATERA UTARA
Universitas Sumatera Utara
2012
ABSTRACT
JEVLEN SIMARMATA. Comparative Study of JIS A 5908-2003 with SNI 032105-2006. Supervised by YUNUS AFIFUDDIN dan LUTHFI HAKIM.
Japan and Indonesia has own criteria in determinating the applicable standards for particleboard in accordance with the development of industry in each country. JIS and SNI have weaknesses and strengths that are only applicable in their respective countries so that the necessary information to evaluate these standards in order to be valid not only in each country.
The purpose of this research is to compare JIS A 5908-2003 withSNI 032105-2006. Data analysis was done by using descriptive comparative technic that is compare standards specified in JIS A 5908-2003 andSNI 03-2105-2006 so that known weaknesses and strengths of each standard. Based on the quality of performance, quality particleboard JIS A 5908-2003 better than quality of particleboard SNI 03-2105-2006. Formaldehyde emissions of JIS A 5908-2003 is lower than SNI 03-2105-2006. Classification of particleboard based on surface condition, thickness, length and width, emissions of formaldehyde, the qualityof performances between JIS A 5908-2003 andSNI 03-2105-2006 are different. Classification of particleboard by an adhesive and Terms defined mechanical properties betweenJIS A 5908-2003 andSNI 03-2105-2006 are the same.SNI 032105-2006 not test the fire insulation and heat insulation power.JIS A 5908-2003 has more excellence compared toSNI 03-2105-2006. Based on parameters required, JIS A 5908-2003 and SNI 03-2105-2006 have more similarities.
Keywords: Particleboard, Indonesia National Standard, Japanese Industrial Standar, Compare.
Universitas Sumatera Utara
ABSTRAK
JEVLEN SIMARMATA. Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003. Dibimbing oleh YUNUS AFIFUDDIN dan LUTHFI HAKIM.
Indonesia dan Jepang memiliki kriteria tersendiri dalam menentukan standar yang berlaku untuk papan partikel sesuai dengan perkembangan industri di masing-masing negara. SNI dan JIS memiliki kelemahan dan kelebihan yang hanya berlaku di negara masing-masing sehingga diperlukan informasi untuk mengevaluasi standar tersebut agar dapat berlaku tidak hanya di masing-masing negara.
Tujuan penelitian ini adalah untuk membandingkan standar papan partikel SNI 03-2105-2006 dan JIS A 5908-2003. Analisa data dilakukan dengan teknik deskriptif komparatif yaitu membandingkan standarisasi yang ditetapkan pada JIS A 5908-2003 dan SNI 03-2105-2006 sehingga diketahui kelemahan dan kelebihan dari masing-masing standar.Berdasarkan mutu penampilan, kualitas papan partikel JIS A 5908-2003 lebih baik dibandingkan dengan kualitas papan partikel SNI 03-2105-2006. Emisi formaldehida pada JIS A 5908-2003 lebih rendah dibandingkan dengan SNI 03-2105-2006. Klasifikasi papan partikel berdasarkan kondisi permukaan, ketebalan, panjang dan lebar, emisi formaldehida, mutu penampilan antara JIS A 5908-2003 dan SNI 03-2105-2006 berbeda. Klasifikasi papan partikel berdasarkan perekat dan syarat sifat mekanis yang ditetapkan antara JIS A 5908-2003 dan SNI 03-2105-2006 adalah sama. SNI 03-2105-2006 tidak melakukan uji ketahanan terhadap api dan uji daya sekat panas.JIS A 59082003 memiliki lebih banyak kelebihan dibandingkan SNI 03-21052006.Berdasarkan parameter yang dipersyaratkan JIS A 5908-2003 dan SNI 032105-2006 lebih banyak memiliki persamaan.
Kata kunci: Papan Partikel, Standar Nasional Indonesia, Standar Industrial Jepang, Komparasi.
Universitas Sumatera Utara
RIWAYAT HIDUP
Penulis dilahirkan di Berastagi, Kabupaten Karo pada tanggal 3 Februari 1989 dari Ayah A. Simarmata dan IbuK. Naibaho. Penulis adalah anak keempat dari empat bersaudara.
Penulis menyelesaikan Sekolah Dasar di SD Letjen Djamin Ginting Berastagi, Kabupaten Karo pada tahun 2000, Sekolah Lanjutan Tingkat Pertama (SLTP) di SLTP Negeri 1 Berastagi, Kabupaten Karo tahun 2003, dan Sekolah Menengah Kejuruan (SMK) di SMK Negeri 1 Berastagi, Kabupaten Karo tahun 2006. Tahun 2007 penulis kuliah di Universitas Sumatera Utara (USU) melalui jalur Seleksi Penerimaan Mahasiswa Baru (SPMB). Penulis memilih Program Studi Teknologi Hasil Hutan, Departemen Kehutanan.
Pada tahun 2009, penulis mengikuti kegiatan Praktik Pengenalan dan Pengelolaan Hutan (P3H) di Pulau Sembilan dan Aras Napal, Kabupaten Langkat Provinsi Sumatera Utara. Pada Tahun 2011, penulis juga melaksanakan Praktik Kerja Lapangan (PKL) di Taman Nasional Baluran Surabaya, Provinsi Jawa Timur selama 1 bulan. Penulis melaksanakan penelitiandengan judul ”Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003”, di bawah bimbingan Bapak Yunus Afifuddin S.Hut., M.Si.dan Bapak Luthfi Hakim S.Hut., M.Si.
Universitas Sumatera Utara
KATA PENGANTAR
Puji dan syukur penulis ucapkan kehadirat Tuhan Yang Maha Esa,atas kasih dan karunia-Nyapenulis dapat menyelesaikan skripsi yang berjudul ”Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003”. SkripsiinimerupakansalahsatusyaratuntukmenjadiSarjanaKehutanan.
Penulis menyampaikan terima kasih kepada kedua orang tua, abang, dan
kakak
penulis
yang
selalumendoakan,
memberidukungan,
kasihsayangdanmaterisertamenginspirasipenulisuntuktetapsemangatdalammewuju
dkanskripsiinisertakepada teman-teman THH angkatan 2007 yang
selalumembantu sertamemberidorongandalammengerjakanskripsiini. Penulis juga
mengucapkan terima kasih kepada komisi pembimbing skripsiyaituBapak Yunus
Afifuddin S.Hut., M.Si.danBapak Luthfi Hakim S.Hut., M.Si. selakuketuadan
anggotakomisi pembimbing yang telah membimbing dan memberikan berbagai
masukan berharga serta saran dalam pembuatan skripsiini.
Penulis menyadari terdapat beberapa kekurangan dalam penulisan skripsi ini, oleh karena itu penulis memohon maaf atas kekurangan tersebut. Penulis mengharapkan agar skripsiinidapatmenjadipanduanbelajardanbacaan yang bermanfaatbagimahasiswa/i kehutanansecarakhususdanmasyarakatsecaraumum. Akhir kata penulis menyampaikan terima kasih.
Medan, Juli 2012
Penulis
Universitas Sumatera Utara
DAFTAR ISI
Halaman
ABSTRACT....................................................................................................... i ABSTRAK ....................................................................................................... ii RIWAYAT HIDUP ......................................................................................... iii KATA PENGANTAR ..................................................................................... iv DAFTAR ISI.................................................................................................... v DAFTAR TABEL............................................................................................ vi DAFTAR LAMPIRAN.................................................................................... vii PENDAHULUAN Latar Belakang ................................................................................................. 1 Tujuan Penelitian ............................................................................................. 2 Manfaat Penelitian ........................................................................................... 2
TINJAUAN PUSTAKA Japanese Industrial Standard ........................................................................... 3 Standar Nasional Indonesia ............................................................................. 5 METODE PENELITIAN Waktu Penelitian ............................................................................................. 7 Bahan Penelitian .............................................................................................. 7 Metode Penelitian ............................................................................................ 7
HASIL DAN PEMBAHASAN Kondisi permukaan .......................................................................................... 11 Ketebalan, Panjang dan Lebar ......................................................................... 12 Toleransi dan Kesikuan.................................................................................... 13 Perekat.............................................................................................................. 13 Emisi Formaldehida ......................................................................................... 15 Mutu Penampilan ............................................................................................. 15 Syarat Sifat Fisis dan Mekanis......................................................................... 16 Pengujian Papan Partikel ................................................................................. 22 KESIMPULAN................................................................................................ 29 DAFTAR PUSTAKA ...................................................................................... 30 LAMPIRAN..................................................................................................... 30
Universitas Sumatera Utara
DAFTAR TABEL
No. Halaman
1. Komparasi parameter JIS A 5908-2003 dan SNI 03-2105-2006.................. 8 2. Acuan normatif standar JIS A 5908-2003 dan SNI 03-2105-2006.............. 10 3. Klasifikasi papan partikel berdasarkan kondisi permukaan......................... 11 4. Klasifikasi papan partikel berdasarkan ketebalan........................................ 12 5. Klasifikasi papan partikel berdasarkan panjang dan lebar........................... 12 6. Toleransi tebal papan partikel...................................................................... 13 7. Klasifikasi papan partikel berdasarkan perekat ........................................... 14 8. Klasifikasi papan partikel berdasarkan emisi formaldehida ........................ 15 9. Syarat umum papan partikel biasa ............................................................... 16 10. Syarat kerapatan papan partikel ................................................................... 16 11. Syarat kadar air papan partikel .................................................................... 17 12. Syarat pengembangan tebal papan partikel.................................................. 17 13. Syarat pengujian papan partikel................................................................... 18 14. Syarat uji daya sekat api .............................................................................. 18 15. Syarat uji ketahanan terhadap api ................................................................ 19 16. Syarat sifat mekanis papan partikel ............................................................. 19 17. Keteguhan lentur basah................................................................................ 20 18. Syarat minimum keteguhan tarik tegak lurus permukaan papan partikel.... 21 19. Syarat minimum keteguhan cabut sekrup papan partikel ............................ 21 20. Syarat minimum modulus elastisitas papan partikel.................................... 22 21. Ukuran contoh uji papan partikel................................................................. 23 22. Bentuk penandaan pada papan partikel........................................................ 26 23. Jumlah Pengambilan contoh papan partikel ................................................ 27 24. Kelemahan dan kelebihan JIS dan SNI........................................................ 28 25. Komparasi parameter JIS A 5908-2003 dan SNI 03-2105-2006................. 28
Universitas Sumatera Utara
DAFTAR LAMPIRAN
No. Halaman 1.JIS A 5908 : 2003 ......................................................................................... 31 2. SNI 03-2105-2006 ....................................................................................... 32
Universitas Sumatera Utara
2012
ABSTRACT
JEVLEN SIMARMATA. Comparative Study of JIS A 5908-2003 with SNI 032105-2006. Supervised by YUNUS AFIFUDDIN dan LUTHFI HAKIM.
Japan and Indonesia has own criteria in determinating the applicable standards for particleboard in accordance with the development of industry in each country. JIS and SNI have weaknesses and strengths that are only applicable in their respective countries so that the necessary information to evaluate these standards in order to be valid not only in each country.
The purpose of this research is to compare JIS A 5908-2003 withSNI 032105-2006. Data analysis was done by using descriptive comparative technic that is compare standards specified in JIS A 5908-2003 andSNI 03-2105-2006 so that known weaknesses and strengths of each standard. Based on the quality of performance, quality particleboard JIS A 5908-2003 better than quality of particleboard SNI 03-2105-2006. Formaldehyde emissions of JIS A 5908-2003 is lower than SNI 03-2105-2006. Classification of particleboard based on surface condition, thickness, length and width, emissions of formaldehyde, the qualityof performances between JIS A 5908-2003 andSNI 03-2105-2006 are different. Classification of particleboard by an adhesive and Terms defined mechanical properties betweenJIS A 5908-2003 andSNI 03-2105-2006 are the same.SNI 032105-2006 not test the fire insulation and heat insulation power.JIS A 5908-2003 has more excellence compared toSNI 03-2105-2006. Based on parameters required, JIS A 5908-2003 and SNI 03-2105-2006 have more similarities.
Keywords: Particleboard, Indonesia National Standard, Japanese Industrial Standar, Compare.
Universitas Sumatera Utara
ABSTRAK
JEVLEN SIMARMATA. Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003. Dibimbing oleh YUNUS AFIFUDDIN dan LUTHFI HAKIM.
Indonesia dan Jepang memiliki kriteria tersendiri dalam menentukan standar yang berlaku untuk papan partikel sesuai dengan perkembangan industri di masing-masing negara. SNI dan JIS memiliki kelemahan dan kelebihan yang hanya berlaku di negara masing-masing sehingga diperlukan informasi untuk mengevaluasi standar tersebut agar dapat berlaku tidak hanya di masing-masing negara.
Tujuan penelitian ini adalah untuk membandingkan standar papan partikel SNI 03-2105-2006 dan JIS A 5908-2003. Analisa data dilakukan dengan teknik deskriptif komparatif yaitu membandingkan standarisasi yang ditetapkan pada JIS A 5908-2003 dan SNI 03-2105-2006 sehingga diketahui kelemahan dan kelebihan dari masing-masing standar.Berdasarkan mutu penampilan, kualitas papan partikel JIS A 5908-2003 lebih baik dibandingkan dengan kualitas papan partikel SNI 03-2105-2006. Emisi formaldehida pada JIS A 5908-2003 lebih rendah dibandingkan dengan SNI 03-2105-2006. Klasifikasi papan partikel berdasarkan kondisi permukaan, ketebalan, panjang dan lebar, emisi formaldehida, mutu penampilan antara JIS A 5908-2003 dan SNI 03-2105-2006 berbeda. Klasifikasi papan partikel berdasarkan perekat dan syarat sifat mekanis yang ditetapkan antara JIS A 5908-2003 dan SNI 03-2105-2006 adalah sama. SNI 03-2105-2006 tidak melakukan uji ketahanan terhadap api dan uji daya sekat panas.JIS A 59082003 memiliki lebih banyak kelebihan dibandingkan SNI 03-21052006.Berdasarkan parameter yang dipersyaratkan JIS A 5908-2003 dan SNI 032105-2006 lebih banyak memiliki persamaan.
Kata kunci: Papan Partikel, Standar Nasional Indonesia, Standar Industrial Jepang, Komparasi.
Universitas Sumatera Utara
PENDAHULUAN
Latar Belakang Standar Nasional Indonesia (SNI) merupakan standar yang berlaku secara
nasional di Indonesia. Standar Nasional Indonesia dirumuskan oleh panitia teknis dan ditetapkan oleh Badan Standarisasi Nasional. Japanese Industrial Standar (JIS) merupakan standar yang berlaku secara nasional di negara Jepang. Japanese Industrial Standar disusun oleh badan yang disebut Japanese Industrial Standars Committee.
Papan partikel merupakan salah satu jenis produk atau panel kayu yang terbuat dari partikel-partikel kayu atau bahan berlignoselulosa lainnya yang diikat dengan perekat sintetis atau bahan pengikat lain dan dikempa panas. Standar papan partikel yang berlaku di Indonesia adalah SNI 03-2105-2006 dan JIS A 5908-2003 merupakan standar yang berlaku di Jepang.
Indonesia dan Jepang memiliki kriteria tersendiri dalam menentukan standar yang berlaku untuk papan partikel sesuai dengan perkembangan industri di masing-masing negara. SNI dan JIS memiliki kelemahan dan kelebihan serta persamaan dan perbedaan dalam menentukan kualitas papan partikel yang berlaku di negara masing-masing. Pada penelitian ini dilakukan studi komparasi terhadap kedua standar tersebut untuk mengetahui kelemahan dan kelebihan serta persamaan dan perbedaan kedua standar. Penelitian ini akan dijadikan bahan infomasi untuk mengevaluasi kedua standar tersebut sehingga dapat berlaku tidak hanya di masing-masing negara.
Universitas Sumatera Utara
Tujuan Penelitian Penelitian ini bertujuan untuk membandingkan standar papan partikel SNI
03-2105-2006 dan JIS A 5908-2003. Manfaat Penelitian Penelitian ini bermanfaat untuk memberikan informasi meningkatkan standar yang berlaku di Indonesia dan Jepang sehingga dapat berlaku di kedua negara.
Universitas Sumatera Utara
TINJAUAN PUSTAKA
Standar didefinisikan sebagai suatu dokumen tertulis, yang naskah utamanya berisi ketentuan-ketentuan yang menunjukkan persyaratan yang perlu ditaati, dan secara umum tidak bertentangan dengan standar atau kode lain, atau bila diadopsi menjadi ketentuan hukum tidak bertentangan dengan ketentuan hukum yang berlaku.
JIS meliputi produk industri dan mineral dengan pengecualian obat, bahankimia pertanian, pupuk kimia, benang sutra, dan bahan makanan, produkpertanian dan hutan yang ditunjuk berdasarkan UndangUndangmengenai Standardisasi dan tepat Pelabelan Produk Pertanian dan Kehutanan.Simbol huruf,menunjukkan area teknis (Divisi JIS), dan jumlah 4 digit atau 5digit ditambahkan untuk menemukan JIS di tempat yang tepat alam divisi tersebut. Standardisasi item ditetapkan sebagai JIS memiliki Simbolberikut : JIS C7501: Mayoritas JIS memilikijenis simbol.JIS Q 1400: Lambang ini terutama digunakandalam JIS kasus tersebut mengadopsi standar internasional identik. JIS X 5056 : Simbol ini digunakan dalam kasus JISmengadopsi standar internasionalmenetapkan hanya sebagian dari persyaratan yang diperlukan.
Jumlah suatu Standar Industri Jepang (JIS) terdiri dari sebuahsimbol huruf Inggris dan empat (4) atau lima (5) digit angka. Angka tersebut mungkin memiliki nomor bagian setelah 4-5 angka dan sebuah tanda hubung "" Simbol hurufmenunjukkan 19 bidang teknis seperti A untuk "Teknik Sipildan Arsitektur", X untuk "Pengolahan Informasi." Dari angka tersebut,
Universitas Sumatera Utara
dua digit pertama menunjukkan sebuah divisi yang ditentukan sub-teknis daerah dan dua terakhir diberikan secara bebas. H 7501,misalnya, berarti area teknis "Bahan non-besi dan Metal" dan sebuah divisi dari "bahan fungsional". JIS jugadikategorikan ke dalam tiga domain yaitu produk, metode dan dasar. Ada sekitar 4000, 1600 dan 2800 masing-masing standar.
(JISC, 2005).
Standardisasi dapat
didefinisikan
sebagai "pengurangan,
penyederhanaan, dan
mengatur hal-hal
yang cenderung menjadi beragam, rumit, dan kacau jikadibiarkan tidak
terkendali." Standar dapat didefinisikan sebagai "aturan" yang ditetapkan oleh
standardisasi. Standardisasi industri merupakan standarisasi di sektor industri, dan
di Jepang, Standar Industri Jepang diadopsi sebagai standar industri nasional.
Berkenaan
dengan "barang"
dan "masalah",
yang cenderungmenjadi beragam, rumit,dan kacau jika dibiarkan tidak
Universitas Sumatera Utara
terkendali, standardisasi industri bertujuan untuk menetapkan tingkat "standar"
suatu wilayah dalam bentuk dokumen teknis dan untuk "menyatukan" atau
"menyederhanakan"sehingga sama diseluruh Jepang, dari berbagai sudut
pandang untukmemastikan kenyamanan dalam kegiatan ekonomi dan sosial
(menjagakesesuaian), meningkatkan
efisiensi produksi
(produksi
massaldenganmengurangikeragaman), menjaga keadilan (jaminan keuntungan
konsumen dan penyederhanaan transaksi), mempromosikan kemajuan teknologi
(dukungan untuk penciptaan pengetahuan baru dan pengembangan/penyebaran
teknologi
baru),
menjaga
keselamatan
dan kesehatan,
dan melestarikan lingkungan.(JISC, 2005).
Standar Nasional Indonesia (SNI) disusun untuk mendefinisikan ketentuan
yang berhubungan dengan industri, perdagangan, kesehatan/keselamatan, ilmu
pengetahuan dan teknologi serta komunikasi internasional. Penyusunannya
sebagai bagian dari proses perumusan SNI harus lengkap, berkesinambungan,
jelas, tepat, menggambarkan kerangka perkembangan teknologi masa depan,
lugas, tegas, tidak menimbulkan interpretasi lain dan mudah dipahami oleh pihak
yang tidak berpartisipasi dalam perumusan SNI (BSN, 2000).
Standar adalah spesifikasi teknis atau sesuatu yang dibakukan, disusun
berdasarkan konsensus semua pihak yang terkait dengan memprhatikan syarat-
syarat kesehatan, keamanan, keselamatan, prkembangan ilmu pengetahuan dan
teknologi, serta berdasarkan pengalaman, perkembangan masa kini dan masa yang
akan datang untuk memperoleh manfaat sebesar-besarnya.
Standar Nasional Indonesia (SNI) adalahdokumen berisi ketentuan teknis
(aturan, pedoman atau karakteristik) dari suatu kegiatan atau hasilnya yang
Universitas Sumatera Utara
dirumuskan secara konsensus dan ditetapkan oleh Instansi terkait untuk dipergunakan oleh stakeholder dengan tujuan mencapai keteraturan yang optimum ditinjau dari konteks keperluan tertentu. RSNI adalah naskah standar sebelum menjadi Standar Nasional Indonesia (BSN, 2000).
Tujuan SNI adalah untuk menjabarkan ketentuan secara jelas dan tidak bermakna ganda dalam hal memfasilitasi perdagangan dan komunikasi. Untuk mencapai tujuan tersebut, SNI harus :
- Cukup lengkap dalam batas lingkup yang telah ditentukan, - Konsisten, jelas dan akurat, - Memperhatikan kerangka untuk pengembangan teknologi mendatang,
dan - Dapat dipahami oleh tenaga yang berkualifikasi dan tidak ikut dalam
mempersiapkan standar tersebut (BSN, 2000). Struktur penomoran SNI terdiri atas serangkaian kode dengan arti tertentu yaitu berupa kode SNI, nomor unik, nomor bagian dan nomor seksi serta tahun penetapan. Kode SNI menyatakan bahwa dokumen tersebut adalah Standar Nasional Indonesia. Nomor unik merupakan identifikasi dari suatu standar tertentu yang jumlah digitnya sesuai dengan kebutuhan, minimal 4 digit dan dapat diawali dengan angka nol (0), kecuali untuk SNI adopsi identik, kode nomor unik sama dengan standar yang diadopsi. Nomor bagian merupakan identifikasi yang menunjukkan nomor urut bagian dari suatu standar yang mempunyai bagian. Nomor seksi merupakan identifikasi yang menunjukkan nomor urut seksi dari suatu standar bagian tertentu. Tahun penetapan sebanyak 4 digit menyatakan tahun standar tersebut ditetapkan oleh BSN.
Universitas Sumatera Utara
Universitas Sumatera Utara
METODE PENELITIAN
Waktu penelitian
Penelitian ini dilaksanakan pada bulan April hingga Juli 2012.
Bahan penelitian Bahan yang digunakan pada penelitian ini adalah standar JIS A 5908-2003
dan SNI 03-2105-2006.
Metode penelitian Penelitian ini bersifatdeskriptif, yaitu memberikan gambaran tentang JIS
A 5908-2003 dan SNI 03-2105-2006. Data yang digunakan pada penelitian ini merupakan data parameter-parameter JIS A 5908-2003 dan SNI 03-2105-2006. Analisis data dilakukan dengan teknik deskriptif komparatif yaitu membandingkan parameter-parameter yang tertera pada JIS A 5908-2003 dan SNI 03-2105-2006 sehingga diketahui kelemahan dan kelebihan dari masing-masing standar. Tahapan kegiatan tertera pada diagram alur pada Gambar 1. Tahapan kegiatan yang dilakukan adalah mengumpulkan data parameter-parameter standar JIS A 5908-2003 dan SNI 03-2105-2006, hasil perolehan data diidentifikasi dan ditabulasikan, selanjutnya dilakukan proses screening yaitu menganalisa serta membandingkan data yang ada pada kedua standar. Proses screening dilakukan untuk mendapatkan informasi tentang persamaan dan perbedaan data serta keunggulan dan kelemahan dari masing-masing standar. Hasil dari proses screening atau komparasi standar yang telah diperoleh ditabulasikan seperti yang tertera pada Tabel 1.
Universitas Sumatera Utara
JIS A 5908-2003
SNI 03-2105-2006
Identifikasi
Screening
Persamaan / Perbedaan
Keunggulan / Kelemahan
Komparasi Standar Gambar 1. Skema Metode Perancangan
Tabel 1. Komparasi parameter JIS A 5908-2003 dan SNI 03-2105-2006
SNI JIS Ketebalan
Ukuran Kadar air
MOE
…..
Ketebalan Ukuran
-
Kadar air ✓
MOE ✓
…. ….
Universitas Sumatera Utara
HASIL DAN PEMBAHASAN
Hasil dan Pembahasan JIS A 5908-2003 merupakan standar papan partikel untuk wilayah Jepang
yang secara umum dibentuk oleh partikel-partikel kayu dengan penambahan bahan perekat dan dikempa dengan kempa panas. Standar tersebut memiliki simbol berupa huruf inggris dan angka. Simbol huruf A menunjukkan bidang teknis untuk teknik sipil dan arsitektur, untuk angka 5908 menunjukkan divisi dari standar tersebut dan 2003 menunjukkan tahun penetapan standar tersebut. SNI 032105-2006 merupakan standar yang menetapkan klasifikasi mutu dan cara uji papan partikel yang diperdagangkan di Indonesia. Standar tersebut juga memiliki symbol berupa huruf inggris dan angka. Angka 03-2105 merupakan nomor unik SNI yang di revisi sedangkan 2006 merupakan tahun penetapan SNI revisi.
Standar SNI 03-2105-2006 mengacu pada standar nasional indonesia lain terkait dengan persyaratan yang berlaku maupun prosedur yang digunakan dalam pengujian, sedangkan JIS A 5908-2003 mengacu pada standar jepang (JIS) lainnya terkait dengan persyaratan yang berlaku maupun prosedur yang digunakan dalam pengujian. SNI 03-2105-2006 mengacu pada Standar Nasional Indonesia tentang kayu lapis dan produk panel kayu, sedangkan JIS A 5908-2003 mengacu pada standar yang lebih spesifik untuk pengujian serta standarisasi produk papan partikel. Standar-standar yang menjadi acuan normatif SNI 03-2105-2006 dan JIS A 5908-2003 dapat dilihat pada Tabel 2.
Universitas Sumatera Utara
Tabel 2. Acuan normatif standar JIS A 5908-2003 dan SNI 03-2105-2006
Acuan Normatif
JIS SNI
(JIS A 1321)
(SNI 01-7201-2006)
testing method for incombustibility of internal standar kayu lapis dan papan blok bermuka
finish material and procedure of buildings
kertas indah
(JIS A 1460)
(SNI 01-6050-1999)
buildings boards determination of formaldehyde cara uji emisi formaldehida pada panel
emission-desiccator method
kayu
(JIS A 1420)
(SNI 01-5008.2-2000)
determination of steady-state thermal standar kayu lapis penggunaan umum
transmission properties-hot box method
(JIS A 1408)
(SNI 01-20250-1996)
test methods of bending and impact for buildings standar kayu lapis indah dan papan blok
boards
indah
(JIS B 1112) cross-recessed head wood screws
(JIS B 7526) squares
(JIS K 7120)
testing method for colour fastness of plastics upon
exposure to light of the carbon arc
(JIS K 8355) acetic acid
(JIS K 8594) petroleum benzene
(JIS K 8264)sodium carbonate decahydrate
(JIS L 0804)grey scale for assessing change in
colour
(JIS L 0805)grey scale for assessing staining
(JIS S 6026)crayons and oil pastels
(JIS Z 8401)guide to the rounding of numbers
(JIS Z 8730)
colour specification-colour differences of object
colours
Sumber : JIS A 5908-2003 dan SNI 03-2105-2006
Papan partikel dibagi menjadi 3 macam papan yaitu papan partikel biasa (base particle board), papan partikel berlapis venir (veenered particleboard) dan papan partikel dekoratif (decorative particleboard).Berdasarkan JIS A 5908-2003, papan partikel diklasifikasikan berdasarkan kondisi bagian atas (face) dan bagian bawah (core), kekuatan lentur, perekat, jumlah emisi formaldehida, dan ketahanan terhadap api. Pada SNI 03-5908-2006 papan partikel diklasifikasikan berdasarkan mutu penampilan, perekat, tingkat pengolahan permukaan, keteguhan lentur, emisi formaldehida, tetapi untuk klasifikasi ketahanan api tidak ditetapkan pada SNI.
Universitas Sumatera Utara
Kondisi Permukaan
Standar untuk klasifikasi kondisi permukaan papan partikel berdasarkan standar JIS dan SNI tidak jauh berbeda, hanya pada standar JIS klasifikasi kondisi permukaan dibagi juga berdasarkan papan yang diamplas dan tidak diamplas seperti yang tertera pada Tabel 3.
Tabel 3. Klasifikasi papan partikel berdasarkan kondisi permukaan
Klasifikasi
Simbol Standar
Kondisi permukaan (Face dan Back)
Komparasi
Papan partikel biasa
Papan partikel berlapis venir
RN RS -
VN
VS
-
DV
DO
Papan partikel dekoratif
DC
-
JIS SNI
Kedua sisi tidak dilapisi dan tidak diamplas Kedua sisi tanpa lapisan tetapi diamplas Permukaan papan partikel tidak diberi bahan lain
Beda
Papan partikel biasa yang dilapisi venir di
JIS
kedua sisinya dan tidak diamplas Papan partikel biasa yang dilapisi venir di kedua sisinya dan diamplas
Beda
SNI
Permukaan papan partikel diberi lapisan dikedua sisinya
Venir dekoratif dilapisi di kedua sisi atau
salah satu sisi papan partikel biasa
Film atau lembaran resin sintetis, kertas
yang telah diberi resin sintetis, lapisan
kertas atau sejenisnya dilapisi di kedua sisi
atau salah satu sisi papan partikel biasa
termasuk produk yang tidak berpola yang
permukaan dekoratifnya telah diberi warna
JIS
dan produk-produk yang mengalami pengembangan atau pola-pola abstrak
Lapisan resin sintetis yang ditekan dan telah mengering atau dicetak di kedua sisi
Beda
atau salah satu sisi papan partikel biasa,
termasuk produk tidak berpola yang
permukaannya telah yang permukaan
dekoratifnya telah diberi warna dan
produk-produk yang mengalami
pengembangan atau pola-pola abstrak
Permukaan papan partikel diberi lapisan
SNI
venir indah atau kertas indah atau resin sintetis atau cat pada kedua sisi atau di
salah satu sisinya
Produk-produk papan partikel untuk pemasaran areal jepang berdasarkan
tipe permukaannya diberi tanda sesuai dengan standar JIS A 5908-2003,
Universitas Sumatera Utara
sedangkan produk untuk pemasaran tidak diberi tanda untuk menunjukkan tipe permukaannya.
Ketebalan, Panjang dan Lebar
Ukuran papan partikel berdasarkan JIS dibagi menjadi klasifikasi ketebalan seperti yang tertera pada Tabel 4. Untuk ukuran papan partikel pada SNI tidak ditetapkan klasifikasi besarnya ukuran ketebalan yang digunakan pada pembuatan papan partikel.
Tabel 4. Klasifikasi papan partikel berdasarkan ketebalan
Tipe papan partikel
Tipe 24-10, Tipe17,5-10,5 Tipe 30-15 Tipe 18 Tipe 8
Ketebalan (mm) JIS 9,5; 11; 12,7;16;19; 28,5
9, 10, 12, 15, 18, 20, 25, 30, 35, 40
SNI -
-
Komparasi Beda Beda
Tabel 5. Klasifikasi papan partikel berdasarkan panjang dan lebar
Tipe papan partikel
Tipe 24-10, Tipe17,5-10,5 Tipe 30-15 Tipe 18 Tipe 8
1820x900, 2420x900, 2730x900,
Ukuran (mm) JIS
2440 x 1220
1820x910, 1820x1210, 2420x910, 2420x1210, 2730x910, 2730x1210
SNI -
-
Komparasi Beda Beda
Ukuran panjang dan lebar papan partikel yang umum digunakan adalah
ukuran pada tipe 8, 18, dan 30-15. Akan tetapi ukuran produk papan partikel
tersebut dapat dibuat berdasarkan ukuran pesanan sesuai dengan perjanjian antara
pihak-pihak terkait.
Universitas Sumatera Utara
Toleransi dan Kesikuan
Toleransi yang diperbolehkan pada JIS A 5908-2003 dan SNI 03-59082006 untuk panjang dan lebar ± 3 mm, toleransi kesikuan (perbedaan dari garis siku) yang diperbolehkan maksimal 2 mm. Toleransi tebal yang diperbolehkan antara kedua standar ini tidak memiliki perbedaan, seperti yang terlampir pada Tabel 6.
Tabel 6. Toleransi tebal papan partikel
Macam papan partikel Papan partikel biasa Papan partikel berlapis venir Papan partikel dekoratif
Tebal (mm) < 15 ≥ 15 < 20 ≥ 20 12,7 mm sesuai dengan ketentuan yang tertera pada Tabel 9. Hal ini menunjukkan toleransi kadar air yang dipersyaratkan pada JIS untuk tipe 8 dan 24-10 lebih rendah dibandingkan dengan standar yang ditetapkan SNI.
Tabel 10. Syarat kerapatan papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir
Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5 Tipe 30-15 Tipe 18 Tipe 13 Tipe 8
Kerapatan g/cm3
JIS SNI
0,4-0,9
0,4-0,9
0,4-0,9
0,4-0,9
0,4-0,9
0,4-0,9
0,4-0,9 0,4-0,9 0,4-0,9
0,4-0,9 0,4-0,9 0,4-0,9
Komparasi
Sama Sama Sama Sama Sama Sama
Tabel 11. Syarat kadar air papan partikel
Klasifikasi
Papan partikel biasa
Papan partikel berlapis venir Papan partikel dekoratif
Tipe 24-10
Tipe 17,510,5 Tipe 30-15 Tipe 18 Tipe 13 Tipe 8
Kadar air (%)
JIS Maks 12 %
SNI
Bila tebal ≤ 12,7 mm
maksimum 25 %, Bila
tebal
> 12,7 mm
maksimum 20 %
Maks 12 % Maks 12 %
Komparasi Beda Sama
Maks 12 % Maks 12 %
Maks 12 % Maks 12 % Maks 12 % Maks 12 % Maks 12 % Tidak dipersyaratkan
Sama
Sama Sama Beda
Universitas Sumatera Utara
Tabel 12. Syarat pengembangan tebal papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir
Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5
Tipe 30-15
Tipe 18 Tipe 13 Tipe 8
Pengembangan tebal (%)
JIS SNI
5 – 13
≤ 14
5 – 13
≤ 14
5 – 13
≤ 14
5 – 13 5 – 13 5 – 13
≤ 14 ≤ 14 ≤ 14
Komparasi
Beda Beda
Beda
Beda Beda Beda
Pengujian keteguhan tarik lapisan dekoratif, ketahanan pukul, ketahanan terhadap asam, ketahanan terhadap basa , standar yang ditetapkan antara JIS dan SNI adalah sama, sedangkan untuk ketahanan papan partikel terhadap goresan pada SNI tidak ditentukan kriterianya seperti yang tertera pada Tabel 13.
Tabel 13. Syarat pengujian papan partikel
Macam pengujian Keteguhan tarik lapisan dekoratif
Ketahanan pukul
Ketahanan terhadap asam Ketahanan terhadap basa Ketahanan terhadap noda
Ketahanan terhadap perubahan warna
Ketahananterhadap goresan
JIS Minimal 0,4 N/mm2
SNI Minimal 4,0 kgf/cm2
Komparasi Sama
Bebas dari retak pada bidang radial, patah dan mengelupas pada bagian permukaan
Tidak ada perubahan warna
Tidak ada perubahan warna
Skala 3 atau lebih dalam skala gray
Penampilan bebas dari cacat seperti pembengkakan pada permukaan dan dalam skala Gray nilainya 4 atau lebih Tidak ada goresan yang jelas
Tidak ada retak dan terkelupas pada lapisan dekoratif
Tidak ada perubahan warna
Tidak ada perubahan warna Tidak ada bekas warna atau noda yang tertinggal
Tidak terjadi perubahan warna dan pemudaran kilap
Tidak ditentukan kriteria
Sama Sama Sama Beda
Beda
Beda
Pengujian daya sekat api, pada SNI tidak dilakukan sedangkan pada JIS di
uji berdasarkan ketebalan papan partikel. Untuk pengujian daya sekat api papan
Universitas Sumatera Utara
partikel hanya ditetapkan untuk papan dengan tipe 8, 18, 30-15 seperti yang tertera pada tabel 14.
Tabel 14. Syarat uji daya sekat api
Ketebalan
10 12 15 18 20 25 30 35 40
Daya tahan panas
JIS SNI
0,060
-
0,077
-
0,095
-
0,112
-
0,120
-
0,155
-
0,181
-
0,215
-
0,241
-
Komparasi
Beda Beda Beda Beda Beda Beda Beda Beda Beda
Untuk pengujian ketahanan terhadap api, pada SNI tidak ada ditetapkan pengujian sedangkan untuk JIS, grade ketahanan terhadap api ditetapkan menjadi dua yaitu grade 2 dan grade 3 seperti yang tertera pada Tabel 15. Hal ini menunjukkan produk yang di produksi berdasarkan JIS lebih baik untuk kualitas ketahanan terhadap api.
Tabel 15. Syarat uji ketahanan terhadap api
Klasifikasi
Ketahanan terhadap api grade 2 Ketahanan terhadap api grade 3
Ketahanan terhadap api JIS SNI
Grade 2
-
Grade 3
-
Komparasi Beda Beda
Satuan yang digunakan di indonesia untuk pengujian sifat mekanis adalah kgf/cm2 sedangkan satuan yang digunakan untuk JIS adalah N/mm2 seperti yang tertera pada Tabel 16 dan Tabel 17. Tetapi untuk pengujian keteguhan cabut
Universitas Sumatera Utara
sekrup satuan yang digunakan pada JIS adalah Newton, sedangkan pada SNI satuan yang digunakan adalah kgf (kilogram force).
Tabel 16. Syarat sifat mekanis papan partikel
Klasifikasi
Papan partikel biasa struktural Papan partikel berlapis venir
Papan partikel biasa dan papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5
Tipe 30-15
Tipe 18 Tipe 13 Tipe 8
Keteguhan lentur kering minimum
JIS (N/mm2)
SNI (kgf/cm2)
Arah Arah Arah Arah
panjang lebar panjang lebar
24,0 10,0 245 102
17,5 10,5 178 107
30,0 15,0 306 153
18,0 18,0 184 184 13,0 13,0 133 133 8,0 8,0 82 82
Komparasi
Sama Sama Sama Sama Sama Sama
Tabel 17. Keteguhan lentur basah
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir
Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5
Tipe 30-15
Tipe 18 Tipe 13 Tipe 8
Keteguhan lentur basah minimum JIS (N/mm2) SNI (kgf/cm2) Arah Arah Arah Arah panjang lebar panjang lebar 12,0 5,0 122 51 8,8 5,3 90 54
15,0 7,5 153 77
9,0 9,0 92 92 6,5 9,0 66 66 ----
Komparasi
Sama Sama Sama Sama Sama Sama
Klasifikasi keteguhan lentur pada JIS A 5908-2003 dan SNI 03-5908-2006 dibagi menjadi tipe 8,18, 13 untuk penggunaan papan partikel biasa dan dekoratif, tipe 24-10, 17.5-10,5 untuk papan partikel biasa struktural, tipe 30-15untuk penggunaan papan partikel berlapis venir seperti yang tertera pada Tabel 17.
Universitas Sumatera Utara
Pemberian nama tipe-tipe didasarkan pada pembagian keteguhan lentur kering masing-masing tipe. Pemberian tipe 18 dikarenakan keteguhan lentur minimumnya sebesar 18,0 N/mm2 arah panjang dan arah lebarnya, tipe 13 dikarenakan keteguhan lentur minimumnya sebesar 13,0 N/mm2 pada arah panjang dan arah lebar, tipe 8 dikarenakan keteguhan lentur minimumnya sebesar 8,0 N/mm2 pada arah panjang panjang dan arah lebarnya. Tipe 24-10 dikarenakan keteguhan lentur minimumya sebesar 24,0 N/mm2 pada arah panjang dan sebesar 10,0 N/mm2 pada arah lebar, tipe 17,5-10,5 dikarenakan keteguhan lentur minimumnya sebesar 17,5 N/mm2 pada arah panjang dan sebesar 10,5 N/mm2 pada arah lebar, Tipe 30-15 keteguhan lentur minimumnya sebesar 30,0 N/mm2 pada arah panjang dan sebesar 15,0 N/mm2 atau pada arah lebar. Tipe 24-10 berarti tipe OSB, dan tipe 17,5-10-5 berarti papan untuk tipe wafer.
Table 18. Syarat minimum keteguhan tarik tegak lurus permukaan papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5 Tipe 30-15 Tipe 18 Tipe 13 Tipe 8
Keteguhan tarik tegak lurus permukaan minimum JIS SNI
(N/mm2) (kgf/cm2) 0,3 3,1 0,3 3,1 0,3 3,1 0.3 3,1 0,2 2,0 0,15 1,5
Komparasi
Sama Sama Sama Sama Sama Sama
Universitas Sumatera Utara
Tabel 19. Syarat minimum keteguhan cabut sekrup papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5 Tipe 30-15 Tipe 18 Tipe 13 Tipe 8
Keteguhan cabut sekrup minimum JIS SNI (N) (kgf) 500 51 500 51 500 51 500 51 400 41 300 31
Komparasi
Sama Sama Sama Sama Sama Sama
Standar keteguhan tarik tegak lurus permukaan dan keteguhan cabut
sekrup papan partikel yang ditetapkan JIS dan SNI adalah sama seperti yang
tertera pada Tabel 18 dan Tabel 19. Untuk pengujian keteguhan cabut sekrup,
berdasarkan SNI pengujian keteguhan cabut sekrup hanya dilakukan untuk papan
partikel dengan ketebalan minimal 15 mm, sedangkan pada JIS tidak ditentukan
tebal minimum papan partikel yang akan di uji.
Modulus elastisitas merupakan ukuran kemampuan kayu untuk menahanperubahan bentuk atau lentur yang terjadi sampai dengan batas proporsi.Nilai Modulus elastisitas yang ditetapkan oleh JIS dan SNI adalah sama, akan tetapi satuan yang digunakan untuk nilai berbeda, JIS menggunakan satuan N/mm2 sedangkan SNI menggunakan kgf/cm2 seperti yang tertera pada Tabel 20.
Universitas Sumatera Utara
Tabel 20. Syarat minimum modulus elastisitas papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir Papan partikel dekoratif
Tipe 24-10
Tipe 17,510,5
Tipe 30-15
Tipe 18 Tipe 13 Tipe 8
Modulus elastisitas minimum
JIS (N/mm2)
SNI (kgf/cm2)
4000 arah panjang, 4,08 arah panjang;
1300 arah lebar
1,33 arah lebar
3000 arah panjang; 3,06 arah panjang;
2000 arah lebar
2,04 arah lebar
4000 arah panjang; 4,59 arah panjang;
2800 arah lebar
2,86 arah lebar
3000 arah lebar
3,06 arah lebar
2500 arah lebar
2,55 arah lebar
2000 arah lebar
2,04 arah lebar
Komparasi
Sama
Sama
Sama Sama Sama Sama
Pengujian Papan Partikel
Ukuran contoh uji papan partikel yang ditetapkan JIS dan SNI tidak berbeda untuk semua pengujian kecuali pada pengujian emisi formaldehida yang diuji berdasarkan standar emisi formaldehida masing-masing negara, serta pengujian daya sekat api dan ketahan terhadap api yang tidak diujikan pada SNI. Pada JIS pengujian emisi formaldehida mengacu pada JIS A 1460, sedangkan pada SNI mengacu pada SNI 6050-1999 seperti yang tertera pada Tabel 21.
Universitas Sumatera Utara
Tabel 21. Ukuran contoh uji papan partikel
JIS
No Macam pengujian Ukuran Banyaknya
contoh uji contoh uji
1 Kerapatan
100 x 100
1
2 Kadar air
100 x 100
1
3
Pengembangan tebal setelah direndam air
50 x 50
1
4
Keteguhan lentur (kering)
Lebar 50 x Arah
panjang (S panjang 1,
+ 50)
arah lebar 1
5
Keteguhan lentur (basah)
Lebar 50 x Arah
panjang (S panjang 1,
+ 50)
arah lebar 1
6
Keteguhan tarik tegak lurus permukaan
50 x 50
1
7
Keteguhan cabut sekrup
50 x 100
1
50 x 150 Mengacu
8 Emisi formaldehida
pada JIS A
1460
9
Keteguhan tarik lapisan dekoratif
50 x 50
1
10 Keteguhan pukul
300 x 300
1
Ukuran contoh uji 100 x 100 100 x 100
SNI Banyaknya contoh uji 1 1
50 x 50
1
Lebar 50 x panjang (S + 50) Lebar 50 x panjang (S + 50)
Arah panjang 1, arah lebar 1
Arah panjang 1, arah lebar 1
50 x 50
1
50 x 100
1
50 x 100
Mengacu pada SNI 60501999
50 x 50
1
300 x 300
1
Komparasi Sama Sama Sama
Sama
Sama
Sama Sama
Sama
Sama Sama
11
Ketahanan terhadap asam
100 x 100
1
12
Ketahanan terhadap basa
100 x 100
1
13
Ketahanan terhadap noda
100 x 100
1
14
Ketahanan terhadap perubahan warna
150 x 150
1
1(3 untuk
15
Ketahanan terhadap goresan
50 x 50
yang lebih dari 1
warna)
16 Uji daya sekat panas 900 x 900
1
17 Ketahanan terhadap api 220 x 220
1
100 x 100 100 x 100
100 x 100 150 x 150
50 x 50
-
1
1
1
1 1 ( 3 untuk yang lebih dari 1 warna)
-
Sama Sama Sama Sama
Sama
Beda Beda
Untuk pengambilan contoh uji sebaiknya diambil pada sekitar bagian
tengah dan untuk papan dekoratif dengan alur pada permukaan dekoratif, contoh
uji yang diambil harus sampel dengan bagian alur. Kondisi contoh uji yang
dibawah kondisi kering udara atau mencapai kondisi berat yang konstan pada suhu 20±20 C dan kelembaban sekitar 65±5 %. Dalam hal ini kondisi kering udara
adalah kondisi contoh uji telah dikeringkan selama 7 hari atau lebih pada ruangan
Universitas Sumatera Utara
dengan ventilasi dan berat konstan adalah perubahan berat yang di ukur sebesar 0,1% setiap 24 jam.
Untuk pengujian kerapatan, antara JIS dan SNI tidak memiliki perbedaan yaitu pengujian dilakukan dengan pengukuran panjang dan lebar contoh uji di kedua sisinya, 25 mm dari tepi dengan ketelitian 0,1 mm, pengukuran tebal contoh uji pada keempat sudutnya, 25 mm dari keempat sudutnya (pada titik persilangan pengukuran panjang dan lebar) dengan ketelitian 0,05 mm, pengukuran berat dilakukan dengan ketelitian 0,1 g dan penghitungan kerapatan dilakukan dengan rumus yang berlaku dengan ketelitian 0,01 g/cm3. Untuk pengujian kadar air, antara JIS dn SNI tidak memiliki perbedaan yaitu contoh uji ditimbang beratnya untuk mengetahui berat awal dengan ketelitian 0,1gram, contoh uji dikeringkan kedalam oven pada suhu 103±20C lalu ditimbang hingga perbedaan berat maksimum 0,1 %.
Untuk pengujian pengembangan tebal, terdapat perbedaan terhadap suhu air yang dipakai untuk pengujian rendaman contoh uji. Pada JIS suhu air yang dipakai adalah 20±10C sedangkan pada SNI suhu air yang dipakai adalah 25±10C. Hal ini dikarenakan Indonesia merupakan daerah tropis sedangkan jepang merupakan da
HASIL PENELITIAN
Oleh Jevlen Joel Simarmata 071203035/Teknologi Hasil Hutan
DEPARTEMEN KEHUTANAN FAKULTAS PERTANIAN
UNIVERSITAS SUMATERA UTARA
Universitas Sumatera Utara
2012
ABSTRACT
JEVLEN SIMARMATA. Comparative Study of JIS A 5908-2003 with SNI 032105-2006. Supervised by YUNUS AFIFUDDIN dan LUTHFI HAKIM.
Japan and Indonesia has own criteria in determinating the applicable standards for particleboard in accordance with the development of industry in each country. JIS and SNI have weaknesses and strengths that are only applicable in their respective countries so that the necessary information to evaluate these standards in order to be valid not only in each country.
The purpose of this research is to compare JIS A 5908-2003 withSNI 032105-2006. Data analysis was done by using descriptive comparative technic that is compare standards specified in JIS A 5908-2003 andSNI 03-2105-2006 so that known weaknesses and strengths of each standard. Based on the quality of performance, quality particleboard JIS A 5908-2003 better than quality of particleboard SNI 03-2105-2006. Formaldehyde emissions of JIS A 5908-2003 is lower than SNI 03-2105-2006. Classification of particleboard based on surface condition, thickness, length and width, emissions of formaldehyde, the qualityof performances between JIS A 5908-2003 andSNI 03-2105-2006 are different. Classification of particleboard by an adhesive and Terms defined mechanical properties betweenJIS A 5908-2003 andSNI 03-2105-2006 are the same.SNI 032105-2006 not test the fire insulation and heat insulation power.JIS A 5908-2003 has more excellence compared toSNI 03-2105-2006. Based on parameters required, JIS A 5908-2003 and SNI 03-2105-2006 have more similarities.
Keywords: Particleboard, Indonesia National Standard, Japanese Industrial Standar, Compare.
Universitas Sumatera Utara
ABSTRAK
JEVLEN SIMARMATA. Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003. Dibimbing oleh YUNUS AFIFUDDIN dan LUTHFI HAKIM.
Indonesia dan Jepang memiliki kriteria tersendiri dalam menentukan standar yang berlaku untuk papan partikel sesuai dengan perkembangan industri di masing-masing negara. SNI dan JIS memiliki kelemahan dan kelebihan yang hanya berlaku di negara masing-masing sehingga diperlukan informasi untuk mengevaluasi standar tersebut agar dapat berlaku tidak hanya di masing-masing negara.
Tujuan penelitian ini adalah untuk membandingkan standar papan partikel SNI 03-2105-2006 dan JIS A 5908-2003. Analisa data dilakukan dengan teknik deskriptif komparatif yaitu membandingkan standarisasi yang ditetapkan pada JIS A 5908-2003 dan SNI 03-2105-2006 sehingga diketahui kelemahan dan kelebihan dari masing-masing standar.Berdasarkan mutu penampilan, kualitas papan partikel JIS A 5908-2003 lebih baik dibandingkan dengan kualitas papan partikel SNI 03-2105-2006. Emisi formaldehida pada JIS A 5908-2003 lebih rendah dibandingkan dengan SNI 03-2105-2006. Klasifikasi papan partikel berdasarkan kondisi permukaan, ketebalan, panjang dan lebar, emisi formaldehida, mutu penampilan antara JIS A 5908-2003 dan SNI 03-2105-2006 berbeda. Klasifikasi papan partikel berdasarkan perekat dan syarat sifat mekanis yang ditetapkan antara JIS A 5908-2003 dan SNI 03-2105-2006 adalah sama. SNI 03-2105-2006 tidak melakukan uji ketahanan terhadap api dan uji daya sekat panas.JIS A 59082003 memiliki lebih banyak kelebihan dibandingkan SNI 03-21052006.Berdasarkan parameter yang dipersyaratkan JIS A 5908-2003 dan SNI 032105-2006 lebih banyak memiliki persamaan.
Kata kunci: Papan Partikel, Standar Nasional Indonesia, Standar Industrial Jepang, Komparasi.
Universitas Sumatera Utara
RIWAYAT HIDUP
Penulis dilahirkan di Berastagi, Kabupaten Karo pada tanggal 3 Februari 1989 dari Ayah A. Simarmata dan IbuK. Naibaho. Penulis adalah anak keempat dari empat bersaudara.
Penulis menyelesaikan Sekolah Dasar di SD Letjen Djamin Ginting Berastagi, Kabupaten Karo pada tahun 2000, Sekolah Lanjutan Tingkat Pertama (SLTP) di SLTP Negeri 1 Berastagi, Kabupaten Karo tahun 2003, dan Sekolah Menengah Kejuruan (SMK) di SMK Negeri 1 Berastagi, Kabupaten Karo tahun 2006. Tahun 2007 penulis kuliah di Universitas Sumatera Utara (USU) melalui jalur Seleksi Penerimaan Mahasiswa Baru (SPMB). Penulis memilih Program Studi Teknologi Hasil Hutan, Departemen Kehutanan.
Pada tahun 2009, penulis mengikuti kegiatan Praktik Pengenalan dan Pengelolaan Hutan (P3H) di Pulau Sembilan dan Aras Napal, Kabupaten Langkat Provinsi Sumatera Utara. Pada Tahun 2011, penulis juga melaksanakan Praktik Kerja Lapangan (PKL) di Taman Nasional Baluran Surabaya, Provinsi Jawa Timur selama 1 bulan. Penulis melaksanakan penelitiandengan judul ”Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003”, di bawah bimbingan Bapak Yunus Afifuddin S.Hut., M.Si.dan Bapak Luthfi Hakim S.Hut., M.Si.
Universitas Sumatera Utara
KATA PENGANTAR
Puji dan syukur penulis ucapkan kehadirat Tuhan Yang Maha Esa,atas kasih dan karunia-Nyapenulis dapat menyelesaikan skripsi yang berjudul ”Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003”. SkripsiinimerupakansalahsatusyaratuntukmenjadiSarjanaKehutanan.
Penulis menyampaikan terima kasih kepada kedua orang tua, abang, dan
kakak
penulis
yang
selalumendoakan,
memberidukungan,
kasihsayangdanmaterisertamenginspirasipenulisuntuktetapsemangatdalammewuju
dkanskripsiinisertakepada teman-teman THH angkatan 2007 yang
selalumembantu sertamemberidorongandalammengerjakanskripsiini. Penulis juga
mengucapkan terima kasih kepada komisi pembimbing skripsiyaituBapak Yunus
Afifuddin S.Hut., M.Si.danBapak Luthfi Hakim S.Hut., M.Si. selakuketuadan
anggotakomisi pembimbing yang telah membimbing dan memberikan berbagai
masukan berharga serta saran dalam pembuatan skripsiini.
Penulis menyadari terdapat beberapa kekurangan dalam penulisan skripsi ini, oleh karena itu penulis memohon maaf atas kekurangan tersebut. Penulis mengharapkan agar skripsiinidapatmenjadipanduanbelajardanbacaan yang bermanfaatbagimahasiswa/i kehutanansecarakhususdanmasyarakatsecaraumum. Akhir kata penulis menyampaikan terima kasih.
Medan, Juli 2012
Penulis
Universitas Sumatera Utara
DAFTAR ISI
Halaman
ABSTRACT....................................................................................................... i ABSTRAK ....................................................................................................... ii RIWAYAT HIDUP ......................................................................................... iii KATA PENGANTAR ..................................................................................... iv DAFTAR ISI.................................................................................................... v DAFTAR TABEL............................................................................................ vi DAFTAR LAMPIRAN.................................................................................... vii PENDAHULUAN Latar Belakang ................................................................................................. 1 Tujuan Penelitian ............................................................................................. 2 Manfaat Penelitian ........................................................................................... 2
TINJAUAN PUSTAKA Japanese Industrial Standard ........................................................................... 3 Standar Nasional Indonesia ............................................................................. 5 METODE PENELITIAN Waktu Penelitian ............................................................................................. 7 Bahan Penelitian .............................................................................................. 7 Metode Penelitian ............................................................................................ 7
HASIL DAN PEMBAHASAN Kondisi permukaan .......................................................................................... 11 Ketebalan, Panjang dan Lebar ......................................................................... 12 Toleransi dan Kesikuan.................................................................................... 13 Perekat.............................................................................................................. 13 Emisi Formaldehida ......................................................................................... 15 Mutu Penampilan ............................................................................................. 15 Syarat Sifat Fisis dan Mekanis......................................................................... 16 Pengujian Papan Partikel ................................................................................. 22 KESIMPULAN................................................................................................ 29 DAFTAR PUSTAKA ...................................................................................... 30 LAMPIRAN..................................................................................................... 30
Universitas Sumatera Utara
DAFTAR TABEL
No. Halaman
1. Komparasi parameter JIS A 5908-2003 dan SNI 03-2105-2006.................. 8 2. Acuan normatif standar JIS A 5908-2003 dan SNI 03-2105-2006.............. 10 3. Klasifikasi papan partikel berdasarkan kondisi permukaan......................... 11 4. Klasifikasi papan partikel berdasarkan ketebalan........................................ 12 5. Klasifikasi papan partikel berdasarkan panjang dan lebar........................... 12 6. Toleransi tebal papan partikel...................................................................... 13 7. Klasifikasi papan partikel berdasarkan perekat ........................................... 14 8. Klasifikasi papan partikel berdasarkan emisi formaldehida ........................ 15 9. Syarat umum papan partikel biasa ............................................................... 16 10. Syarat kerapatan papan partikel ................................................................... 16 11. Syarat kadar air papan partikel .................................................................... 17 12. Syarat pengembangan tebal papan partikel.................................................. 17 13. Syarat pengujian papan partikel................................................................... 18 14. Syarat uji daya sekat api .............................................................................. 18 15. Syarat uji ketahanan terhadap api ................................................................ 19 16. Syarat sifat mekanis papan partikel ............................................................. 19 17. Keteguhan lentur basah................................................................................ 20 18. Syarat minimum keteguhan tarik tegak lurus permukaan papan partikel.... 21 19. Syarat minimum keteguhan cabut sekrup papan partikel ............................ 21 20. Syarat minimum modulus elastisitas papan partikel.................................... 22 21. Ukuran contoh uji papan partikel................................................................. 23 22. Bentuk penandaan pada papan partikel........................................................ 26 23. Jumlah Pengambilan contoh papan partikel ................................................ 27 24. Kelemahan dan kelebihan JIS dan SNI........................................................ 28 25. Komparasi parameter JIS A 5908-2003 dan SNI 03-2105-2006................. 28
Universitas Sumatera Utara
DAFTAR LAMPIRAN
No. Halaman 1.JIS A 5908 : 2003 ......................................................................................... 31 2. SNI 03-2105-2006 ....................................................................................... 32
Universitas Sumatera Utara
2012
ABSTRACT
JEVLEN SIMARMATA. Comparative Study of JIS A 5908-2003 with SNI 032105-2006. Supervised by YUNUS AFIFUDDIN dan LUTHFI HAKIM.
Japan and Indonesia has own criteria in determinating the applicable standards for particleboard in accordance with the development of industry in each country. JIS and SNI have weaknesses and strengths that are only applicable in their respective countries so that the necessary information to evaluate these standards in order to be valid not only in each country.
The purpose of this research is to compare JIS A 5908-2003 withSNI 032105-2006. Data analysis was done by using descriptive comparative technic that is compare standards specified in JIS A 5908-2003 andSNI 03-2105-2006 so that known weaknesses and strengths of each standard. Based on the quality of performance, quality particleboard JIS A 5908-2003 better than quality of particleboard SNI 03-2105-2006. Formaldehyde emissions of JIS A 5908-2003 is lower than SNI 03-2105-2006. Classification of particleboard based on surface condition, thickness, length and width, emissions of formaldehyde, the qualityof performances between JIS A 5908-2003 andSNI 03-2105-2006 are different. Classification of particleboard by an adhesive and Terms defined mechanical properties betweenJIS A 5908-2003 andSNI 03-2105-2006 are the same.SNI 032105-2006 not test the fire insulation and heat insulation power.JIS A 5908-2003 has more excellence compared toSNI 03-2105-2006. Based on parameters required, JIS A 5908-2003 and SNI 03-2105-2006 have more similarities.
Keywords: Particleboard, Indonesia National Standard, Japanese Industrial Standar, Compare.
Universitas Sumatera Utara
ABSTRAK
JEVLEN SIMARMATA. Studi Komparasi SNI 03-2105-2006 dengan JIS A 5908-2003. Dibimbing oleh YUNUS AFIFUDDIN dan LUTHFI HAKIM.
Indonesia dan Jepang memiliki kriteria tersendiri dalam menentukan standar yang berlaku untuk papan partikel sesuai dengan perkembangan industri di masing-masing negara. SNI dan JIS memiliki kelemahan dan kelebihan yang hanya berlaku di negara masing-masing sehingga diperlukan informasi untuk mengevaluasi standar tersebut agar dapat berlaku tidak hanya di masing-masing negara.
Tujuan penelitian ini adalah untuk membandingkan standar papan partikel SNI 03-2105-2006 dan JIS A 5908-2003. Analisa data dilakukan dengan teknik deskriptif komparatif yaitu membandingkan standarisasi yang ditetapkan pada JIS A 5908-2003 dan SNI 03-2105-2006 sehingga diketahui kelemahan dan kelebihan dari masing-masing standar.Berdasarkan mutu penampilan, kualitas papan partikel JIS A 5908-2003 lebih baik dibandingkan dengan kualitas papan partikel SNI 03-2105-2006. Emisi formaldehida pada JIS A 5908-2003 lebih rendah dibandingkan dengan SNI 03-2105-2006. Klasifikasi papan partikel berdasarkan kondisi permukaan, ketebalan, panjang dan lebar, emisi formaldehida, mutu penampilan antara JIS A 5908-2003 dan SNI 03-2105-2006 berbeda. Klasifikasi papan partikel berdasarkan perekat dan syarat sifat mekanis yang ditetapkan antara JIS A 5908-2003 dan SNI 03-2105-2006 adalah sama. SNI 03-2105-2006 tidak melakukan uji ketahanan terhadap api dan uji daya sekat panas.JIS A 59082003 memiliki lebih banyak kelebihan dibandingkan SNI 03-21052006.Berdasarkan parameter yang dipersyaratkan JIS A 5908-2003 dan SNI 032105-2006 lebih banyak memiliki persamaan.
Kata kunci: Papan Partikel, Standar Nasional Indonesia, Standar Industrial Jepang, Komparasi.
Universitas Sumatera Utara
PENDAHULUAN
Latar Belakang Standar Nasional Indonesia (SNI) merupakan standar yang berlaku secara
nasional di Indonesia. Standar Nasional Indonesia dirumuskan oleh panitia teknis dan ditetapkan oleh Badan Standarisasi Nasional. Japanese Industrial Standar (JIS) merupakan standar yang berlaku secara nasional di negara Jepang. Japanese Industrial Standar disusun oleh badan yang disebut Japanese Industrial Standars Committee.
Papan partikel merupakan salah satu jenis produk atau panel kayu yang terbuat dari partikel-partikel kayu atau bahan berlignoselulosa lainnya yang diikat dengan perekat sintetis atau bahan pengikat lain dan dikempa panas. Standar papan partikel yang berlaku di Indonesia adalah SNI 03-2105-2006 dan JIS A 5908-2003 merupakan standar yang berlaku di Jepang.
Indonesia dan Jepang memiliki kriteria tersendiri dalam menentukan standar yang berlaku untuk papan partikel sesuai dengan perkembangan industri di masing-masing negara. SNI dan JIS memiliki kelemahan dan kelebihan serta persamaan dan perbedaan dalam menentukan kualitas papan partikel yang berlaku di negara masing-masing. Pada penelitian ini dilakukan studi komparasi terhadap kedua standar tersebut untuk mengetahui kelemahan dan kelebihan serta persamaan dan perbedaan kedua standar. Penelitian ini akan dijadikan bahan infomasi untuk mengevaluasi kedua standar tersebut sehingga dapat berlaku tidak hanya di masing-masing negara.
Universitas Sumatera Utara
Tujuan Penelitian Penelitian ini bertujuan untuk membandingkan standar papan partikel SNI
03-2105-2006 dan JIS A 5908-2003. Manfaat Penelitian Penelitian ini bermanfaat untuk memberikan informasi meningkatkan standar yang berlaku di Indonesia dan Jepang sehingga dapat berlaku di kedua negara.
Universitas Sumatera Utara
TINJAUAN PUSTAKA
Standar didefinisikan sebagai suatu dokumen tertulis, yang naskah utamanya berisi ketentuan-ketentuan yang menunjukkan persyaratan yang perlu ditaati, dan secara umum tidak bertentangan dengan standar atau kode lain, atau bila diadopsi menjadi ketentuan hukum tidak bertentangan dengan ketentuan hukum yang berlaku.
JIS meliputi produk industri dan mineral dengan pengecualian obat, bahankimia pertanian, pupuk kimia, benang sutra, dan bahan makanan, produkpertanian dan hutan yang ditunjuk berdasarkan UndangUndangmengenai Standardisasi dan tepat Pelabelan Produk Pertanian dan Kehutanan.Simbol huruf,menunjukkan area teknis (Divisi JIS), dan jumlah 4 digit atau 5digit ditambahkan untuk menemukan JIS di tempat yang tepat alam divisi tersebut. Standardisasi item ditetapkan sebagai JIS memiliki Simbolberikut : JIS C7501: Mayoritas JIS memilikijenis simbol.JIS Q 1400: Lambang ini terutama digunakandalam JIS kasus tersebut mengadopsi standar internasional identik. JIS X 5056 : Simbol ini digunakan dalam kasus JISmengadopsi standar internasionalmenetapkan hanya sebagian dari persyaratan yang diperlukan.
Jumlah suatu Standar Industri Jepang (JIS) terdiri dari sebuahsimbol huruf Inggris dan empat (4) atau lima (5) digit angka. Angka tersebut mungkin memiliki nomor bagian setelah 4-5 angka dan sebuah tanda hubung "" Simbol hurufmenunjukkan 19 bidang teknis seperti A untuk "Teknik Sipildan Arsitektur", X untuk "Pengolahan Informasi." Dari angka tersebut,
Universitas Sumatera Utara
dua digit pertama menunjukkan sebuah divisi yang ditentukan sub-teknis daerah dan dua terakhir diberikan secara bebas. H 7501,misalnya, berarti area teknis "Bahan non-besi dan Metal" dan sebuah divisi dari "bahan fungsional". JIS jugadikategorikan ke dalam tiga domain yaitu produk, metode dan dasar. Ada sekitar 4000, 1600 dan 2800 masing-masing standar.
(JISC, 2005).
Standardisasi dapat
didefinisikan
sebagai "pengurangan,
penyederhanaan, dan
mengatur hal-hal
yang cenderung menjadi beragam, rumit, dan kacau jikadibiarkan tidak
terkendali." Standar dapat didefinisikan sebagai "aturan" yang ditetapkan oleh
standardisasi. Standardisasi industri merupakan standarisasi di sektor industri, dan
di Jepang, Standar Industri Jepang diadopsi sebagai standar industri nasional.
Berkenaan
dengan "barang"
dan "masalah",
yang cenderungmenjadi beragam, rumit,dan kacau jika dibiarkan tidak
Universitas Sumatera Utara
terkendali, standardisasi industri bertujuan untuk menetapkan tingkat "standar"
suatu wilayah dalam bentuk dokumen teknis dan untuk "menyatukan" atau
"menyederhanakan"sehingga sama diseluruh Jepang, dari berbagai sudut
pandang untukmemastikan kenyamanan dalam kegiatan ekonomi dan sosial
(menjagakesesuaian), meningkatkan
efisiensi produksi
(produksi
massaldenganmengurangikeragaman), menjaga keadilan (jaminan keuntungan
konsumen dan penyederhanaan transaksi), mempromosikan kemajuan teknologi
(dukungan untuk penciptaan pengetahuan baru dan pengembangan/penyebaran
teknologi
baru),
menjaga
keselamatan
dan kesehatan,
dan melestarikan lingkungan.(JISC, 2005).
Standar Nasional Indonesia (SNI) disusun untuk mendefinisikan ketentuan
yang berhubungan dengan industri, perdagangan, kesehatan/keselamatan, ilmu
pengetahuan dan teknologi serta komunikasi internasional. Penyusunannya
sebagai bagian dari proses perumusan SNI harus lengkap, berkesinambungan,
jelas, tepat, menggambarkan kerangka perkembangan teknologi masa depan,
lugas, tegas, tidak menimbulkan interpretasi lain dan mudah dipahami oleh pihak
yang tidak berpartisipasi dalam perumusan SNI (BSN, 2000).
Standar adalah spesifikasi teknis atau sesuatu yang dibakukan, disusun
berdasarkan konsensus semua pihak yang terkait dengan memprhatikan syarat-
syarat kesehatan, keamanan, keselamatan, prkembangan ilmu pengetahuan dan
teknologi, serta berdasarkan pengalaman, perkembangan masa kini dan masa yang
akan datang untuk memperoleh manfaat sebesar-besarnya.
Standar Nasional Indonesia (SNI) adalahdokumen berisi ketentuan teknis
(aturan, pedoman atau karakteristik) dari suatu kegiatan atau hasilnya yang
Universitas Sumatera Utara
dirumuskan secara konsensus dan ditetapkan oleh Instansi terkait untuk dipergunakan oleh stakeholder dengan tujuan mencapai keteraturan yang optimum ditinjau dari konteks keperluan tertentu. RSNI adalah naskah standar sebelum menjadi Standar Nasional Indonesia (BSN, 2000).
Tujuan SNI adalah untuk menjabarkan ketentuan secara jelas dan tidak bermakna ganda dalam hal memfasilitasi perdagangan dan komunikasi. Untuk mencapai tujuan tersebut, SNI harus :
- Cukup lengkap dalam batas lingkup yang telah ditentukan, - Konsisten, jelas dan akurat, - Memperhatikan kerangka untuk pengembangan teknologi mendatang,
dan - Dapat dipahami oleh tenaga yang berkualifikasi dan tidak ikut dalam
mempersiapkan standar tersebut (BSN, 2000). Struktur penomoran SNI terdiri atas serangkaian kode dengan arti tertentu yaitu berupa kode SNI, nomor unik, nomor bagian dan nomor seksi serta tahun penetapan. Kode SNI menyatakan bahwa dokumen tersebut adalah Standar Nasional Indonesia. Nomor unik merupakan identifikasi dari suatu standar tertentu yang jumlah digitnya sesuai dengan kebutuhan, minimal 4 digit dan dapat diawali dengan angka nol (0), kecuali untuk SNI adopsi identik, kode nomor unik sama dengan standar yang diadopsi. Nomor bagian merupakan identifikasi yang menunjukkan nomor urut bagian dari suatu standar yang mempunyai bagian. Nomor seksi merupakan identifikasi yang menunjukkan nomor urut seksi dari suatu standar bagian tertentu. Tahun penetapan sebanyak 4 digit menyatakan tahun standar tersebut ditetapkan oleh BSN.
Universitas Sumatera Utara
Universitas Sumatera Utara
METODE PENELITIAN
Waktu penelitian
Penelitian ini dilaksanakan pada bulan April hingga Juli 2012.
Bahan penelitian Bahan yang digunakan pada penelitian ini adalah standar JIS A 5908-2003
dan SNI 03-2105-2006.
Metode penelitian Penelitian ini bersifatdeskriptif, yaitu memberikan gambaran tentang JIS
A 5908-2003 dan SNI 03-2105-2006. Data yang digunakan pada penelitian ini merupakan data parameter-parameter JIS A 5908-2003 dan SNI 03-2105-2006. Analisis data dilakukan dengan teknik deskriptif komparatif yaitu membandingkan parameter-parameter yang tertera pada JIS A 5908-2003 dan SNI 03-2105-2006 sehingga diketahui kelemahan dan kelebihan dari masing-masing standar. Tahapan kegiatan tertera pada diagram alur pada Gambar 1. Tahapan kegiatan yang dilakukan adalah mengumpulkan data parameter-parameter standar JIS A 5908-2003 dan SNI 03-2105-2006, hasil perolehan data diidentifikasi dan ditabulasikan, selanjutnya dilakukan proses screening yaitu menganalisa serta membandingkan data yang ada pada kedua standar. Proses screening dilakukan untuk mendapatkan informasi tentang persamaan dan perbedaan data serta keunggulan dan kelemahan dari masing-masing standar. Hasil dari proses screening atau komparasi standar yang telah diperoleh ditabulasikan seperti yang tertera pada Tabel 1.
Universitas Sumatera Utara
JIS A 5908-2003
SNI 03-2105-2006
Identifikasi
Screening
Persamaan / Perbedaan
Keunggulan / Kelemahan
Komparasi Standar Gambar 1. Skema Metode Perancangan
Tabel 1. Komparasi parameter JIS A 5908-2003 dan SNI 03-2105-2006
SNI JIS Ketebalan
Ukuran Kadar air
MOE
…..
Ketebalan Ukuran
-
Kadar air ✓
MOE ✓
…. ….
Universitas Sumatera Utara
HASIL DAN PEMBAHASAN
Hasil dan Pembahasan JIS A 5908-2003 merupakan standar papan partikel untuk wilayah Jepang
yang secara umum dibentuk oleh partikel-partikel kayu dengan penambahan bahan perekat dan dikempa dengan kempa panas. Standar tersebut memiliki simbol berupa huruf inggris dan angka. Simbol huruf A menunjukkan bidang teknis untuk teknik sipil dan arsitektur, untuk angka 5908 menunjukkan divisi dari standar tersebut dan 2003 menunjukkan tahun penetapan standar tersebut. SNI 032105-2006 merupakan standar yang menetapkan klasifikasi mutu dan cara uji papan partikel yang diperdagangkan di Indonesia. Standar tersebut juga memiliki symbol berupa huruf inggris dan angka. Angka 03-2105 merupakan nomor unik SNI yang di revisi sedangkan 2006 merupakan tahun penetapan SNI revisi.
Standar SNI 03-2105-2006 mengacu pada standar nasional indonesia lain terkait dengan persyaratan yang berlaku maupun prosedur yang digunakan dalam pengujian, sedangkan JIS A 5908-2003 mengacu pada standar jepang (JIS) lainnya terkait dengan persyaratan yang berlaku maupun prosedur yang digunakan dalam pengujian. SNI 03-2105-2006 mengacu pada Standar Nasional Indonesia tentang kayu lapis dan produk panel kayu, sedangkan JIS A 5908-2003 mengacu pada standar yang lebih spesifik untuk pengujian serta standarisasi produk papan partikel. Standar-standar yang menjadi acuan normatif SNI 03-2105-2006 dan JIS A 5908-2003 dapat dilihat pada Tabel 2.
Universitas Sumatera Utara
Tabel 2. Acuan normatif standar JIS A 5908-2003 dan SNI 03-2105-2006
Acuan Normatif
JIS SNI
(JIS A 1321)
(SNI 01-7201-2006)
testing method for incombustibility of internal standar kayu lapis dan papan blok bermuka
finish material and procedure of buildings
kertas indah
(JIS A 1460)
(SNI 01-6050-1999)
buildings boards determination of formaldehyde cara uji emisi formaldehida pada panel
emission-desiccator method
kayu
(JIS A 1420)
(SNI 01-5008.2-2000)
determination of steady-state thermal standar kayu lapis penggunaan umum
transmission properties-hot box method
(JIS A 1408)
(SNI 01-20250-1996)
test methods of bending and impact for buildings standar kayu lapis indah dan papan blok
boards
indah
(JIS B 1112) cross-recessed head wood screws
(JIS B 7526) squares
(JIS K 7120)
testing method for colour fastness of plastics upon
exposure to light of the carbon arc
(JIS K 8355) acetic acid
(JIS K 8594) petroleum benzene
(JIS K 8264)sodium carbonate decahydrate
(JIS L 0804)grey scale for assessing change in
colour
(JIS L 0805)grey scale for assessing staining
(JIS S 6026)crayons and oil pastels
(JIS Z 8401)guide to the rounding of numbers
(JIS Z 8730)
colour specification-colour differences of object
colours
Sumber : JIS A 5908-2003 dan SNI 03-2105-2006
Papan partikel dibagi menjadi 3 macam papan yaitu papan partikel biasa (base particle board), papan partikel berlapis venir (veenered particleboard) dan papan partikel dekoratif (decorative particleboard).Berdasarkan JIS A 5908-2003, papan partikel diklasifikasikan berdasarkan kondisi bagian atas (face) dan bagian bawah (core), kekuatan lentur, perekat, jumlah emisi formaldehida, dan ketahanan terhadap api. Pada SNI 03-5908-2006 papan partikel diklasifikasikan berdasarkan mutu penampilan, perekat, tingkat pengolahan permukaan, keteguhan lentur, emisi formaldehida, tetapi untuk klasifikasi ketahanan api tidak ditetapkan pada SNI.
Universitas Sumatera Utara
Kondisi Permukaan
Standar untuk klasifikasi kondisi permukaan papan partikel berdasarkan standar JIS dan SNI tidak jauh berbeda, hanya pada standar JIS klasifikasi kondisi permukaan dibagi juga berdasarkan papan yang diamplas dan tidak diamplas seperti yang tertera pada Tabel 3.
Tabel 3. Klasifikasi papan partikel berdasarkan kondisi permukaan
Klasifikasi
Simbol Standar
Kondisi permukaan (Face dan Back)
Komparasi
Papan partikel biasa
Papan partikel berlapis venir
RN RS -
VN
VS
-
DV
DO
Papan partikel dekoratif
DC
-
JIS SNI
Kedua sisi tidak dilapisi dan tidak diamplas Kedua sisi tanpa lapisan tetapi diamplas Permukaan papan partikel tidak diberi bahan lain
Beda
Papan partikel biasa yang dilapisi venir di
JIS
kedua sisinya dan tidak diamplas Papan partikel biasa yang dilapisi venir di kedua sisinya dan diamplas
Beda
SNI
Permukaan papan partikel diberi lapisan dikedua sisinya
Venir dekoratif dilapisi di kedua sisi atau
salah satu sisi papan partikel biasa
Film atau lembaran resin sintetis, kertas
yang telah diberi resin sintetis, lapisan
kertas atau sejenisnya dilapisi di kedua sisi
atau salah satu sisi papan partikel biasa
termasuk produk yang tidak berpola yang
permukaan dekoratifnya telah diberi warna
JIS
dan produk-produk yang mengalami pengembangan atau pola-pola abstrak
Lapisan resin sintetis yang ditekan dan telah mengering atau dicetak di kedua sisi
Beda
atau salah satu sisi papan partikel biasa,
termasuk produk tidak berpola yang
permukaannya telah yang permukaan
dekoratifnya telah diberi warna dan
produk-produk yang mengalami
pengembangan atau pola-pola abstrak
Permukaan papan partikel diberi lapisan
SNI
venir indah atau kertas indah atau resin sintetis atau cat pada kedua sisi atau di
salah satu sisinya
Produk-produk papan partikel untuk pemasaran areal jepang berdasarkan
tipe permukaannya diberi tanda sesuai dengan standar JIS A 5908-2003,
Universitas Sumatera Utara
sedangkan produk untuk pemasaran tidak diberi tanda untuk menunjukkan tipe permukaannya.
Ketebalan, Panjang dan Lebar
Ukuran papan partikel berdasarkan JIS dibagi menjadi klasifikasi ketebalan seperti yang tertera pada Tabel 4. Untuk ukuran papan partikel pada SNI tidak ditetapkan klasifikasi besarnya ukuran ketebalan yang digunakan pada pembuatan papan partikel.
Tabel 4. Klasifikasi papan partikel berdasarkan ketebalan
Tipe papan partikel
Tipe 24-10, Tipe17,5-10,5 Tipe 30-15 Tipe 18 Tipe 8
Ketebalan (mm) JIS 9,5; 11; 12,7;16;19; 28,5
9, 10, 12, 15, 18, 20, 25, 30, 35, 40
SNI -
-
Komparasi Beda Beda
Tabel 5. Klasifikasi papan partikel berdasarkan panjang dan lebar
Tipe papan partikel
Tipe 24-10, Tipe17,5-10,5 Tipe 30-15 Tipe 18 Tipe 8
1820x900, 2420x900, 2730x900,
Ukuran (mm) JIS
2440 x 1220
1820x910, 1820x1210, 2420x910, 2420x1210, 2730x910, 2730x1210
SNI -
-
Komparasi Beda Beda
Ukuran panjang dan lebar papan partikel yang umum digunakan adalah
ukuran pada tipe 8, 18, dan 30-15. Akan tetapi ukuran produk papan partikel
tersebut dapat dibuat berdasarkan ukuran pesanan sesuai dengan perjanjian antara
pihak-pihak terkait.
Universitas Sumatera Utara
Toleransi dan Kesikuan
Toleransi yang diperbolehkan pada JIS A 5908-2003 dan SNI 03-59082006 untuk panjang dan lebar ± 3 mm, toleransi kesikuan (perbedaan dari garis siku) yang diperbolehkan maksimal 2 mm. Toleransi tebal yang diperbolehkan antara kedua standar ini tidak memiliki perbedaan, seperti yang terlampir pada Tabel 6.
Tabel 6. Toleransi tebal papan partikel
Macam papan partikel Papan partikel biasa Papan partikel berlapis venir Papan partikel dekoratif
Tebal (mm) < 15 ≥ 15 < 20 ≥ 20 12,7 mm sesuai dengan ketentuan yang tertera pada Tabel 9. Hal ini menunjukkan toleransi kadar air yang dipersyaratkan pada JIS untuk tipe 8 dan 24-10 lebih rendah dibandingkan dengan standar yang ditetapkan SNI.
Tabel 10. Syarat kerapatan papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir
Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5 Tipe 30-15 Tipe 18 Tipe 13 Tipe 8
Kerapatan g/cm3
JIS SNI
0,4-0,9
0,4-0,9
0,4-0,9
0,4-0,9
0,4-0,9
0,4-0,9
0,4-0,9 0,4-0,9 0,4-0,9
0,4-0,9 0,4-0,9 0,4-0,9
Komparasi
Sama Sama Sama Sama Sama Sama
Tabel 11. Syarat kadar air papan partikel
Klasifikasi
Papan partikel biasa
Papan partikel berlapis venir Papan partikel dekoratif
Tipe 24-10
Tipe 17,510,5 Tipe 30-15 Tipe 18 Tipe 13 Tipe 8
Kadar air (%)
JIS Maks 12 %
SNI
Bila tebal ≤ 12,7 mm
maksimum 25 %, Bila
tebal
> 12,7 mm
maksimum 20 %
Maks 12 % Maks 12 %
Komparasi Beda Sama
Maks 12 % Maks 12 %
Maks 12 % Maks 12 % Maks 12 % Maks 12 % Maks 12 % Tidak dipersyaratkan
Sama
Sama Sama Beda
Universitas Sumatera Utara
Tabel 12. Syarat pengembangan tebal papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir
Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5
Tipe 30-15
Tipe 18 Tipe 13 Tipe 8
Pengembangan tebal (%)
JIS SNI
5 – 13
≤ 14
5 – 13
≤ 14
5 – 13
≤ 14
5 – 13 5 – 13 5 – 13
≤ 14 ≤ 14 ≤ 14
Komparasi
Beda Beda
Beda
Beda Beda Beda
Pengujian keteguhan tarik lapisan dekoratif, ketahanan pukul, ketahanan terhadap asam, ketahanan terhadap basa , standar yang ditetapkan antara JIS dan SNI adalah sama, sedangkan untuk ketahanan papan partikel terhadap goresan pada SNI tidak ditentukan kriterianya seperti yang tertera pada Tabel 13.
Tabel 13. Syarat pengujian papan partikel
Macam pengujian Keteguhan tarik lapisan dekoratif
Ketahanan pukul
Ketahanan terhadap asam Ketahanan terhadap basa Ketahanan terhadap noda
Ketahanan terhadap perubahan warna
Ketahananterhadap goresan
JIS Minimal 0,4 N/mm2
SNI Minimal 4,0 kgf/cm2
Komparasi Sama
Bebas dari retak pada bidang radial, patah dan mengelupas pada bagian permukaan
Tidak ada perubahan warna
Tidak ada perubahan warna
Skala 3 atau lebih dalam skala gray
Penampilan bebas dari cacat seperti pembengkakan pada permukaan dan dalam skala Gray nilainya 4 atau lebih Tidak ada goresan yang jelas
Tidak ada retak dan terkelupas pada lapisan dekoratif
Tidak ada perubahan warna
Tidak ada perubahan warna Tidak ada bekas warna atau noda yang tertinggal
Tidak terjadi perubahan warna dan pemudaran kilap
Tidak ditentukan kriteria
Sama Sama Sama Beda
Beda
Beda
Pengujian daya sekat api, pada SNI tidak dilakukan sedangkan pada JIS di
uji berdasarkan ketebalan papan partikel. Untuk pengujian daya sekat api papan
Universitas Sumatera Utara
partikel hanya ditetapkan untuk papan dengan tipe 8, 18, 30-15 seperti yang tertera pada tabel 14.
Tabel 14. Syarat uji daya sekat api
Ketebalan
10 12 15 18 20 25 30 35 40
Daya tahan panas
JIS SNI
0,060
-
0,077
-
0,095
-
0,112
-
0,120
-
0,155
-
0,181
-
0,215
-
0,241
-
Komparasi
Beda Beda Beda Beda Beda Beda Beda Beda Beda
Untuk pengujian ketahanan terhadap api, pada SNI tidak ada ditetapkan pengujian sedangkan untuk JIS, grade ketahanan terhadap api ditetapkan menjadi dua yaitu grade 2 dan grade 3 seperti yang tertera pada Tabel 15. Hal ini menunjukkan produk yang di produksi berdasarkan JIS lebih baik untuk kualitas ketahanan terhadap api.
Tabel 15. Syarat uji ketahanan terhadap api
Klasifikasi
Ketahanan terhadap api grade 2 Ketahanan terhadap api grade 3
Ketahanan terhadap api JIS SNI
Grade 2
-
Grade 3
-
Komparasi Beda Beda
Satuan yang digunakan di indonesia untuk pengujian sifat mekanis adalah kgf/cm2 sedangkan satuan yang digunakan untuk JIS adalah N/mm2 seperti yang tertera pada Tabel 16 dan Tabel 17. Tetapi untuk pengujian keteguhan cabut
Universitas Sumatera Utara
sekrup satuan yang digunakan pada JIS adalah Newton, sedangkan pada SNI satuan yang digunakan adalah kgf (kilogram force).
Tabel 16. Syarat sifat mekanis papan partikel
Klasifikasi
Papan partikel biasa struktural Papan partikel berlapis venir
Papan partikel biasa dan papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5
Tipe 30-15
Tipe 18 Tipe 13 Tipe 8
Keteguhan lentur kering minimum
JIS (N/mm2)
SNI (kgf/cm2)
Arah Arah Arah Arah
panjang lebar panjang lebar
24,0 10,0 245 102
17,5 10,5 178 107
30,0 15,0 306 153
18,0 18,0 184 184 13,0 13,0 133 133 8,0 8,0 82 82
Komparasi
Sama Sama Sama Sama Sama Sama
Tabel 17. Keteguhan lentur basah
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir
Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5
Tipe 30-15
Tipe 18 Tipe 13 Tipe 8
Keteguhan lentur basah minimum JIS (N/mm2) SNI (kgf/cm2) Arah Arah Arah Arah panjang lebar panjang lebar 12,0 5,0 122 51 8,8 5,3 90 54
15,0 7,5 153 77
9,0 9,0 92 92 6,5 9,0 66 66 ----
Komparasi
Sama Sama Sama Sama Sama Sama
Klasifikasi keteguhan lentur pada JIS A 5908-2003 dan SNI 03-5908-2006 dibagi menjadi tipe 8,18, 13 untuk penggunaan papan partikel biasa dan dekoratif, tipe 24-10, 17.5-10,5 untuk papan partikel biasa struktural, tipe 30-15untuk penggunaan papan partikel berlapis venir seperti yang tertera pada Tabel 17.
Universitas Sumatera Utara
Pemberian nama tipe-tipe didasarkan pada pembagian keteguhan lentur kering masing-masing tipe. Pemberian tipe 18 dikarenakan keteguhan lentur minimumnya sebesar 18,0 N/mm2 arah panjang dan arah lebarnya, tipe 13 dikarenakan keteguhan lentur minimumnya sebesar 13,0 N/mm2 pada arah panjang dan arah lebar, tipe 8 dikarenakan keteguhan lentur minimumnya sebesar 8,0 N/mm2 pada arah panjang panjang dan arah lebarnya. Tipe 24-10 dikarenakan keteguhan lentur minimumya sebesar 24,0 N/mm2 pada arah panjang dan sebesar 10,0 N/mm2 pada arah lebar, tipe 17,5-10,5 dikarenakan keteguhan lentur minimumnya sebesar 17,5 N/mm2 pada arah panjang dan sebesar 10,5 N/mm2 pada arah lebar, Tipe 30-15 keteguhan lentur minimumnya sebesar 30,0 N/mm2 pada arah panjang dan sebesar 15,0 N/mm2 atau pada arah lebar. Tipe 24-10 berarti tipe OSB, dan tipe 17,5-10-5 berarti papan untuk tipe wafer.
Table 18. Syarat minimum keteguhan tarik tegak lurus permukaan papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5 Tipe 30-15 Tipe 18 Tipe 13 Tipe 8
Keteguhan tarik tegak lurus permukaan minimum JIS SNI
(N/mm2) (kgf/cm2) 0,3 3,1 0,3 3,1 0,3 3,1 0.3 3,1 0,2 2,0 0,15 1,5
Komparasi
Sama Sama Sama Sama Sama Sama
Universitas Sumatera Utara
Tabel 19. Syarat minimum keteguhan cabut sekrup papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir Papan partikel dekoratif
Tipe 24-10 Tipe 17,5-10,5 Tipe 30-15 Tipe 18 Tipe 13 Tipe 8
Keteguhan cabut sekrup minimum JIS SNI (N) (kgf) 500 51 500 51 500 51 500 51 400 41 300 31
Komparasi
Sama Sama Sama Sama Sama Sama
Standar keteguhan tarik tegak lurus permukaan dan keteguhan cabut
sekrup papan partikel yang ditetapkan JIS dan SNI adalah sama seperti yang
tertera pada Tabel 18 dan Tabel 19. Untuk pengujian keteguhan cabut sekrup,
berdasarkan SNI pengujian keteguhan cabut sekrup hanya dilakukan untuk papan
partikel dengan ketebalan minimal 15 mm, sedangkan pada JIS tidak ditentukan
tebal minimum papan partikel yang akan di uji.
Modulus elastisitas merupakan ukuran kemampuan kayu untuk menahanperubahan bentuk atau lentur yang terjadi sampai dengan batas proporsi.Nilai Modulus elastisitas yang ditetapkan oleh JIS dan SNI adalah sama, akan tetapi satuan yang digunakan untuk nilai berbeda, JIS menggunakan satuan N/mm2 sedangkan SNI menggunakan kgf/cm2 seperti yang tertera pada Tabel 20.
Universitas Sumatera Utara
Tabel 20. Syarat minimum modulus elastisitas papan partikel
Klasifikasi
Papan partikel biasa Papan partikel berlapis venir Papan partikel dekoratif
Tipe 24-10
Tipe 17,510,5
Tipe 30-15
Tipe 18 Tipe 13 Tipe 8
Modulus elastisitas minimum
JIS (N/mm2)
SNI (kgf/cm2)
4000 arah panjang, 4,08 arah panjang;
1300 arah lebar
1,33 arah lebar
3000 arah panjang; 3,06 arah panjang;
2000 arah lebar
2,04 arah lebar
4000 arah panjang; 4,59 arah panjang;
2800 arah lebar
2,86 arah lebar
3000 arah lebar
3,06 arah lebar
2500 arah lebar
2,55 arah lebar
2000 arah lebar
2,04 arah lebar
Komparasi
Sama
Sama
Sama Sama Sama Sama
Pengujian Papan Partikel
Ukuran contoh uji papan partikel yang ditetapkan JIS dan SNI tidak berbeda untuk semua pengujian kecuali pada pengujian emisi formaldehida yang diuji berdasarkan standar emisi formaldehida masing-masing negara, serta pengujian daya sekat api dan ketahan terhadap api yang tidak diujikan pada SNI. Pada JIS pengujian emisi formaldehida mengacu pada JIS A 1460, sedangkan pada SNI mengacu pada SNI 6050-1999 seperti yang tertera pada Tabel 21.
Universitas Sumatera Utara
Tabel 21. Ukuran contoh uji papan partikel
JIS
No Macam pengujian Ukuran Banyaknya
contoh uji contoh uji
1 Kerapatan
100 x 100
1
2 Kadar air
100 x 100
1
3
Pengembangan tebal setelah direndam air
50 x 50
1
4
Keteguhan lentur (kering)
Lebar 50 x Arah
panjang (S panjang 1,
+ 50)
arah lebar 1
5
Keteguhan lentur (basah)
Lebar 50 x Arah
panjang (S panjang 1,
+ 50)
arah lebar 1
6
Keteguhan tarik tegak lurus permukaan
50 x 50
1
7
Keteguhan cabut sekrup
50 x 100
1
50 x 150 Mengacu
8 Emisi formaldehida
pada JIS A
1460
9
Keteguhan tarik lapisan dekoratif
50 x 50
1
10 Keteguhan pukul
300 x 300
1
Ukuran contoh uji 100 x 100 100 x 100
SNI Banyaknya contoh uji 1 1
50 x 50
1
Lebar 50 x panjang (S + 50) Lebar 50 x panjang (S + 50)
Arah panjang 1, arah lebar 1
Arah panjang 1, arah lebar 1
50 x 50
1
50 x 100
1
50 x 100
Mengacu pada SNI 60501999
50 x 50
1
300 x 300
1
Komparasi Sama Sama Sama
Sama
Sama
Sama Sama
Sama
Sama Sama
11
Ketahanan terhadap asam
100 x 100
1
12
Ketahanan terhadap basa
100 x 100
1
13
Ketahanan terhadap noda
100 x 100
1
14
Ketahanan terhadap perubahan warna
150 x 150
1
1(3 untuk
15
Ketahanan terhadap goresan
50 x 50
yang lebih dari 1
warna)
16 Uji daya sekat panas 900 x 900
1
17 Ketahanan terhadap api 220 x 220
1
100 x 100 100 x 100
100 x 100 150 x 150
50 x 50
-
1
1
1
1 1 ( 3 untuk yang lebih dari 1 warna)
-
Sama Sama Sama Sama
Sama
Beda Beda
Untuk pengambilan contoh uji sebaiknya diambil pada sekitar bagian
tengah dan untuk papan dekoratif dengan alur pada permukaan dekoratif, contoh
uji yang diambil harus sampel dengan bagian alur. Kondisi contoh uji yang
dibawah kondisi kering udara atau mencapai kondisi berat yang konstan pada suhu 20±20 C dan kelembaban sekitar 65±5 %. Dalam hal ini kondisi kering udara
adalah kondisi contoh uji telah dikeringkan selama 7 hari atau lebih pada ruangan
Universitas Sumatera Utara
dengan ventilasi dan berat konstan adalah perubahan berat yang di ukur sebesar 0,1% setiap 24 jam.
Untuk pengujian kerapatan, antara JIS dan SNI tidak memiliki perbedaan yaitu pengujian dilakukan dengan pengukuran panjang dan lebar contoh uji di kedua sisinya, 25 mm dari tepi dengan ketelitian 0,1 mm, pengukuran tebal contoh uji pada keempat sudutnya, 25 mm dari keempat sudutnya (pada titik persilangan pengukuran panjang dan lebar) dengan ketelitian 0,05 mm, pengukuran berat dilakukan dengan ketelitian 0,1 g dan penghitungan kerapatan dilakukan dengan rumus yang berlaku dengan ketelitian 0,01 g/cm3. Untuk pengujian kadar air, antara JIS dn SNI tidak memiliki perbedaan yaitu contoh uji ditimbang beratnya untuk mengetahui berat awal dengan ketelitian 0,1gram, contoh uji dikeringkan kedalam oven pada suhu 103±20C lalu ditimbang hingga perbedaan berat maksimum 0,1 %.
Untuk pengujian pengembangan tebal, terdapat perbedaan terhadap suhu air yang dipakai untuk pengujian rendaman contoh uji. Pada JIS suhu air yang dipakai adalah 20±10C sedangkan pada SNI suhu air yang dipakai adalah 25±10C. Hal ini dikarenakan Indonesia merupakan daerah tropis sedangkan jepang merupakan da