Hasil Pengujian - 105 Kode Beton = Hasil Pengujian - 106 Hasil Pengujian - 107 Kode Beton =

Jl. Babarsari No.44 Yogyakarta 55281 Indonesia KotakPos 1086 Telp.+62-274-487711 hunting Fax. +62-274-487748 105

D. Hasil Pengujian - 105 Kode Beton =

SF 30 1 Po = 202,3 mm Ao = 17671,45868 mm 2 Beban Compressometer Compressometer Tegangan Regangan Regangan Koreksi kgf N Δ P 10 -3 Δ P2 10 -3 MPa 10 -5 10 -5 0,0000 -1,1100 0,0000 100 980,671 2 1 0,0555 0,4943 1,6043 200 1961,342 6 3 0,1110 1,4829 2,5929 300 2942,013 10 5 0,1665 2,4716 3,5816 400 3922,684 14 7 0,2220 3,4602 4,5702 500 4903,355 19 9,5 0,2775 4,6960 5,8060 600 5884,026 24 12 0,3330 5,9318 7,0418 700 6864,697 30 15 0,3885 7,4147 8,5247 800 7845,368 35 17,5 0,4440 8,6505 9,7605 900 8826,039 41 20,5 0,4995 10,1335 11,2435 1000 9806,71 53 26,5 0,5549 13,0994 14,2094 1100 10787,381 64 32 0,6104 15,8181 16,9281 1200 11768,052 73 36,5 0,6659 18,0425 19,1525 1300 12748,723 90 45 0,7214 22,2442 23,3542 1400 13729,394 104 52 0,7769 25,7044 26,8144 1500 14710,065 121 60,5 0,8324 29,9061 31,0161 Jl. Babarsari No.44 Yogyakarta 55281 Indonesia KotakPos 1086 Telp.+62-274-487711 hunting Fax. +62-274-487748 106

D. Hasil Pengujian - 106

Contoh Hitungan : f = 100 x 9,80671 = 980,671N A = 0,25 x π x d 2 = 0,25 x π x 150 2 = 17671,46 mm 2 P = 202,3 mm 0,0555MPa 17671,46 980,671 A f σ    5 3 0,4943x10 208,06 1x10 P Δ p ε      X koreksi = -1,11. 10 -5 5 5 5 koreksi koreksi 1,6043.10 1,11.10 0,4943.10 x ε ε          Beban maks = 1585 kgf Fmax = 46 , 17671 80671 , 9 1585x = 0,8796 MPa σ p = 0,222 MPa ε p = 4,5702 . 10 -5 Modulus elastisitas =  p p ε σ 4857,077 MPa Modulus elastisitas teori = fc x0,043x W 1,5 c = 2610,1557 MPa y = -0.0008x 2 + 0.0491x + 0.0555 R² = 0.9941 0.0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 0.0 10.0 20.0 30.0 40.0 M Pa .10 -5 Grafik Kuat Tekan SF 30 1 Jl. Babarsari No.44 Yogyakarta 55281 Indonesia KotakPos 1086 Telp.+62-274-487711 hunting Fax. +62-274-487748 107

D. Hasil Pengujian - 107 Kode Beton =

SF 30 2 Po = 209,06 mm Ao = 17813,11309 mm 2 Beban Compressometer Compressometer Tegangan Regangan Regangan Koreksi kgf N Δ P 10 -3 Δ P2 10 -3 MPa 10 -5 10 -5 0,0000 -0,9470 0,0000 50 490,3355 1 0,5 0,0275 0,2392 1,1862 100 980,671 3 1,5 0,0551 0,7175 1,6645 150 1471,0065 5 2,5 0,0826 1,1958 2,1428 200 1961,342 8 4 0,1101 1,9133 2,8603 250 2451,6775 10 5 0,1376 2,3917 3,3387 300 2942,013 13 6,5 0,1652 3,1092 4,0562 350 3432,3485 16 8 0,1927 3,8267 4,7737 400 3922,684 19 9,5 0,2202 4,5442 5,4912 450 4413,0195 21 10,5 0,2477 5,0225 5,9695 500 4903,355 24 12 0,2753 5,7400 6,6870 550 5393,6905 27 13,5 0,3028 6,4575 7,4045 600 5884,026 31 15,5 0,3303 7,4141 8,3611 650 6374,3615 34 17 0,3578 8,1316 9,0786 700 6864,697 37 18,5 0,3854 8,8491 9,7961 750 7355,0325 42 21 0,4129 10,0450 10,9920 800 7845,368 46 23 0,4404 11,0016 11,9486 850 8335,7035 48 24 0,4680 11,4800 12,4270 900 8826,039 53 26,5 0,4955 12,6758 13,6228 950 9316,3745 58 29 0,5230 13,8716 14,8186 1000 9806,71 62 31 0,5505 14,8283 15,7753 1050 10297,0455 66 33 0,5781 15,7849 16,7319 1100 10787,381 69 34,5 0,6056 16,5024 17,4494 1150 11277,7165 74 37 0,6331 17,6983 18,6453 1200 11768,052 77 38,5 0,6606 18,4158 19,3628 1250 12258,3875 84 42 0,6882 20,0899 21,0369 1300 12748,723 87 43,5 0,7157 20,8074 21,7544 1350 13239,0585 91 45,5 0,7432 21,7641 22,7111 1400 13729,394 95 47,5 0,7707 22,7208 23,6678 1450 14219,7295 99 49,5 0,7983 23,6774 24,6244 1500 14710,065 104 52 0,8258 24,8732 25,8202 1550 15200,4005 109 54,5 0,8533 26,0691 27,0161 1600 15690,736 114 57 0,8809 27,2649 28,2119 Jl. Babarsari No.44 Yogyakarta 55281 Indonesia KotakPos 1086 Telp.+62-274-487711 hunting Fax. +62-274-487748 108

D. Hasil Pengujian - 108

Dokumen yang terkait

PENGARUH FOAMING AGENT ADT TERHADAP KUAT TEKAN,MODULUS ELASTISITAS, DAN PENYERAPAN AIR PADA BETON PENGARUH FOAMING AGENT ADT TERHADAP KUAT TEKAN, MODULUS ELASTISITAS, DAN PENYERAPAN AIR PADA BETON DENGAN BAHAN TAMBAH SILICA FUME.

0 2 17

PENDAHULUAN PENGARUH FOAMING AGENT ADT TERHADAP KUAT TEKAN, MODULUS ELASTISITAS, DAN PENYERAPAN AIR PADA BETON DENGAN BAHAN TAMBAH SILICA FUME.

0 3 4

TINJAUAN PUSTAKA PENGARUH FOAMING AGENT ADT TERHADAP KUAT TEKAN, MODULUS ELASTISITAS, DAN PENYERAPAN AIR PADA BETON DENGAN BAHAN TAMBAH SILICA FUME.

0 2 5

LANDASAN TEORI PENGARUH FOAMING AGENT ADT TERHADAP KUAT TEKAN, MODULUS ELASTISITAS, DAN PENYERAPAN AIR PADA BETON DENGAN BAHAN TAMBAH SILICA FUME.

0 2 9

PENGARUH PENAMBAHAN FLY ASH PADA KUAT TEKAN DAN MODULUS ELASTISITAS BETON MUTU PENGARUH PENAMBAHAN FLY ASH PADA KUAT TEKAN DAN MODULUS ELASTISITAS BETON MUTU TINGGI DENGAN SILICA FUME, SUPERPLASTICIZER, DAN FILLER PASIR KUARSA.

0 3 17

PENDAHULUAN PENGARUH PENAMBAHAN FLY ASH PADA KUAT TEKAN DAN MODULUS ELASTISITAS BETON MUTU TINGGI DENGAN SILICA FUME, SUPERPLASTICIZER, DAN FILLER PASIR KUARSA.

0 3 6

KESIMPULAN DAN SARAN PENGARUH PENAMBAHAN FLY ASH PADA KUAT TEKAN DAN MODULUS ELASTISITAS BETON MUTU TINGGI DENGAN SILICA FUME, SUPERPLASTICIZER, DAN FILLER PASIR KUARSA.

1 6 76

KAJIAN PENAMBAHAN METAKAOLIN TERHADAP KUAT TEKAN DAN MODULUS ELASTISITAS KAJIAN PENAMBAHAN METAKAOLIN TERHADAP KUAT TEKAN DAN MODULUS ELASTISITAS PADA BETON MUTU TINGGI DENGAN SILICA FUME, SUPERPLATICIZER DAN FILLER PASIR KWARSA.

0 4 15

BAB 6 KESIMPULAN DAN SARAN KAJIAN PENAMBAHAN METAKAOLIN TERHADAP KUAT TEKAN DAN MODULUS ELASTISITAS PADA BETON MUTU TINGGI DENGAN SILICA FUME, SUPERPLATICIZER DAN FILLER PASIR KWARSA.

0 4 70

PENGARUH ABRASI AIR LAUT TERHADAP KUAT TEKAN DAN MODULUS ELASTISITAS BETON MUTU TINGGI DENGAN BAHAN TAMBAH ABU SEKAM PADI

0 1 8