Peranan Penambahan Nanopartikel Batu Kapur Terhadap Sifat Mekanis Dan Ketahanan Termal Komposit Polietilen Densitas Tinggi
Lampiran A.
A.1 Hasil Analisa XRD Batu Kapur
A.2 Kurva DSC HDPE
A.3 Kurva DSC Komposit HDPE-g-MA + NBK 3 %
A.4 Termogram HDPE Murni
A.5 Termogram Komposit HDPE-g-MA + NBK 3%
A.6 Hasil Uji Tarik HDPE Murni
A.7 Hasil Uji Tarik Komposit HDPE-g-MA + NBK 1%
A.8 Hasil Uji Tarik Komposit HDPE-g-MA + NBK 3%
A.9 Hasil uji Tarik komposit HDPE-g-MA + NBK 5%
A.10 Hasil Uji Tarik Komposit HDPE-g-MA + NBK 7%
A.11 Hasil uji Tarik Komposit HDPE-g-MA + NBK 9%
50
45
40
35
30
25
4000
2000
Wavenumbers (cm-1)
894.92
786.29
693.28
987.43
947.97
65
862.37
834.66
55
1287.77
65
60
718.99
1462.80
70
1056.86
60
1855.41
2057.72
2005.77
1982.77
1018.86
1743.39
75
1264.49
1241.35
1219.05
70
2204.33
2177.22
2163.78
2138.99
4000
2363.84
80
1458.45
1431.13
75
2685.46
%Transmittance
85
1632.91
80
2915.53
2847.92
35
2886.61
40
1776.25
85
3122.64
3057.97
45
1704.28
1585.90
1565.15
%Transmittance
A.12 Spektrum FTIR HDPE
90
55
50
2000
Wavenumbers (cm-1)
A.13 Spektrum FTIR Maleat Anhidrida
95
90
A.14 Spektrum FTIR HDPE-g-MA
1217.35
80
1719.03
2344.89
85
2084.60
2007.20
90
65
60
55
50
45
40
4000
2915.81
2848.08
%Transmittance
70
2000
Wavenumbers (cm-1)
719.16
1463.13
75
Lampiran B
B.1 Perhitungan Persentase Derajat Grafting Maleat Anhidrat
%MA =
x MWMA x 100
VB = volume KOH yang digunakan (ml)
NB = konsentrasi KOH yang digunakan (0.05 N)
VA = volume HCl yang digunakan (ml)
NA = konsentrasi HCl yang digunakan (0.05 N)
MWMA = berat molekul dari Maleat Anhidrat (98 g/mol)
Ws = berat sampel
2 = faktor konversi dari 2 bentuk asam karboksil dari 1 molekul Ma
1000 = faktor konversi dari 1 g menjadi 1000 mg
No.
Ө Sampel
Indikator BTB
Volume KOH
Volume HCl
0.05N
1
5 ml
5 tetes
3,5 ml
0,10 ml
2
5 ml
5 tetes
3,45 ml
0,15 ml
3
5 ml
5 tetes
3,5 ml
0,10 ml
3,483 ml
0,133 ml
rata
rata
%MA =
= 0.82%
-
x 98 g/mol x 100%
B.2 Perhitungan Kekuatan Tarik
Kekuatan tarik dihitung dengan menggunakan rumus:
σ =
Dimana:
σ =kekuatan tarik (Mpa)
F =beban tarik (N)
A = luas penampang (m2)
Dan,
A = tebal x lebar spesimen
= 2 mm x 6 mm
= 12 mm2
Satuan tegangan dari kg/mm2 diubah menjadi N/m2dimana, 1 kgf = 9,81 N
Contoh :
Kekuatan tarik dari HDPE-g-Ma + NBK = (99 : 3)%
F = 41.08 kgf
A = 12 mm2
Maka nilai kekuatan tariknya:
σ =
=
= 3.423 kgf/mm2
= 3.423 kgf/mm2 x 9,81 = 33.59 Mpa
B.3 Perhitungan Kemuluran
Kemuluran dihitung berdasarkan rumus:
ε=
x 100 %
Dimana :
ɛ = kemuluran (%)
l =panjang setelah dibebani (mm)
lo = panjang sebelum dibebani (mm)
dan ∆l = l – lo = Stroke
lo = 50 mm
Contoh :
Kemuluran dari HDPE-g-Ma : NBK = (97 : 3)%
Stroke = 28.96 mm
ε=
=
x 100 %
x 100% = 57.93%
B.4 Perhitungan Ukuran Partikel Nano Batu Kapur
Ukuran partikel NBK diukur dengan rumus:
D=
keterangan :
D
= jari – jari
k
= konstanta
λ
= panjanggelombang
FWHM = full width at half maximum peak
Contoh :
Jika diketahui k = 0,9, λ = 1,5406 dan θ = 18,662, maka ukuran partikel
sebesar :
D=
= 3.886492 nm
A.1 Hasil Analisa XRD Batu Kapur
A.2 Kurva DSC HDPE
A.3 Kurva DSC Komposit HDPE-g-MA + NBK 3 %
A.4 Termogram HDPE Murni
A.5 Termogram Komposit HDPE-g-MA + NBK 3%
A.6 Hasil Uji Tarik HDPE Murni
A.7 Hasil Uji Tarik Komposit HDPE-g-MA + NBK 1%
A.8 Hasil Uji Tarik Komposit HDPE-g-MA + NBK 3%
A.9 Hasil uji Tarik komposit HDPE-g-MA + NBK 5%
A.10 Hasil Uji Tarik Komposit HDPE-g-MA + NBK 7%
A.11 Hasil uji Tarik Komposit HDPE-g-MA + NBK 9%
50
45
40
35
30
25
4000
2000
Wavenumbers (cm-1)
894.92
786.29
693.28
987.43
947.97
65
862.37
834.66
55
1287.77
65
60
718.99
1462.80
70
1056.86
60
1855.41
2057.72
2005.77
1982.77
1018.86
1743.39
75
1264.49
1241.35
1219.05
70
2204.33
2177.22
2163.78
2138.99
4000
2363.84
80
1458.45
1431.13
75
2685.46
%Transmittance
85
1632.91
80
2915.53
2847.92
35
2886.61
40
1776.25
85
3122.64
3057.97
45
1704.28
1585.90
1565.15
%Transmittance
A.12 Spektrum FTIR HDPE
90
55
50
2000
Wavenumbers (cm-1)
A.13 Spektrum FTIR Maleat Anhidrida
95
90
A.14 Spektrum FTIR HDPE-g-MA
1217.35
80
1719.03
2344.89
85
2084.60
2007.20
90
65
60
55
50
45
40
4000
2915.81
2848.08
%Transmittance
70
2000
Wavenumbers (cm-1)
719.16
1463.13
75
Lampiran B
B.1 Perhitungan Persentase Derajat Grafting Maleat Anhidrat
%MA =
x MWMA x 100
VB = volume KOH yang digunakan (ml)
NB = konsentrasi KOH yang digunakan (0.05 N)
VA = volume HCl yang digunakan (ml)
NA = konsentrasi HCl yang digunakan (0.05 N)
MWMA = berat molekul dari Maleat Anhidrat (98 g/mol)
Ws = berat sampel
2 = faktor konversi dari 2 bentuk asam karboksil dari 1 molekul Ma
1000 = faktor konversi dari 1 g menjadi 1000 mg
No.
Ө Sampel
Indikator BTB
Volume KOH
Volume HCl
0.05N
1
5 ml
5 tetes
3,5 ml
0,10 ml
2
5 ml
5 tetes
3,45 ml
0,15 ml
3
5 ml
5 tetes
3,5 ml
0,10 ml
3,483 ml
0,133 ml
rata
rata
%MA =
= 0.82%
-
x 98 g/mol x 100%
B.2 Perhitungan Kekuatan Tarik
Kekuatan tarik dihitung dengan menggunakan rumus:
σ =
Dimana:
σ =kekuatan tarik (Mpa)
F =beban tarik (N)
A = luas penampang (m2)
Dan,
A = tebal x lebar spesimen
= 2 mm x 6 mm
= 12 mm2
Satuan tegangan dari kg/mm2 diubah menjadi N/m2dimana, 1 kgf = 9,81 N
Contoh :
Kekuatan tarik dari HDPE-g-Ma + NBK = (99 : 3)%
F = 41.08 kgf
A = 12 mm2
Maka nilai kekuatan tariknya:
σ =
=
= 3.423 kgf/mm2
= 3.423 kgf/mm2 x 9,81 = 33.59 Mpa
B.3 Perhitungan Kemuluran
Kemuluran dihitung berdasarkan rumus:
ε=
x 100 %
Dimana :
ɛ = kemuluran (%)
l =panjang setelah dibebani (mm)
lo = panjang sebelum dibebani (mm)
dan ∆l = l – lo = Stroke
lo = 50 mm
Contoh :
Kemuluran dari HDPE-g-Ma : NBK = (97 : 3)%
Stroke = 28.96 mm
ε=
=
x 100 %
x 100% = 57.93%
B.4 Perhitungan Ukuran Partikel Nano Batu Kapur
Ukuran partikel NBK diukur dengan rumus:
D=
keterangan :
D
= jari – jari
k
= konstanta
λ
= panjanggelombang
FWHM = full width at half maximum peak
Contoh :
Jika diketahui k = 0,9, λ = 1,5406 dan θ = 18,662, maka ukuran partikel
sebesar :
D=
= 3.886492 nm