Pengaruh Temperatur Air Terhadap Kuat Tekan Beton pada Beton SCC (Self Compacting Concrete)
ABSTRACT
The development of technology for the use of concrete as a construction
material that can be solidified concrete result by its own weight or called SCC
(Self Compacting Concrete). This research was done experimentally in the
laboratory to determine the effect of water temperature on the compressive
strength of concrete SCC. Variations in the temperature of the water mixture
concrete used is 5ºC, 15ºC, normal temperature (28ºc), 50 ºC and 75 ºC. Testing
of concrete used in the form of tests on the test fresh concrete as a requirement to
test the workability of SCC include testing Slump flow to determine the passing
ability, J-ring flow to determine the filling ability and V-funnel for Segregation
resistance. In this test variations in water temperature the mixture at a temperature
of 5 ° C, 15 ° C and normal temperatures meet standard workability of SCC, while
the temperature of 50 ºC and 75 ºC not meet. Testing the hard concrete SCC
made with testing concrete compressive strength and tensile strength of concrete
sides, it is to get a conclusion on the effects on the quality of concrete. Testing the
compressive strength of concrete at 5 ° C higher 25.70%, temperature 15 ° C
higher 19.74%, 28 ° C (normal temperature) is higher 10.46%, temperature 50 ° C
higher 0.80 % and at a temperature of 75 ° C lower 1.16% of the quality plan 25
Mpa.
Keywords : SCC , workability , water temperature mixed concrete , concrete
compressive strength .
i
Universitas Sumatera Utara
ABSTRAK
Perkembangan teknologi terhadap pemanfaatan beton sebagai bahan
konstruksi menghasilkan beton yang bisa memadat dengan beratnya sendiri atau
yang disebut dengan SCC (Self Compacting Concrete.. Penelitian ini dilakukan
secara eksperimental di laboratorium yang untuk mengetahui pengaruh temperatur
air terhadap kuat tekan beton SCC. Variasi suhu air campuran beton yang
digunakan adalah 5ºc, 15ºc, suhu normal (28ºc), 50 ºc dan 75 ºc. Pengujian beton
yang digunakan berupa pengujian terhadap pengujian beton segar sebagai
persyaratan terhadap pengujian workability SCC antara lain pengujian Slump flow
untuk mengetahui passing ability, J-ring flow untuk mengetahui filling ability dan
V-funnel untuk Segregation Resistance. Pada pengujian ini variasi suhu air
campuran pada suhu 5 ºc, 15 ºc dan suhu normal memenuhi persyratan
workability SCC, sedangkan untuk suhu 50 ºc dan 75 ºc tidak memenuhi.
Pengujian beton keras SCC dilakukan dengan pengujian kuat tekan beton dan kuat
tarik belah beton, hal ini untuk mendapatkan kesimpulan terhadap pengaruhnya
terhadap mutu beton. Pengujian kuat tekan beton pada suhu 5°c lebih tinggi
25,70%, suhu 15°c lebih tingggi 19,74%, 28°c (suhu normal) lebih tinggi 10,46%,
suhu 50°c lebih tinggi 0,80% dan pada suhu 75°c lebih rendah 1,16% dari mutu
rencana 25 Mpa.
Kata kunci: SCC, workability, suhu air campuran beton, kuat tekan beton.
ii
Universitas Sumatera Utara
The development of technology for the use of concrete as a construction
material that can be solidified concrete result by its own weight or called SCC
(Self Compacting Concrete). This research was done experimentally in the
laboratory to determine the effect of water temperature on the compressive
strength of concrete SCC. Variations in the temperature of the water mixture
concrete used is 5ºC, 15ºC, normal temperature (28ºc), 50 ºC and 75 ºC. Testing
of concrete used in the form of tests on the test fresh concrete as a requirement to
test the workability of SCC include testing Slump flow to determine the passing
ability, J-ring flow to determine the filling ability and V-funnel for Segregation
resistance. In this test variations in water temperature the mixture at a temperature
of 5 ° C, 15 ° C and normal temperatures meet standard workability of SCC, while
the temperature of 50 ºC and 75 ºC not meet. Testing the hard concrete SCC
made with testing concrete compressive strength and tensile strength of concrete
sides, it is to get a conclusion on the effects on the quality of concrete. Testing the
compressive strength of concrete at 5 ° C higher 25.70%, temperature 15 ° C
higher 19.74%, 28 ° C (normal temperature) is higher 10.46%, temperature 50 ° C
higher 0.80 % and at a temperature of 75 ° C lower 1.16% of the quality plan 25
Mpa.
Keywords : SCC , workability , water temperature mixed concrete , concrete
compressive strength .
i
Universitas Sumatera Utara
ABSTRAK
Perkembangan teknologi terhadap pemanfaatan beton sebagai bahan
konstruksi menghasilkan beton yang bisa memadat dengan beratnya sendiri atau
yang disebut dengan SCC (Self Compacting Concrete.. Penelitian ini dilakukan
secara eksperimental di laboratorium yang untuk mengetahui pengaruh temperatur
air terhadap kuat tekan beton SCC. Variasi suhu air campuran beton yang
digunakan adalah 5ºc, 15ºc, suhu normal (28ºc), 50 ºc dan 75 ºc. Pengujian beton
yang digunakan berupa pengujian terhadap pengujian beton segar sebagai
persyaratan terhadap pengujian workability SCC antara lain pengujian Slump flow
untuk mengetahui passing ability, J-ring flow untuk mengetahui filling ability dan
V-funnel untuk Segregation Resistance. Pada pengujian ini variasi suhu air
campuran pada suhu 5 ºc, 15 ºc dan suhu normal memenuhi persyratan
workability SCC, sedangkan untuk suhu 50 ºc dan 75 ºc tidak memenuhi.
Pengujian beton keras SCC dilakukan dengan pengujian kuat tekan beton dan kuat
tarik belah beton, hal ini untuk mendapatkan kesimpulan terhadap pengaruhnya
terhadap mutu beton. Pengujian kuat tekan beton pada suhu 5°c lebih tinggi
25,70%, suhu 15°c lebih tingggi 19,74%, 28°c (suhu normal) lebih tinggi 10,46%,
suhu 50°c lebih tinggi 0,80% dan pada suhu 75°c lebih rendah 1,16% dari mutu
rencana 25 Mpa.
Kata kunci: SCC, workability, suhu air campuran beton, kuat tekan beton.