BALOK LAMINASI DENGAN KOMBINASI DARI BATANG KELAPA SAWIT (Elaeis guineensis Jacq.) DAN KAYU MAHONI (Swietenia mahagoni)

BALOK LAMINASI DENGAN KOMBINASI DARI BATANG

  

KELAPA SAWIT (Elaeis guineensis Jacq.) DAN

KAYU MAHONI (Swietenia mahagoni) SKRIPSI

  Oleh :

DENNI ARDIAN R. GINTING 061203038

  

LEMBAR PENGESAHAN

  Judul Skripsi : BALOK LAMINASI DENGAN KOMBINASI DARI BATANG KELAPA SAWIT (Elaeis guineensis Jacq.) DAN KAYU MAHONI (Swietenia mahagoni)

  Nama : DENNI ARDIAN R. GINTING NIM : 061203038 Program Studi : Kehutanan

  Disetujui oleh, Komisi Pembimbing

  Ketua Anggota ( Evalina Herawati, S. Hut., M. Si. ) ( Dr. rer. silv. Erwinsyah, S. Hut., MSc. )

  Diketahui oleh, Ketua Program Studi

  ( Siti Latifah, S. Hut., M. Si., Ph. D. )

  

ABSTRACT

The use of timber as a structural material is not only limited to solid

timber but also as laminate called lamination wood (gluelam). This research

explored the optimum total of layers, and height of the oil-palm stem to evaluate

physis and mechanis properties of lamination wood which is a combination of oil-

palm stem (Elaies guineensis jacq) and mahoni (Swietenia mahagoni). The

lamination wood had 50 cm long, 5 cm wide, and 5 cm deep. Glue spread are 300

  2

g/m with double side of glue lines. Each layer of lumber glued with water based

  2

polymer-isocianate (Koyo Bond) adhesive at pressure of 30 kg/cm for 50 minutes

pressing time. Testing method followed American Society for Testing and

Materials D143-93. The results of lamination wood testing shows that both of the

treatment and its interaction did not show significant effect on moisture

content,delamination, modulus of elasticity and modulus of rupture. But, was

significant effect on density

Keywords : lamination wood, oil palm (Elaeis guineensis Jacq), Mahoni

(Swietenia mahagoni), physis properties, mechanis properties, total of layers, and

height of the stem.

  

ABSTRAK

  Pemakaian kayu sebagai bahan struktural tidak hanya terbatas sebagai kayu utuh, tetapi juga sebagai kayu laminasi atau gluelam. Penelitian ini mencari jumlah lapisan, dan ketinggian posisi batang kelapa sawit yang optimum untuk mengevaluasi sifat fisis dan mekanis kayu laminasi kombinasi dari batang kelapa sawit ( Elaeis guineensis Jacq ) dan kayu mahoni (Swietenia mahagoni). Kayu laminasi berukuran panjang 80 cm, lebar 5 cm, dan tebal 5 cm. Jumlah perekat

  2

  terlabur terdiri dari 300 g/m dengan perekatan dua sisi. Masing – masing lapisan papan direkat dengan water based polymer-isocianate (Koyo Bond) pada tekanan

  2

  30 kg/cm , selama 50 menit. Pengujian benda uji dilakukan menurut ASTM D 143-93. Hasil pengujian kayu laminasi menunjukkan bahwa kedua perlakuan beserta interaksinya tidak berpengaruh nyata terhadap kadar air,delaminasi, keteguhan lentur dan keteguhan patah. Namun berbeda nyata pada kerapatan.

  Kata Kunci : kayu laminasi, kelapa sawit (Elaeis guineensis Jacq), mahoni(Swietenia mahagoni), sifat fisis, sifat mekanis, jumlah lapisan, ketinggian posisi batang.

RIWAYAT HIDUP

  Penulis dilahirkan di Binjai pada tanggal 19 Desember 1986. Anak dari Bapak E. Ginting dan Ibu J. Sembiring. Penulis merupakan putra pertama dari empat bersaudara.

  Penulis memulai pendidikan di SD Negeri 101735 Sei Semayang, lulus tahun 2000. Penulis melanjutkan pendidikan di SLTP Negeri I Sunggal dan lulus tahun 2003. Tahun 2006, penulis lulus dari SMU Swasta PABA ( Panca Abdi Bangsa) Binjai dan pada tahun yang sama lulus seleksi masuk USU melalui jalur PMDK. Penulis memilih program studi Kehutanan dengan minat dan bakat Teknologi Hasil Hutan, Fakultas Pertanian.

  Selama mengikuti perkuliahan, penulis aktif mengikuti kegiatan organisasi Himpunan Mahasiswa Sylva, PEMA Pertanian, dan KPU Pertanian.

  Penulis melaksanakan Praktikum Pengenalan dan Pengolahan Ekosistem Hutan selama 10 hari di Hutan TNGL Kabupaten Langkat dan Hutan Mangrove Pulau Sembilan Kabupaten Langkat. Penulis juga melaksanakan PKL di HPH Banten Provinsi Banten, selama 1 bulan.

  Pada akhir studi, penulis melaksanakan penelitian dibawah bimbingan Evalina Herawati, S.Hut., M.Si dan Dr. rer.silv. Erwinsyah, S.Hut., MSc. Dengan mengambil judul “Balok Laminasi Dengan Kombinasi Dari Batang kelapa

  

Sawit (Elaeis guineensis Jacq) Dan Kayu Mahoni (Swietenia mahagoni.)”

sebagai bahan skripsi untuk memperoleh gelar Sarjana Kehutanan.

KATA PENGANTAR

  Puji dan syukur penulis ucapkan kepada Tuhan Yang Maha Esa yang telah memberikan segala berkat dan karunia-Nya sehingga skripsi ini dapat selesai dengan baik. Judul dari skripsi ini adalah “Balok Laminasi Dengan Kombinasi Dari Batang kelapa Sawit (Elaeis guineensis Jacq) Dan Kayu Mahoni (Swietenia mahagoni.)”.

  Penulis banyak mendapat bantuan, dukungan dan motivasi dari berbagai pihak selama pelaksanaan penelitian hingga penyelesaian skripsi. Untuk itu penulis menyampaikan terima kasih yang sebenernya kepada: 1.

  Ayahanda E. Ginting dan Ibunda J. Sembiring, serta kepada adinda Dewi A. Susanti Ginting, S.Kom.,Mpd, Devita Permata sari Ginting,S.

  Kom, dan Daud Suranta Ginting, yang telah memberikan kasih sayang dan perhatian yang sangat besar serta turut mendoakan untuk keberhasilan penulis.

  2. Ibu Evalina Herawati, S.Hut., M.Si dan Bapak Dr. rer.silv. Erwinsyah, S.Hut., MSc, yang telah banyak meluangkan waktu untuk membimbing, mengoreksi, memberikan saran dan kritik kepada penulis dalam pelaksanaan penelitian hingga penyelesaian skripsi. Dan tidak lupa penulis ucapkan banyak terima kasih kepada Ibu Ketua Jurusan Kehutanan Siti Latifah, S.Hut.,M.Si.,Ph.D.

  3. Teman satu tim, lily, Ory, Paian, dan Heru atas tenaga, semangat, kerjasama dan kebersamaannya.

  4.

5. Teman-teman dari Program Studi Kehutanan dengan minat dan bakat

  THH, BDH, dan MNH 2006 lainya atas bantuannya dalam bentuk apapun.

  Penulis menyadari bahwa dalam penyusunan skripsi masih banyak terdapat kekurangan, baik dalam penyusunan dan penulisan kata maupun isinya.

  Penulis sangat mengharapkan kritik dan saran yang sifatnya membimbing dan membangun guna meningkatkan kualitas dan kesempurnaan penulisan ataupun penelitian selanjutnya. Semoga skripsi penelitian ini dapat bermanfaat.

  Medan, Desember 2012 Penulis

  

DAFTAR ISI

Hal.

  ABSTRACT ......................................................................................................... i ABSTRAK ........................................................................................................... ii RIWAYAT HIDUP .............................................................................................. iii KATA PENGANTAR .......................................................................................... iv DAFTAR ISI ........................................................................................................ vi DAFTAR TABEL ................................................................................................ viii DAFTAR GAMBAR ............................................................................................ ix DAFTAR LAMPIRAN ........................................................................................ x PENDAHULUAN

  Latar Belakang Penelitian ............................................................................. 1 Tujuan Penelitian .......................................................................................... 4 Manfaat Penelitian ........................................................................................ 4 Hipotesis Penelitian ...................................................................................... 4

  TINJAUAN PUSTAKA Defenisi Balok Laminasi .............................................................................. 5 Potensi Kelapa Sawit .................................................................................... 6 Karakteristik Batang Kelapa Sawit ............................................................... 7 Sifat Fisis Batang Kelapa Sawit ................................................................... 9 Sifat Mekanis Batang Kelapa Sawit ............................................................. 11 Pemanfaatan Kayu Mahoni .......................................................................... 12 Penggunaan Kayu Mahoni ............................................................................ 13 Perekat Isocyanat .......................................................................................... 14

  METODOLOGI Waktu dan Tempat ........................................................................................ 16 Bahan dan Alat ............................................................................................. 16 Prosedur Penelitian ....................................................................................... 17 Pengujian ...................................................................................................... 21 Analisis Data ................................................................................................. 26

  HASIL DAN PEMBAHASAN Kadar Air (KA) dan Kerapatan Sirekat ........................................................ 29 Sifat Fisis Balok Laminasi ............................................................................ 30

  Pengaruh Ketinggian Batang Dan Jumlah Lapisan serta Interaksi Terhadap Kadar Air (KA) Balok Laminasi ........................................... 30 Pengaruh Ketinggian Batang dan Jumlah Lapisan serta Interaksi Terhadap Kerapatan Balok Laminasi .................................................... 32

  Sifat Mekanis Balok Laminasi ..................................................................... 34 Pengaruh Ketinggian Batang Dan Jumlah Lapisan serta Interaksi Terhadap Keteguhan Lentur (Modulus of Elastisity/MOE) Balok

  Pengaruh Ketinggian Batang Dan Jumlah Lapisan serta Interaksi Terhadap Keteguhan Patah (Modulus of Rupture/MOR) Balok Laminasi ................................................................................................ 36

  Pengujian Delaminasi ................................................................................... 38 Pengaruh Ketinggian Batang Dan Jumlah Lapisan serta Interaksi Terhadap Perendaman Air Panas Balok Laminasi ............................... 38 Pengaruh Ketinggian Batang Dan Jumlah Lapisan serta Interaksi Terhadap Perendaman Air Dingin Balok Laminasi .............................. 40

  KESIMPULAN DAN SARAN Kesimpulan ................................................................................................... 42 Saran ............................................................................................................. 43

  DAFTAR PUSTAKA ........................................................................................... 44 LAMPIRAN ......................................................................................................... 47

  

DAFTAR TABEL

No.

  Hal.

  1. Macam – Macam Kondisi Kadar Air Kayu

  10

  2. Perbandingan Sifat Elaeis guineensis Jacq. dengan Beberapa Jenis Kayu ........................................................................................................... 11

  3. Sifat-Sifat Dasar Batang Kelapa Sawit ....................................................... 12

  4. Nilai Rata-Rata Kadar Air dan Kerapatan Batang Kelapa Sawit dan Kayu Mahoni secara Umum ....................................................................... 29

  

DAFTAR GAMBAR

No.

  Hal.

  1. Kelapa sawit (Elaeis guineensis Jacq.) ...................................................... 7 2.

  Skema Balok Laminasi .........................................................................................

  20

  3. Cara Pembebanan Pengujian MOE dan MOR ........................................... 24

  4. Skema Pembuatan Balok Laminasi ............................................................ 28

  5. Grafik Pengukuran Kadar Air Balok Laminasi .......................................... 31

  6. Grafik Pengukuran Kerapatan Balok Laminasi ......................................... 33

  7. Grafik Pengukuran MOE Balok Laminasi ................................................. 35

  8. Grafik Pengukuran MOR Balok Laminasi ................................................. 36

  9. Grafik Pengukuran Uji Delaminasi Balok Laminasi Air Panas ................. 39

  10. Grafik Pengukuran Uji Delaminasi Balok Laminasi Air Dingin ............... 40