Komposisi Serat Pandan Wangi 0,1 gr Komposisi Tanpa Serat Pandan Wangi 0,2 gr Komposisi Serat Pandan Wangi 0,3 gr Komposisi Serat Pandan Wangi 0,4 gr Komposisi Serat Pandan Wangi 0,5 gr Komposisi Tanpa Serat Pandan Wangi

Load beban � = 2,53 kgf x 9,8 ms 2 =24,794 N 3 �� = 3 x 24,794 N x 0,1 m = 7,43 Nm 2 �� 2 = 2 x 15mm 3 mm 2 = 270 mm 3 = 0,27 x 10 -6 m 3 ��� = ��� � �� � = 7,43 �� 0,27 x 10 −6 m3 = 27,51 MPa

d. Komposisi Serat Pandan Wangi 0,1 gr

Load beban = 3,41 kgf Lebar sampel = 15 mm Tebal sampel = 3 mm Jarak span = 0,1 m Sehingga Load beban � = 3,41 kgf x 9,8 ms 2 =33, 41 N 3 �� = 3 x 33,41 N x 0,1 m = 10,02 Nm 2 �� 2 = 2 x 15mm 3 mm 2 = 270 mm 3 = 0,27 x 10 -6 m 3 ��� = ��� � �� � = 10,02 �� 0,27 x 10 −6 m3 = 37,11 Mpa

e. Komposisi Tanpa Serat Pandan Wangi 0,2 gr

Load beban = 3,90 kgf Lebar sampel = 15 mm Tebal sampel = 3 mm Jarak span = 0,1 m Sehingga Load beban � = 3,90 kgf x 9,8 ms 2 =38,22 N 3 �� = 3 x 38,22 N x 0,1 m = 11,46 Nm 2 �� 2 = 2 x 15mm 3 mm 2 = 270 mm 3 = 0,27 x 10 -6 m 3 ��� = ��� � �� � = 11,46 �� 0,27 x 10 −6 m3 = 42,46 Mpa

f. Komposisi Serat Pandan Wangi 0,3 gr

Load beban = 4,17 kgf Lebar sampel = 15 mm Tebal sampel = 3 mm Jarak span = 0,1 m Sehingga Load beban � = 4,17kgf x 9,8 ms 2 =40,86 N 3 �� = 3 x 40,86 N x 0,1 m = 12,25 Nm 2 �� 2 = 2 x 15mm 3 mm 2 = 270 mm 3 = 0,27 x 10 -6 m 3 ��� = ��� � �� � = 12,25 �� 0,27 x 10 −6 m3 = 45,37 Mpa

g. Komposisi Serat Pandan Wangi 0,4 gr

Load beban = 4,57 kgf Lebar sampel = 15 mm Tebal sampel = 3 mm Jarak span = 0,1 m Sehingga Load beban � = 4,57 kgf x 9,8 ms 2 =44,78 N 3 �� = 3 x 44,78 N x 0,1 m = 13,43 Nm 2 �� 2 = 2 x 15mm 3 mm 2 = 270 mm 3 = 0,27 x 10 -6 m 3 ��� = ��� � �� � = 13,43 �� 0,27 x 10 −6 m3 = 49,74 Mpa

h. Komposisi Serat Pandan Wangi 0,5 gr

Load beban = 4,30 kgf Lebar sampel = 15 mm Tebal sampel = 3 mm Jarak span = 0,1 m Sehingga Load beban � = 4,30 kgf x 9,8 ms 2 = 42, 14 N 3 �� = 3 x 42,14 N x 0,1 m = 12,642 Nm 2 �� 2 = 2 x 15mm 3 mm 2 = 270 mm 3 = 0,27 x 10 -6 m 3 ��� = ��� � �� � = 12,642 �� 0,27 x 10 −6 m3 = 46,82 Mpa

3. Menghitung Kekuatan Impak Sampel Komposit Serat Pandan Wangi-

Resin Epoksi Nilai kekuatan Impak dapat dihitung dengan persamaan berikut : � � = � � � Dimana : I s = kekuatan impak E s = energi serap J A = Luas Penampang mm 2

a. Komposisi Tanpa Serat Pandan Wangi

Energi serap = 0,5 J Lebar sampel = 15 mm Tebal sampel = 3 mm Sehingga : � = � � � = 15 mm x 3 mm = 45 mm 2 = � � = � � � = �,� ��� −� �� �,�� � �� −� � � = 11 Kjm 2

b. Komposisi Serat Pandan Wangi 0,1 gr