Pengaruh Penambahan Serat Polypropylene Terhadap Kuat Awal Beton Type SCC (Self Compacting Concrete)
LAMPIRAN I
Pemeriksaan Material
Universitas Sumatera Utara
ANALISA AYAKAN AGREGAT HALUS
UNTUK MATERIAL PENYUSUN BETON
(ASTM C 136 - 84a)
Diameter Ayakan
(mm)
(No.)
9.50 (3/8 - in)
4.75 (No. 4)
2.36 (No. 8)
1.18 (No. 16)
0.60 (No. 30)
0.30 (No. 50)
0.15 (No. 100)
Pan
Berat
Sampel 1
(gram)
0.0
60.0
72.0
102.0
198.0
228.0
265.0
75.0
Total
1000.0
Fraksi Tertahan
Berat
Berat
Sampel 2
Total
(gram)
(gram)
0.0
0.0
53.0
113.0
75.0
147.0
102.0
204.0
199.0
397.0
228.0
456.0
260.0
525.0
83.0
158.0
1000.0
242.85
100
Klasifikasi FM Pasir Yang Memenuhi Syarat :
Halus
2.2 < FM < 2.6
Sedang
2.6 < FM < 2.9
Kasar
2.9 < FM < 3.2
Modulus Kehalusan (FM)
=
Kumulatif
(%)
0.00
5.65
7.35
10.20
19.85
22.80
26.25
7.90
2000
100
=
2.43
Tertahan
(%)
0.00
5.65
13.00
23.20
43.05
65.85
92.10
100.00
Lolos
(%)
100.00
94.35
87.00
76.80
56.95
34.15
7.90
0.00
Universitas Sumatera Utara
ANALISA AYAKAN AGREGAT KASAR
UNTUK MATERIAL PENYUSUN BETON
(ASTM C 136 - 84a & ASTM D 448 - 86)
Diameter Ayakan
(mm)
38.1 mm
19.1 mm
9.52 mm
4.76 mm
2.38 mm
1.19 mm
0.60 mm
0.30 mm
0.15 mm
Pan
Total
Retained Fraction
Berat
Berat
Berat
Sampel 1
Sampel 2
Total
(gram)
(gram)
(gram)
0.0
0.0
0.0
0.0
0.0
0.0
1544.0
1541.0
3085.0
431.0
429.0
860.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
25.0
30.0
55.0
2000.0
2000.0
4000
668.88
=
100
Klasifikasi FM Agregat Kasar Yang Memenuhi Syarat :
5.5 ≤ FM ≤ 7.5
Modulus Kehalusan ( FM ) =
Kumulatif
(%)
0.00
0.00
77.13
21.50
0.00
0.00
0.00
0.00
0.00
1.38
100
Tertahan
(%)
0.00
0.00
77.13
98.63
98.63
98.63
98.63
98.63
98.63
100.00
Lolos
(%)
100.00
100.00
22.88
1.38
1.38
1.38
1.38
1.38
1.38
0.00
6.69
Universitas Sumatera Utara
BERAT JENIS DAN ABSORBSI AGREGAT HALUS
UNTUK MATERIAL PENYUSUN BETON
(ASTM C 128 - 88)
KETERANGAN
Sampel 1
Sampel 2
Rata-rata
Berat mula-mula,
gram (S)
500.0
500.0
500.0
Berat piknometer + air +
Pasir ,gram ( C )
976.0
976.0
976.0
Berat kering, gram
(A)
491.0
490.0
490.5
675.0
675.0
675.0
Berat piknometer +
air, gram (B)
Berat jenis kering
=
A
(B+S-C)
2.47
2.46
2.46
Berat jenis SSD
=
S
(B+S-C)
2.51
2.51
2.51
Berat jenis semu
=
A
(B+A-C)
2.58
2.59
2.59
Absorbsi, %
=
( S - A ) x100
A
1.83
2.04
1.94
Universitas Sumatera Utara
BERAT JENIS DAN ABSORBSI AGREGAT KASAR
UNTUK MATERIAL PENYUSUN BETON
(ASTM C 127 - 88)
Sample
I
Sample
II
Average
Berat mula-mula, gram ( B )
1250.0
1250.0
1250.0
Berat piknometer + air + pasir,
gram ( C )
769.0
769.0
769.0
Berat kering, gram (A)
1239.0
1240.0
1239.5
KETERANGAN
Berat jenis kering
=
A
(B-C)
2.58
2.58
2.58
Berat jenis SSD
=
B
(B-C)
2.60
2.60
2.60
Berat jenis semu
=
A
(A-C)
2.64
2.63
2.63
Absorbsi, %
=
( B - A ) x 100
A
0.89
0.81
0.85
Universitas Sumatera Utara
BERAT ISI AGREGAT HALUS
UNTUK MATERIAL PENYUSUN BETON
ASTM C 29/C 29M – 90
Koreksi
(0C)
Suhu ruangan
28.00
0
Suhu air
Massa bejana kosong
Massa air ( A )
Berat isi air ( B )
Faktor koreksi : C =(B/A)
Diameter maksimum
agregat
( C)
(kg)
(kg)
26.00
0.46
1.90
(kg/m3)
996.77
523.79
(mm)
5.00
Hasil pengujian
KETERANGAN
Berat
Sampel I
Sampel II
Total
Cara merojok
3.54
3.55
7.09
Cara menyiram
3.34
3.36
6.70
Rata-rata
3.55
3.35
Berat net (G)
3.09
2.89
1615.89
1513.75
Berat isi (G*C) [kg/m3]
Universitas Sumatera Utara
BERAT ISI AGREGAT KASAR
UNTUK MATERIAL PENYUSUN BETON
ASTM C 29/C 29M - 90
Koreksi
Suhu ruangan
(0C)
28.00
Suhu air
Massa bejana kosong
Massa air ( A )
(0C)
(kg)
(kg)
26.00
5.00
9.20
(kg/m3)
996.77
(mm)
108.345
25.00
Berat isi air ( B )
Faktor koreksi : C =(B/A)
Diameter maksimum agregat
Hasil
pengujian
KETERANGAN
Berat
Sampel I
Sampel II
Total
Cara merojok
19.6
19.5
39.1
Cara menyiram
18.4
18.5
36.9
Rata-rata
19.55
18.45
Berat net (G)
14.55
13.45
1576.42
1457.24
Berat isi (G*C) [kg/m3]
Universitas Sumatera Utara
KADAR LUMPUR AGREGAT HALUS
DENGAN PENCUCIAN
UNTUK MATERIAL PENYUSUN BETON
( ASTM C 117 - 90 )
KETERANGAN
Sampel I
Sampel II
Rata-rata
Berat mula - mula, gram
500
500
500
Berat kering, gram
489
487
488
Berat material yang lolos ayakan No.
200, gram
11
13
12
Persentasi material yang lolos ayakan
No. 200, gram
2.2
2.6
2.4
Universitas Sumatera Utara
KADAR LUMPUR AGREGAT KASAR
DENGAN PENCUCIAN
UNTUK MATERIAL PENYUSUN BETON
( ASTM C 117 - 90 )
KETERANGAN
Sampel I
Sampel II
Rata-rata
1000
1000
1000
997
996.0
996.5
Berat material yang lolos ayakan No.
200, gram
3
4.0
3.5
Persentasi material yang lolos ayakan
No. 200, gram
0.3
0.4
0.35
Berat mula - mula, gram
Berat kering, gram
Universitas Sumatera Utara
LAMPIRAN II
Perencanaan Campuran
Universitas Sumatera Utara
Langkah 1. Menentukan Slump dan kekuatan beton yang diinginkan
Beton f'c 35 Mpa dengan menggunakan HRWR, slump yang digunakan
sebelum penambahan HRWR yaitu 2,5-5cm
f’cr
=
121.8 Mpa
Langkah 2. Menentukan ukuran maksimum agregat : 1-1,3cm
Langkah 3. Menentukan kadar optimum agregat kasar
Berat kering agregat kasar
= 945.852
kg/m3
Langkah 4. Estimasi air campuran dan kadar udara
estimasi air=
130.00 kg/m3
Langkah 5. Menentukan w/c+p =
0.288889
Langkah 6. Menghitung kadar bahan semen
semen
=
450.00 kg/m3
Langkah 7. Perhitungan komposisi dasar
- kadar semen per m3=
450.00
- volume material per kg/m3 kecuali pasir
semen=
0.145 m3
a. Kasar=
0.367 m3
air=
0.130 m3
udara=
0 m3
volume total=
0.642 m3
- volume pasir=
0.358 m3
berat pasir=
881.24 kg
Universitas Sumatera Utara
campuran akhir /m3 beton
semen=
450.00
pasir=
881.24
agregat kasar=
945.852
air=
130.00
berat total=
2407.10
HRWR=
5400.00
kg
kg
kg
kg
mL
substitusi fly ash 10%
- kadar semen per m3=
405.00
- volume material per kg/m3 kecuali pasir
semen=
0.131 m3
fly ash=
0.020 m3
a. Kasar=
0.367 m3
air=
0.130 m3
udara=
0 m3
volume total=
0.648 m3
volume pasir=
0.352 m3
405
45
945.852
130
kg
kg
kg
kg
866.64 kg
Campuran akhir /m3 beton:
Semen
Silica fume
Pasir
Agregat kasar
Air
berat total
HRWR
405.00
45.00
866.64
945.852
130.00
2392.49
5.40
kg
kg
kg
kg
kg
kg
L
Universitas Sumatera Utara
LAMPIRAN III
Data Pengujian
Universitas Sumatera Utara
PENGUJIAN BETON SEGAR
Kode Benda Uji
No.
Parameter
Syarat
1
2
3
4
5
Slump Flow
Slump Flow t50
J ring
V Funnel
V Funnel T5min
650 - 800 mm
2 - 5 sec
0 - 10 mm
8 - 12 sec
+ 3 sec
Keterangan
SCC 0
PP
685
3.2
9
11
13
SCC 0.25
PP
650
3.5
10
12
15
SCC 0.5
PP
600
4.5
12
14
17
SCC 0.75
PP
530
5.4
13
15
19
OK
OK
Not OK
Not OK
PENGUJIAN BETON KERAS
No.
Kode benda
uji
1
2
3
4
5
6
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
7
8
9
10
11
12
1
2
3
4
5
6
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
7
8
9
10
11
12
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
Variasi
Serat
(kg/m3)
w/c
ratio
Berat
(kg)
Umur
(hari)
1
0
0.288
12.2
28
1
0.25
0.288
12.4
28
Beban tekan
aktual
(kN)
(Mpa)
400
390
392
Beban tarik
aktual
(kN) (Mpa)
22.65
22.08
22.19
22.31
138
142
141
850
770
830
6.24
46.24
8.36
9.42
9.24
21.51
21.63
21.63
9.01
21.59
146
146
148
730
620
710
6.13
6.31
6.27
48.12
43.60
46.99
188
212
208
380
382
382
Ratarata
(Mpa)
6.49
6.49
6.58
41.33
35.10
40.20
6.52
38.88
228
224
228
10.13
9.96
10.13
Universitas Sumatera Utara
10.07
1
2
3
4
5
6
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
7
8
9
10
11
12
1
2
3
4
5
6
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
7
8
9
10
11
12
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
No
1
0.5
0.288
1
0.288
12.8
28
Kode Benda Uji
15.51
14.27
15.17
Variasi Serat
1
2
3
4
SCC 0 PP
SCC 0.25 PP
SCC 0.5 PP
SCC 0.75 PP
(Kg/m3)
0
0.25
0.5
0.75
5
6
7
8
SCC 0 PP
SCC 0.25 PP
SCC 0.5 PP
SCC 0.75 PP
0
0.25
0.5
0.75
14.98
120
98
118
12.5
28
0.75
274
252
268
660
594
612
5.33
4.36
5.24
37.37
33.63
34.65
35.22
170
192
184
158
194
188
7.56
8.53
8.18
8.95
10.98
10.64
4.18
3.64
4.18
24.57
25.48
25.25
1
28
4.00
25.10
174
166
172
Umur
(hari)
8.09
10.19
94
82
94
434
450
446
4.98
7.73
7.38
7.64
Kuat Lentur
kN
32
38
33
33
41
48.4
43.2
42
Universitas Sumatera Utara
7.59
LAMPIRAN IV
Foto Dokumentasi
Universitas Sumatera Utara
Semen Portland Tipe I
Serat Polypropylene
Superplasticizer
Universitas Sumatera Utara
Pembuatan Benda Uji
Pembuatan Benda Uji
Cetakan Silinder Benda Uji
Universitas Sumatera Utara
Pengujian Slump Flow
Pengujian Slump Flow
Universitas Sumatera Utara
Pengujian J ring
Pengujian J ring
Pengujian V Funnel
Pengujian V Funnel
Universitas Sumatera Utara
Pengujian Kuat Tekan
Beton Serat SCC
Pengujian Kuat Tarik
Pengujian Kuat Lentur
Universitas Sumatera Utara
Pemeriksaan Material
Universitas Sumatera Utara
ANALISA AYAKAN AGREGAT HALUS
UNTUK MATERIAL PENYUSUN BETON
(ASTM C 136 - 84a)
Diameter Ayakan
(mm)
(No.)
9.50 (3/8 - in)
4.75 (No. 4)
2.36 (No. 8)
1.18 (No. 16)
0.60 (No. 30)
0.30 (No. 50)
0.15 (No. 100)
Pan
Berat
Sampel 1
(gram)
0.0
60.0
72.0
102.0
198.0
228.0
265.0
75.0
Total
1000.0
Fraksi Tertahan
Berat
Berat
Sampel 2
Total
(gram)
(gram)
0.0
0.0
53.0
113.0
75.0
147.0
102.0
204.0
199.0
397.0
228.0
456.0
260.0
525.0
83.0
158.0
1000.0
242.85
100
Klasifikasi FM Pasir Yang Memenuhi Syarat :
Halus
2.2 < FM < 2.6
Sedang
2.6 < FM < 2.9
Kasar
2.9 < FM < 3.2
Modulus Kehalusan (FM)
=
Kumulatif
(%)
0.00
5.65
7.35
10.20
19.85
22.80
26.25
7.90
2000
100
=
2.43
Tertahan
(%)
0.00
5.65
13.00
23.20
43.05
65.85
92.10
100.00
Lolos
(%)
100.00
94.35
87.00
76.80
56.95
34.15
7.90
0.00
Universitas Sumatera Utara
ANALISA AYAKAN AGREGAT KASAR
UNTUK MATERIAL PENYUSUN BETON
(ASTM C 136 - 84a & ASTM D 448 - 86)
Diameter Ayakan
(mm)
38.1 mm
19.1 mm
9.52 mm
4.76 mm
2.38 mm
1.19 mm
0.60 mm
0.30 mm
0.15 mm
Pan
Total
Retained Fraction
Berat
Berat
Berat
Sampel 1
Sampel 2
Total
(gram)
(gram)
(gram)
0.0
0.0
0.0
0.0
0.0
0.0
1544.0
1541.0
3085.0
431.0
429.0
860.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
0.0
25.0
30.0
55.0
2000.0
2000.0
4000
668.88
=
100
Klasifikasi FM Agregat Kasar Yang Memenuhi Syarat :
5.5 ≤ FM ≤ 7.5
Modulus Kehalusan ( FM ) =
Kumulatif
(%)
0.00
0.00
77.13
21.50
0.00
0.00
0.00
0.00
0.00
1.38
100
Tertahan
(%)
0.00
0.00
77.13
98.63
98.63
98.63
98.63
98.63
98.63
100.00
Lolos
(%)
100.00
100.00
22.88
1.38
1.38
1.38
1.38
1.38
1.38
0.00
6.69
Universitas Sumatera Utara
BERAT JENIS DAN ABSORBSI AGREGAT HALUS
UNTUK MATERIAL PENYUSUN BETON
(ASTM C 128 - 88)
KETERANGAN
Sampel 1
Sampel 2
Rata-rata
Berat mula-mula,
gram (S)
500.0
500.0
500.0
Berat piknometer + air +
Pasir ,gram ( C )
976.0
976.0
976.0
Berat kering, gram
(A)
491.0
490.0
490.5
675.0
675.0
675.0
Berat piknometer +
air, gram (B)
Berat jenis kering
=
A
(B+S-C)
2.47
2.46
2.46
Berat jenis SSD
=
S
(B+S-C)
2.51
2.51
2.51
Berat jenis semu
=
A
(B+A-C)
2.58
2.59
2.59
Absorbsi, %
=
( S - A ) x100
A
1.83
2.04
1.94
Universitas Sumatera Utara
BERAT JENIS DAN ABSORBSI AGREGAT KASAR
UNTUK MATERIAL PENYUSUN BETON
(ASTM C 127 - 88)
Sample
I
Sample
II
Average
Berat mula-mula, gram ( B )
1250.0
1250.0
1250.0
Berat piknometer + air + pasir,
gram ( C )
769.0
769.0
769.0
Berat kering, gram (A)
1239.0
1240.0
1239.5
KETERANGAN
Berat jenis kering
=
A
(B-C)
2.58
2.58
2.58
Berat jenis SSD
=
B
(B-C)
2.60
2.60
2.60
Berat jenis semu
=
A
(A-C)
2.64
2.63
2.63
Absorbsi, %
=
( B - A ) x 100
A
0.89
0.81
0.85
Universitas Sumatera Utara
BERAT ISI AGREGAT HALUS
UNTUK MATERIAL PENYUSUN BETON
ASTM C 29/C 29M – 90
Koreksi
(0C)
Suhu ruangan
28.00
0
Suhu air
Massa bejana kosong
Massa air ( A )
Berat isi air ( B )
Faktor koreksi : C =(B/A)
Diameter maksimum
agregat
( C)
(kg)
(kg)
26.00
0.46
1.90
(kg/m3)
996.77
523.79
(mm)
5.00
Hasil pengujian
KETERANGAN
Berat
Sampel I
Sampel II
Total
Cara merojok
3.54
3.55
7.09
Cara menyiram
3.34
3.36
6.70
Rata-rata
3.55
3.35
Berat net (G)
3.09
2.89
1615.89
1513.75
Berat isi (G*C) [kg/m3]
Universitas Sumatera Utara
BERAT ISI AGREGAT KASAR
UNTUK MATERIAL PENYUSUN BETON
ASTM C 29/C 29M - 90
Koreksi
Suhu ruangan
(0C)
28.00
Suhu air
Massa bejana kosong
Massa air ( A )
(0C)
(kg)
(kg)
26.00
5.00
9.20
(kg/m3)
996.77
(mm)
108.345
25.00
Berat isi air ( B )
Faktor koreksi : C =(B/A)
Diameter maksimum agregat
Hasil
pengujian
KETERANGAN
Berat
Sampel I
Sampel II
Total
Cara merojok
19.6
19.5
39.1
Cara menyiram
18.4
18.5
36.9
Rata-rata
19.55
18.45
Berat net (G)
14.55
13.45
1576.42
1457.24
Berat isi (G*C) [kg/m3]
Universitas Sumatera Utara
KADAR LUMPUR AGREGAT HALUS
DENGAN PENCUCIAN
UNTUK MATERIAL PENYUSUN BETON
( ASTM C 117 - 90 )
KETERANGAN
Sampel I
Sampel II
Rata-rata
Berat mula - mula, gram
500
500
500
Berat kering, gram
489
487
488
Berat material yang lolos ayakan No.
200, gram
11
13
12
Persentasi material yang lolos ayakan
No. 200, gram
2.2
2.6
2.4
Universitas Sumatera Utara
KADAR LUMPUR AGREGAT KASAR
DENGAN PENCUCIAN
UNTUK MATERIAL PENYUSUN BETON
( ASTM C 117 - 90 )
KETERANGAN
Sampel I
Sampel II
Rata-rata
1000
1000
1000
997
996.0
996.5
Berat material yang lolos ayakan No.
200, gram
3
4.0
3.5
Persentasi material yang lolos ayakan
No. 200, gram
0.3
0.4
0.35
Berat mula - mula, gram
Berat kering, gram
Universitas Sumatera Utara
LAMPIRAN II
Perencanaan Campuran
Universitas Sumatera Utara
Langkah 1. Menentukan Slump dan kekuatan beton yang diinginkan
Beton f'c 35 Mpa dengan menggunakan HRWR, slump yang digunakan
sebelum penambahan HRWR yaitu 2,5-5cm
f’cr
=
121.8 Mpa
Langkah 2. Menentukan ukuran maksimum agregat : 1-1,3cm
Langkah 3. Menentukan kadar optimum agregat kasar
Berat kering agregat kasar
= 945.852
kg/m3
Langkah 4. Estimasi air campuran dan kadar udara
estimasi air=
130.00 kg/m3
Langkah 5. Menentukan w/c+p =
0.288889
Langkah 6. Menghitung kadar bahan semen
semen
=
450.00 kg/m3
Langkah 7. Perhitungan komposisi dasar
- kadar semen per m3=
450.00
- volume material per kg/m3 kecuali pasir
semen=
0.145 m3
a. Kasar=
0.367 m3
air=
0.130 m3
udara=
0 m3
volume total=
0.642 m3
- volume pasir=
0.358 m3
berat pasir=
881.24 kg
Universitas Sumatera Utara
campuran akhir /m3 beton
semen=
450.00
pasir=
881.24
agregat kasar=
945.852
air=
130.00
berat total=
2407.10
HRWR=
5400.00
kg
kg
kg
kg
mL
substitusi fly ash 10%
- kadar semen per m3=
405.00
- volume material per kg/m3 kecuali pasir
semen=
0.131 m3
fly ash=
0.020 m3
a. Kasar=
0.367 m3
air=
0.130 m3
udara=
0 m3
volume total=
0.648 m3
volume pasir=
0.352 m3
405
45
945.852
130
kg
kg
kg
kg
866.64 kg
Campuran akhir /m3 beton:
Semen
Silica fume
Pasir
Agregat kasar
Air
berat total
HRWR
405.00
45.00
866.64
945.852
130.00
2392.49
5.40
kg
kg
kg
kg
kg
kg
L
Universitas Sumatera Utara
LAMPIRAN III
Data Pengujian
Universitas Sumatera Utara
PENGUJIAN BETON SEGAR
Kode Benda Uji
No.
Parameter
Syarat
1
2
3
4
5
Slump Flow
Slump Flow t50
J ring
V Funnel
V Funnel T5min
650 - 800 mm
2 - 5 sec
0 - 10 mm
8 - 12 sec
+ 3 sec
Keterangan
SCC 0
PP
685
3.2
9
11
13
SCC 0.25
PP
650
3.5
10
12
15
SCC 0.5
PP
600
4.5
12
14
17
SCC 0.75
PP
530
5.4
13
15
19
OK
OK
Not OK
Not OK
PENGUJIAN BETON KERAS
No.
Kode benda
uji
1
2
3
4
5
6
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
7
8
9
10
11
12
1
2
3
4
5
6
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
7
8
9
10
11
12
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
SCC 0.25 PP
Variasi
Serat
(kg/m3)
w/c
ratio
Berat
(kg)
Umur
(hari)
1
0
0.288
12.2
28
1
0.25
0.288
12.4
28
Beban tekan
aktual
(kN)
(Mpa)
400
390
392
Beban tarik
aktual
(kN) (Mpa)
22.65
22.08
22.19
22.31
138
142
141
850
770
830
6.24
46.24
8.36
9.42
9.24
21.51
21.63
21.63
9.01
21.59
146
146
148
730
620
710
6.13
6.31
6.27
48.12
43.60
46.99
188
212
208
380
382
382
Ratarata
(Mpa)
6.49
6.49
6.58
41.33
35.10
40.20
6.52
38.88
228
224
228
10.13
9.96
10.13
Universitas Sumatera Utara
10.07
1
2
3
4
5
6
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
7
8
9
10
11
12
1
2
3
4
5
6
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.5 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
7
8
9
10
11
12
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
SCC 0.75 PP
No
1
0.5
0.288
1
0.288
12.8
28
Kode Benda Uji
15.51
14.27
15.17
Variasi Serat
1
2
3
4
SCC 0 PP
SCC 0.25 PP
SCC 0.5 PP
SCC 0.75 PP
(Kg/m3)
0
0.25
0.5
0.75
5
6
7
8
SCC 0 PP
SCC 0.25 PP
SCC 0.5 PP
SCC 0.75 PP
0
0.25
0.5
0.75
14.98
120
98
118
12.5
28
0.75
274
252
268
660
594
612
5.33
4.36
5.24
37.37
33.63
34.65
35.22
170
192
184
158
194
188
7.56
8.53
8.18
8.95
10.98
10.64
4.18
3.64
4.18
24.57
25.48
25.25
1
28
4.00
25.10
174
166
172
Umur
(hari)
8.09
10.19
94
82
94
434
450
446
4.98
7.73
7.38
7.64
Kuat Lentur
kN
32
38
33
33
41
48.4
43.2
42
Universitas Sumatera Utara
7.59
LAMPIRAN IV
Foto Dokumentasi
Universitas Sumatera Utara
Semen Portland Tipe I
Serat Polypropylene
Superplasticizer
Universitas Sumatera Utara
Pembuatan Benda Uji
Pembuatan Benda Uji
Cetakan Silinder Benda Uji
Universitas Sumatera Utara
Pengujian Slump Flow
Pengujian Slump Flow
Universitas Sumatera Utara
Pengujian J ring
Pengujian J ring
Pengujian V Funnel
Pengujian V Funnel
Universitas Sumatera Utara
Pengujian Kuat Tekan
Beton Serat SCC
Pengujian Kuat Tarik
Pengujian Kuat Lentur
Universitas Sumatera Utara