Sintesis dan Karakterisasi Mesopori Silika dari Sekam Padi Dengan Metode Kalsinasi
SYNTHESIS AND CARACTERIZATION OF MESOPOROUS SILICA
FROM RICE HUSK BY CALCINATION METHODS
ABSTRACT
Has done research on the synthesis and characterization of mesoporous silica from
rice husk by calcination methods with variations in temperature 800oC, 900oC and
850°C in order to obtain rice husk ash. Further purified by hydrochloric acid to
obtain silica with minimum levels of other minerals. Silica derived from rice
husks were extracted with sodium hydroxide followed by re-precipitation using
hydrochloric acid to obtain mesoporous silica and a large surface area. FT-IR data
which achieved was good enough because has the resemble with commercial
silica. XRD difractogram also show there is wide peak at 22,7o area was show that
silica was amorf. Isotherm of nitrogen adsorbtion-desorption silica result show
that isotherm adsorbtion Type IV was mesophore characteristic and achieved that
distribution of pore size between 5 till 17 nm along with volume and silica width
surface area based on calculation of BJH each 0,817 cm3g-1 and 243,165 m2g-1.
Keywords : rice husk, silica, calcinations, meshopore
Universitas Sumatera Utara
SINTESIS DAN KARAKTERISASI MESOPORI SILIKA
DARI SEKAM PADI DENGAN METODE KALSINASI
ABSTRAK
Telah dilakukan penelitian mengenai sintesis dan karakterisasi mesopori silika
dari sekam padi dengan metode kalsinasi dengan variasi suhu 800oC, 850oC dan
900oC sehingga diperoleh abu sekam padi. Selanjutnya dimurnikan dengan
asam klorida untuk memperoleh silika dengan kadar minimum dari mineral lain.
Silika yang diperoleh dari sekam padi diekstraksi dengan natrium hidroksida
diikuti dengan pengendapan kembali menggunakan asam klorida untuk
memperoleh silika mesopori dan luas permukan yang besar. Data FT-IR yang
diperoleh cukup baik karena memiliki kemiripan dengan silika komersial.
Difraktogram XRD juga menunjukkan adanya puncak melebar pada daerah
22,7o menunjukkan bahwa silika berbentuk amorf. Hasil adsorpsi desorpsi
nitrogen isotherm silika memperlihatkan adsorbsi isotherm Tipe IV yang
merupakan karekteristik material mesopori dan diperoleh distribusi ukuran pori
antara 5 sampai 17 nm serta volume dan luas permukaan silika berdasarkan
perhitungan BJH masing-masing 0,817 cm3g-1 dan 243,165 m2g-1
Kata kunci : sekam padi, silika, kalsinasi, mesopori
Universitas Sumatera Utara
FROM RICE HUSK BY CALCINATION METHODS
ABSTRACT
Has done research on the synthesis and characterization of mesoporous silica from
rice husk by calcination methods with variations in temperature 800oC, 900oC and
850°C in order to obtain rice husk ash. Further purified by hydrochloric acid to
obtain silica with minimum levels of other minerals. Silica derived from rice
husks were extracted with sodium hydroxide followed by re-precipitation using
hydrochloric acid to obtain mesoporous silica and a large surface area. FT-IR data
which achieved was good enough because has the resemble with commercial
silica. XRD difractogram also show there is wide peak at 22,7o area was show that
silica was amorf. Isotherm of nitrogen adsorbtion-desorption silica result show
that isotherm adsorbtion Type IV was mesophore characteristic and achieved that
distribution of pore size between 5 till 17 nm along with volume and silica width
surface area based on calculation of BJH each 0,817 cm3g-1 and 243,165 m2g-1.
Keywords : rice husk, silica, calcinations, meshopore
Universitas Sumatera Utara
SINTESIS DAN KARAKTERISASI MESOPORI SILIKA
DARI SEKAM PADI DENGAN METODE KALSINASI
ABSTRAK
Telah dilakukan penelitian mengenai sintesis dan karakterisasi mesopori silika
dari sekam padi dengan metode kalsinasi dengan variasi suhu 800oC, 850oC dan
900oC sehingga diperoleh abu sekam padi. Selanjutnya dimurnikan dengan
asam klorida untuk memperoleh silika dengan kadar minimum dari mineral lain.
Silika yang diperoleh dari sekam padi diekstraksi dengan natrium hidroksida
diikuti dengan pengendapan kembali menggunakan asam klorida untuk
memperoleh silika mesopori dan luas permukan yang besar. Data FT-IR yang
diperoleh cukup baik karena memiliki kemiripan dengan silika komersial.
Difraktogram XRD juga menunjukkan adanya puncak melebar pada daerah
22,7o menunjukkan bahwa silika berbentuk amorf. Hasil adsorpsi desorpsi
nitrogen isotherm silika memperlihatkan adsorbsi isotherm Tipe IV yang
merupakan karekteristik material mesopori dan diperoleh distribusi ukuran pori
antara 5 sampai 17 nm serta volume dan luas permukaan silika berdasarkan
perhitungan BJH masing-masing 0,817 cm3g-1 dan 243,165 m2g-1
Kata kunci : sekam padi, silika, kalsinasi, mesopori
Universitas Sumatera Utara