Analisis dan Karakterisasi Kitosan Bead Manik dengan Ikatan Silang Glutaraldehida Sebagai Adsorben untuk Menurunkan Kadar Ion Logamcadmium(Cd2+)

ANALISIS DAN KARAKTERISASI, KITOSAN BEAD/MANIK
DENGAN IKAT SILANG GLUTARALDEHIDA SEBAGAI
ADSORBEN UNTUK MENURUNKAN KADAR
IONLOGAM KADMIUM (Cd2+)

ABSTRAK

Penelitian mengenai analisis dan karakterisasi kitosan bead/manik dengan ikat
silang glutaraldehida sebagai adsorben untuk menurunkan kadar ion logam
kadmium(Cd2+) telah dilakukan. Pada penelitian ini, didahului dengan pembuatan
kitosan bead/manik dengan mencampurkan kitosan dan asam asetat 5% dan
diteteskan kedalam larutan NaOH 2M yang kemudian membentuk gel (bead).
Kitosan bead yang telah dikeringkan direndam selama 24 jam dalam larutan
Glutaraldehida 2,5% dengan perbandingan 1,5 mL tiap gram kitosan, dicuci dan
dikeringkan, sebanyak 2 gram kitosan ikat silang glutaraldehida dimasukkan ke
dalam kolom, lalu ditambahkan dengan 50 mL larutan standar kadmium
5mg/L.didiamkan berdasarkan variasi waktu. Hasil penelitian menunjukkan
bahwa proses adsorpsi diperoleh persentase penyerapan 98,472% pada waktu
kontak optimum 30 menit.

Kata kunci : Kitosan Glutaraldehida,Adsorben, Logam Cd

Universitas Sumatera Utara

ANALYSIS AND CHARACTERIZATION OF BEAD CHITOSAN WITH
GLUTARALDEHYDE CROSSLINKING AS REDUCING
ADSORBENT CADMIUM METAL CONTENT
ABSTRACT

Research on the analysis and characterization of chitosan beads with
glutaraldehyde crosslink has been done as an adsorbent to reduce concentration
of Cd metal. In this research, preceded by making chitosan beads by mixing
chitosan and 5% acetic acid and dropped into a solution of NaOH 2M which then
forms gel (bead). Chitosan beads were dried soaked for 24 hours in a solution of
Glutaraldehyde 2.5% with a ratio of 1.5 mL per gram of chitosan, washed and
dried, 2 grams of glutaraldehyde crosslink chitosan included in the column, then
was added with 50 ml of standard solution of cadmium 5mg / L was alllowed by
variations in time. The results showed that the adsorption process was gained
98.472% in the percentage of absorption optimum contact time of 30 minutes.

Keywords: Chitosan Glutaraldehyde, Adsorbent, Cd Metal