Mesoporous ZSM 5 catalysts Preparation, characterisation

  Microporous and Mesoporous Materials 89 (2006) 78–87 www.elsevier.com/locate/micromeso

Mesoporous ZSM-5 catalysts: Preparation, characterisation

and catalytic properties. Part I: Comparison of different synthesis routes

b a c a,* _a

Yi Hsin Chou , Colin S. Cundy , Arthur A. Garforth , Vladimir L. Zholobenko

_b

School of Chemical Engineering and Analytical Science, University of Manchester, P.O. Box 88, Sackville Street, Manchester M60 1QD, United Kingdom

  

Centre for Microporous Materials, School of Chemistry, University of Manchester, P.O. Box 88, Sackville Street, Manchester M60 1QD, United Kingdom

_c

School of Chemistry and Physics, Keele University, Staffordshire ST5 5BG, United Kingdom

Received 13 July 2005; received in revised form 30 September 2005; accepted 12 October 2005

Available online 23 November 2005

  Abstract

In an attempt to improve mass-transport limitations, mesopores were created in a series of ZSM-5 catalysts by the carbon-templating

procedure. A successful low-cost dry gel synthesis route was developed which almost entirely removed the need for the organic structure-

directing agent (TPA/SiO = 0.0033). Both an aqueous colloidal graphite sol and a pyrogenic (carbon black) material were investigated,

₂

at addition levels of 16.5–100 wt.%. No major differences were observed between the two carbon sources. The addition of carbon to the

synthesis composition retarded the crystallisation rate and modified the crystal morphology. The products were characterised by a vari-

ety of physical techniques. Additional post-synthesis treatment (alkaline leaching) extended the mesopore system but also tended to

reduce crystallinity and micropore volume.

  2005 Elsevier Inc. All rights reserved.

  Keywords: Hydrothermal synthesis; Dry gel synthesis; Carbon-templating; ZSM-5; Acidity

  1. Introduction are allowed to ingest carbon particles during their growth

   . On calcination of the resulting carbon-aluminosili-

  The presence of mesopores in zeolite crystals assists in cate composite, mesopores are left by the removal of the alleviating mass transfer limitations for reactants and prod- nanosized carbon particles. Such multiporous crystals are ucts in catalysis by reducing diffusional path lengths effect as reducing the crystallite size of the sample. The A limitation of the current carbon ‘‘templating’’ proce- micropore system of zeolites can be extended to a hierarchy dure appears to be the high quantity of organic structure of pore sizes in a number of ways. For example, an already directing agent (SDA) required for the synthesis, combined porous structure can be ‘‘zeolitised’’ to provide additional with the fairly low aluminium content in the product micropores . The objectives of the present work were (a) to com- packed together to generate inter-crystalline mesopores pare different methods for introducing mesoporosity into

  

. An alternative to these procedures is to modify the zeo- high-silica zeolite crystals and (b) to generate a strongly

  lite crystals themselves in order to create larger intra-crys- acidic ZSM-5 catalyst with a high framework aluminium talline voids, usually by a post-synthesis combination of content using a minimum of SDA. To achieve the first steaming and acid leaching and also used in combination with it. In addition, a special form of the ^* steam-assisted crystallisation (SAC) method was Corresponding author.

  E-mail address: (Y.H. Chou). developed to achieve both objectives. In this procedure, 1387-1811/$ - see front matter 2005 Elsevier Inc. All rights reserved. doi:10.1016/j.micromeso.2005.10.014 the reaction mixture is reduced to a dry powder and then heated in contact with saturated water vapour. This tech- nique has proved effective in the synthesis of a variety of zeolites, usually at modest SDA/SiO

  2

  2

  3

  2 O

  2 O:2.0Al

  2.2.1. Preparation of reference sample (carbon-free, SAC1) The seeding gel as described for HT1 was used in this preparation, whilst the alkali concentration of the feedstock gel was lowered (3.5Na

  2.2. Steam-assisted conversions (SAC)

  and 18.48 g of deion- ised water) was added into the graphite solution under con- tinuous stirring. Ludox AS-40 (15.53 g) was then introduced into the mixture and the gel was stirred for an hour before addition of the seeding gel (3.2 g). The overall gel was stirred for a further hour and then heated in an autoclave at 180 C for 42 h. The product isolation proce- dure was as for HT1.

  2.1.3. Preparation with addition of carbon (HT2) An aqueous colloidal graphite sol (Aquadag P, solids content 22 wt.%, average particle size <2 lm and mostly submicron, Acheson Industries Inc.) was used as the car- bon source. After making allowance for this additional aqueous component, the preparation was otherwise similar to that for HT1. The quantity of carbon from Aquadag P was equivalent to 50 wt.% of the silica used in the reaction. Aquadag P (13.64 g) was diluted with 20.6 g of deionised water, and a pre-prepared sodium aluminate solution (0.62 g of NaOH, 0.69 g of NaAlO

  2

  The feedstock gel was identical to that used in the prep- aration of HT1, colloidal silicalite (5 wt.% with respect to The synthesis and the separation of product were carried out as described in HT1.

  The colloidal silicalite product was dialysed to give an aqueous sol of pH 8.3 and solids content 4.5 wt.% before being used as a seed.

  The reaction solution was prepared by mixing 14.2 g of TEOS (98%, Aldrich), 25 g of TPAOH solution and 5.9 g of deionised water in a sealed PP bottle and then stirring at room temperature for 3 days to give a homogeneous solution. The solution was then heated at 90 C for 3 days.

  2 O:240EtOH.

  :1150H

  2

  :60.0SiO

  : 870H

  In this preparation, colloidal silicalite was used to seed the synthesis of ZSM-5. The colloidal silicalite gel composition was 10.8(TPA)

  2 O) into

  fle furnace (Carbolite Corp.) from ambient temperature at

  2.3. Calcination of as-made materials The as-made zeolite samples were heated in air in a muf-

  Detailed information is given in .

  2 /TPA = 10) in the synthesis was also investigated.

  2.2.2. Preparation with addition of carbon The gel preparations for the syntheses involving carbon were identical to that of the reference sample (SAC1), except for the addition of carbon prior to the drying of the overall gel. Three levels of carbon loading and two carbon sources were used, namely Aquadag P and BP2000 (carbon black with an average particle size 12 nm, Cabot Corp.). The use of additional SDA (TPABr with SiO

  a special autoclave. The water in the overall gel was gently evaporated on a hotplate (75 C) under continuous stirring to obtain a thick gel. This was then dried at 100 C for 16 h. The dry gel was ground into fine powder and placed in a fluoropolymer cup surrounded by sufficient water to provide saturated steam inside a PTFE-lined auto- clave at 180 C for 24 h. The product isolation was as for HT1.

  :0.21TPAOH:896H

  2 O). The preparation procedures were the same as

  2

  :60.0SiO

  3

  2 O

  2 O:1.86Al

  for HT1 except for an additional drying procedure which was carried out prior to transferring the overall gel (3.58Na

  2 O:60SiO

  2.1.2. Preparation using colloidal silicalite as seed (carbon-free, CS1)

  ratios and sometimes in unusual compositional ranges.

  :1200H

  3

  2 O

  2 O:2.0Al

  Using the same reagent sources as above, a feedstock gel (6.5Na

  the formation of the final product. The seeding gel was pre- pared by dissolving 0.30 g of NaOH (99%, BDH) in 11.38 g of deionised water followed by adding 2.54 g of TPAOH (1 M aqueous solution, Lancaster Synthesis). Then 7.50 g of Ludox AS-40 silica sol (Aldrich) was introduced into the solution and the mixture was stirred at room tempera- ture for 30 min. This homogeneous gel was then sealed in a polypropylene (PP) bottle and aged at 100 C for 16 h.

  2 O) was used to direct

  2

  2

  2 O:3.0TPAOH:60SiO

  (4.5Na

  2.1.1. Preparation of reference sample (carbon-free, HT1) A special seeding gel containing no aluminium

   ).

  2.1. Standard hydrothermal preparations The starting point for these preparations was a pub- lished procedure This was adapted for the hydrother- mal syntheses and extensively modified for the steam assisted conversions (Section

  2. Experimental

  :60.0SiO

  :1916.0H

  was then stirred for 30 min to obtain homogeneity, trans- ferred to a PTFE-lined autoclave, and heated at 180 C for 42 h. After cooling, the product was isolated by centrifugation, washed with deionised water and dried at 100 C.

  2 O:1.86Al

  2 O)

  :0.21TPAOH:1864.0H

  2

  :60.0SiO

  3

  2 O

  NaOH solution (0.62 g of NaOH in 49.72 g of deionised water) followed by adding 15.53 g of Ludox AS-40 sol. This mixture was stirred for 1 h at room temperature before addition of 3.2 g of seeding gel. The overall gel (6.36Na

  2 O) was made

  2 O, Fisher Scientific) in

  2 O:17.9 wt.%H

  :31.2 wt.%Na

  3

  2 O

  by dissolving 0.69 g of sodium aluminate (50.9 wt.% Al

  

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87

3.5Na

2 O:6.0TPABr:2.0Al

  The calcined sodium form of the zeolites (1 g) was ion- exchanged with 0.1 M NH

  ^{2 O 3 :60.0SiO 2 :870H 2 O otherwise only minimal} template (derived from the seeding gel) was used (TPA/SiO ^{2 = 0.0033).}

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87

  33 TPABr 168 BP3 BP2000 50 – 168 BP4 BP2000 100 – 504 _a Water in Aquadag P was taken into account in calculating the overall reaction composition. _b Relative to the weight of the silica used in the overall gel (e.g. 6.2 g of BP2000 was used in the synthesis of BP4 where the quantity of silica was also 6.2 g). _c Where indicated the gel composition with added TPABr was

  50 TPABr 168 BP1 BP2000 33 – 168 BP2 BP2000

  96 AP4 Aquadag P 50 – 168 AP5 Aquadag P

  96 AP3 Aquadag P 50 –

  96 AP2 Aquadag P 33 –

  (wt.%) SDA Heating duration (h) AP1 Aquadag P 16.5 –

  Table 1 Conditions for ZSM-5 syntheses at 180 C Sample Carbon Level of carbon

  3.1. Standard hydrothermal synthesis with and without carbon The strategy adopted has been to select a reliable stan- dard preparation of high-Al ZSM-5 and then to adapt this in various ways for carbon-modified syntheses. The route chosen was based on that of Lechert and Kleinwort, as described in the IZA collection of verified syntheses . The method is fundamentally that of an ‘‘inorganic’’ (i.e. non-organic-templated) route , but modified by the use of a Na,TPA-based seeding gel in order to encourage

  3. Results and discussion

  The Brønsted site density was calculated from the pyri- dine uptake using the Beer–Lambert law with an absorption coefficient of 1.0038 derived by calibration against a standard ZSM-5 (Si/Al = 36, Zeolyst) containing very little extra-framework aluminium.

  2.4. Post-synthesis modification—alkaline leaching and ion-exchange Several samples (AP4, BP1, and BP2) were treated with alkali in an attempt to increase pore volume by removing amorphous material as well as potentially developing the mesopores in the zeolite structure. Each calcined sample ( 660 mg) was dispersed in 20 ml 0.2 M sodium hydroxide solution, sealed in a PP bottle and stirred at 85 C for 30 min. The suspension was then cooled to 0 C and the solid material was isolated, washed and dried.

  1

  solution. The treat- ment was repeated three times (4 exchanges in all) and the zeolite was then washed thoroughly with deionised water following by drying at 100 C. The ammonium forms of the zeolites were calcined again (500 C) to produce the hydrogen form.

  3

  solution (150 ml) at

4 NO

  60 C under constant agitation for 4 h. The zeolite suspen- sion was then centrifuged and the liquor was replaced by the same quantity of fresh NH

  3

4 NO

  2.5. Characterisation

  region at a resolution of 2 cm

  2.5.1. X-ray diffraction Zeolite samples were characterised by XRD using a Phi- lips PW 1770 diffractometer with nickel filtered CuK _a radi- ation scanning in the range of 3–50 (2h) at an angular rate of 0.3 /min with a step size of 0.01 .

  2.5.2. Scanning electron microscopy The microscope images were taken under high vacuum and medium voltage (20 kV) using a FEI Quanta 200 Envi- ronmental SEM (Philips). Samples were prepared by evenly dispersing a small amount of powdered zeolite on to a car- bon double-sided tape, which was then attached to a round

  2.5.3. Thermal gravimetric analysis A SDT 2960 simultaneous DTA–TGA instrument was used to determine by weight the amount of water, organic template (TPA) and carbon in the prepared zeolites. Typi- cally, a small sample (10 mg) was heated in flowing air (100 ml/min). The temperature programme of the furnace used was composed of four segments. Samples were initially maintained at 25 C for 1 h, then heated to 150 C (5 C/ min) and held for 2 h. The temperature was then increased to 250 C (10 C/min) and held for a further 2 h. Finally the temperature was raised to 800 C (10 C/min) and held for 1 h.

  2.5.4. Nitrogen physisorption The powdered sample (0.15 g) was previously degassed under vacuum at 350 C for 16 h and nitrogen adsorption at 196 C was carried out using a Micromeritics ASAP 2010 instrument.

  2.5.5. Fourier transform infrared spectroscopy Transmittance FTIR spectra of self-supported zeolite discs (10 mg) were collected using a Nicolet Prote´ge´ 460 spectrometer equipped with an MCT detector by averaging 200 accumulated scans in the 1300–4000 cm

  1

  . The sample discs were activated under vacuum (1.32 mPa) at 450 C for 6 h (the tempera- ture was ramped from ambient temperature at 1 C/min). Acidic properties of the activated samples were evaluated using pyridine (Py) adsorption. Typically, an excess of pyr- idine was admitted by injection of 0.1 ll aliquots into the transmittance cell at 150 C until no changes were observed in the spectra. Following each adsorption step, the sample was evacuated for 5 min at 150 C to remove weakly bound pyridine, and the FTIR spectrum was collected. The obtained infrared spectra were analysed (including integra- tion, subtraction and determination of peak positions) using specialised Nicolet software, Omnic 4.1. In the version employed here, the preparation was found to crystallise reproducibly to give a ZSM-5 sample with Si/Al = 23 and the morphology shown in ((a) and (b)). The synthesis involving colloidal silicalite as a seed (CS1) was found to have a very different morphology from HT1with very small crystallite size ( 150 nm, (c)).

  A trial was then carried out to determine whether any carbon could be incorporated by simply adding an aqueous colloidal graphite dispersion (Aquadag P) to the aqueous reaction mixture. Although the black products (HT2) made by this procedure contained up to 18 wt.% carbon (from TGA), optical and electron microscopic examination showed them to be physical mixtures of carbon particles and ZSM-5 particles having the same morphology as the carbon-free reference sample (HT1). The colloidal graphite clearly had only ‘‘bystander’’ status and consequently little or no influence on the zeolite synthesis. A further proof of this was the observation that the added carbon had no effect on the crystallisation time.

  3.2. Steam-assisted conversion with and without carbon Following the exploratory work described above, the standard preparation was modified to render it suitable for the steam-assisted conversion (SAC) technique

   , principally by a reduction in the base level. At

  180 C, the SAC synthesis yielded a well-crystallised sample of ZSM-5 (Si/Al = 20) in 1 day. However, the mor- thermal route ( ). Rather than the polycrystalline aggregates produced by the bulk solution synthesis, the SAC preparation consisted of well-formed single crystals (some intergrown) in the 6–10 lm size range.

  The SAC method was then used for the incorporation of carbon, utilizing both colloidal (Aquadag P) and nanosized solid (Cabot BP2000) sources. However, the progress of the reaction was now found to be considerably modified by the presence of the carbon, the overall reaction rate slowing down as the level of carbon was increased.

  3.3. Carbon-zeolite composite crystals A range of materials were synthesised with varied levels and type of added carbon. As a further modification, TPA cation (as TPABr) was added in pore-filling quantities (SiO

  2

  /TPA = 10) in an attempt to influence further the product crystal size and morphology.

  3.3.1. X-ray diffraction All the carbon containing zeolite samples (AP1-5, BP1-

  4) were characterised by XRD and some selected patterns are shown in where SAC1 (no carbon) was found to have reached high crystallinity in 24 h The crystallisation rate was found to reduce with increas- ing carbon quantity (16.5–50 wt.%), leading to incomplete reaction even when 96 h heating time was allowed. How- ever, an extended heating time (168 h) improved crystal-

  

Fig. 1. The standard hydrothermal ZSM-5 samples used in this work: (a) HT1 spherical polycrystalline aggregates of particle size 3 lm at low

magnification (·2500), (b) HT1 at high magnification (·30,000), (c) CS1 (high magnification: ·102,400).

  

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87

  

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87

Fig. 2. Carbon-free ZSM-5 sample (SAC1) synthesised by the steam-assisted conversion (SAC) route (a) low magnification (·15,000), (b) high

magnification (·60,000).

  SAC1 AP4L AP4 BP1L BP1 BP2L _{5 10 15 20 25 30 35 40 45 50 2 Theta} BP2 _{5 10 15 20 25 30 35 40 45 50 2 Theta} (a) (b)

Fig. 3. XRD patterns of selected (a) calcined and (b) caustic-leached samples.

  was also observed in the BP series, BP4 (100 wt.%) allowing the caustic solution to attack the framework more requiring three times longer heating (504 h) to gain effectively under similar conditions. approximately the same crystallinity as BP1 (33 wt.%).

  3.3.2. Crystal sizes and morphologies Moreover, the addition of TPABr caused the lower crys-

  The SEM images of selected samples are shown in tallinity ( 70%) of BP2 even though the heating time was extended to 168 h and the carbon level was the same as . Whilst the primary particle size remained similar that for BP1. between SAC1 and the majority of the carbon-loaded sam-

  As mentioned, a range of crystallinities were observed ples ( 6–10 lm), there was a marked change in morphol- for the synthesised zeolites, i.e. these samples contained dif- ogy across the AP and BP series. As the carbon content ferent levels of amorphous material. Several samples (AP4, of the synthesis mixture rose, the crystal blocks of the prod- BP1 and BP2) were selected for alkaline leaching (0.2 M uct became increasingly fissured and polycrystalline. NaOH, 85 C) and the XRD patterns are shown in Finally, at 100% loading in sample BP4, (h), the ori-

  

It is notable that BP1L shows sharper and more ginal block structure was lost and the product crystals

  intense diffraction peaks after the caustic wash while the consisted of lath-like strips. This variation of morphology others (BP2L and AP4L) have reduced diffraction intensi- confirmed that the carbon was exerting a definite effect ties. One possible explanation could be that the caustic upon the crystallisation of zeolite. solution successfully dissolves the amorphous material in The addition of reagent quantities of TPA to the synthe- sample BP1 but at the same time extracts some Si from sis composition (samples AP5 and BP2) did not lead to for- the framework (desilication). However, in AP4 and BP2 mation of smaller crystals, but again modified the crystal the desilication effect was perhaps too severe and conse- morphology, and (h). Surprisingly, there was no quently led to the partial collapse of the framework. There- obvious change in morphology when the nanoparticulate fore, it is reasonable to assume that AP4 and BP2 had more BP2000 replaced Aquadag P as the carbon source in the

  3.3.3. Thermal analysis The carbon contents in the uncalcined products were determined by TGA. The example TGA and DTG plots of AP4 and AP5 are shown in .

  The weight losses before 250 C were due to the mois- ture desorbed from the samples. The only difference of TPA used (30 times larger in the latter) and hence the majority of micropores in AP5 were filled with TPA. As a consequence, AP5 contained less moisture (3% measured weight loss between 25 and 250 C, (b)) compared to AP4 (5.7%). The most prominent weight loss was observed between 250 and 800 C and can be attributed to the

  

Fig. 4. SEM images of calcined samples (nominal carbon contents of precursors in parentheses): (a) AP1 (16.5%); (b) AP2 (33%), (c) AP4 (50%); (d) AP5

(50%); (e) BP1 (33%); (f) BP3 (50%); (g) BP4 (100%); and (h) BP2 (33%). Samples AP5 (d) and BP2 (h) were synthesised with TPA/SiO ^{2 = 0.10, otherwise} TPA/SiO ^{2 = 0.0033.}

  

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87

  43.5 _a From reaction composition. _b Determined by TGA.

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87

  17.6 BP1

  R ate o f W eig h t L o ss ( % /m in )

  ^{900 800 700 600 500 400 300} 100 ^{200 800 o C 250 o C 150 o C}

• _{-0.2 25 o C}
^{0.0 0.2 0.4 0.6 0.8 1.0 1.2 1.4 1.6} _{100 200 300 400 500} Time (min) ^{100 200 300 400 500 600 700 800 900 TPA}

Fig. 5. TGA plots of as-made ZSM-5 (a) AP4, (b) AP5 (with the decomposition of TPA clearly visible) and DTG plots (c) AP4, (d) AP5 (with an

additional TPA peak).

  Table 2 Carbon content in the synthesis mixture and the final product Sample Carbon content (wt.%) Reaction precurso AP4

  33.3

  15.7 AP5 (TPA)

  33.3

  24.8

  Time (min) ^{100 200 300 400 500 600 700 800 900}

  19.6 BP2 (TPA)

  24.8

  17.6 BP3

  33.3

  28.8 BP4

  50.0

  R ate o f W eig h t L o ss ( % /m in )

  (b) (c) (d) ^{98.4% 97% 90.8% 73.2% 25 o C 150 o C 250 o C 800 o C 70 75 80 85 90 95 100 100 200 300 400 500}

• _-0.2 25 ^{o C 150 o C 250 o C 800 o C}
^{0.0 0.2 0.4 0.6 0.8 1.0 1.2 1.4 1.6} _{100 200 300 400 500} Time (min)

  3

   details the carbon levels used in the synthesis and

  the carbon determined from post-synthesis TGA experi- ments. The carbon contents determined in the final prod- ucts are between 70% and 90% of the nominal added carbon in the reaction precursor for the BP series. The rea- son for the apparently much larger discrepancies ( 50%) with the AP materials is not at present known.

  3.3.4. Sorption studies The nitrogen adsorption isotherms of selected zeolite samples are given in . The samples from traditional hydrothermal syntheses (HT1 and CS1) have different types of hysteresis loops. The shape of the HT1 curve (a)) indicates two types of mesopores resulting from the morphology of spherical polycrystalline aggregates slit-shaped pores (p/p = 0.42–0.9) and more

  CS1 appears only at high relative pressure (p/p = 0.9– 1.0) and reflects inter-crystalline voids in the packing of small crystals ( 150 nm). Sample SAC1 shows only a very small hysteresis loop which suggests the presence of some slit-like inter-crystalline voids deriving from the packing of block-like crystals ( ).

  The nitrogen adsorption isotherms of the carbon-modi- fied zeolites (AP4, AP5, BP1-4) are shown in The hysteresis loops of the carbon-derived samples are all larger than that of the carbon-free control (SAC1), suggesting an increase in mesopore volume. The relatively low micropore volumes may result either from incomplete crystallisation or partial pore blockage. The hysteresis loops in BP1 and BP3 indicate the presence of both inter-crystalline voids and intra-crystalline slits. However, the latter feature has disappeared from the disaggregated laths of sample BP4 (h)).

  The caustic-leached samples (APL4, BPL1 and BPL2) were also characterised by nitrogen adsorption and the resulting isotherms are shown in (c). For comparison purposes the isotherm of leached sample SAC2 (SAC2L) is also included. (This sample was very similar to SAC1 but showed a reduced micropore volume: 80 cm

  the decomposition of TPA (in AP5 only, (b) and (d)).

  C) (a)

  3

  /g). In all cases there is a marked increase in meso- pore volume, with BP2 showing the largest effect. The micropore uptake of the carbon-modified samples was reduced, probably due to partial extraction of silicon from the lattice and structure degradation. However, the micro- pore uptake of the ‘‘blank’’ SAC2 was slightly increased, ^78.6% perhaps suggesting that the original difference from the ^{94.3% 95.8% 800 o C 250 o C 150 o C 25 o C 70 75 80 85 90 95 100 100 200 300 400 500}

  Time (min) Weight %

  Weight % _{100 200 300} ^{400 500 600 700 800 900} Temperature ( _o

  C) Temperature ( _o

  C) Temperature ( _o

  C) Temperature ( _o

  /g instead of 100 cm blockage by alkali-soluble amorphous material. This is confirmed by the XRD patterns of the two samples in which SAC2 shows only a slight overall reduction in crys- tallinity in comparison with SAC1 but where the intensities of the low angle lines around 7–8 (2h) (sensitive to intra- pore material) are reduced by 20%.

  Further analysis of sorption data will form the subject of a future publication.

  for HT1 and CS1 derives from the high external surface area (small crystallite size). The absorption peak at 3610 cm

  Volume Adsorbed (cm ³ /g STP) AP4L BP1L BP2L ₆₀ ^{160 140} _{120 80 100} ^{120 80 100 60 120 80 100}

  Volume Adsorbed (cm ³ /g STP) Volume Adsorbed (cm ³ /g STP)

  10 ^{20 30 40 50 60 70 80 390 380 370 360 350 340 330 320 310 300 290 280 270 260 250 240 230 220 210 200 190 180 170 160 150 140 130 120 110 90 100} _{0.2 0.4 0.6 0.8 1} Relative Pressure (P/P o ) Relative Pressure (P/P _o ) Relative Pressure (P/P _o )

   ~ ~ ~ ~ ~ ~ ₁₀ ^{20 30 40 50 60 70 80 390 380 370 360 350 340 330 320 310 300 290 280 270 260 250 240 230 220 210 200 190 180 170 160 150 140 130 120 110 90 100} _{0.2 0.4 0.6 0.8 1} ^{70 80 80} AP4 BP1 BP2 BP4 AP5 BP3 ^{110 90 140 120 100 120 70 100 120} ₁₀₀ ^{90 110} _{120 80 100} ~ ~ ~ ~ ~ ~ ~ ~ ~ ~ ~ ~

  1 ^{0.2 0.4 0.6 0.8 200 180 160 140 120 100 140 120 1 100 200 180 160 140 120 80 100} HT1 CS1 SAC1

  was found to have disappeared after several injections of pyridine which suggests that all the bridging acidic sites were accessible. Also, in SAC1 shows

  1

  1

  3.3.5. Acidity (FTIR spectroscopy) FTIR-pyridine was used to determine the true frame- the spectra of three samples (SAC1, HT1, and CS1) are shown in .

  ). The increased absorption at 3745 cm

  1

  ) and sila- nol groups (3745 cm

  1

  ) and the lowest concentration of extra-framework Al (3660 cm

  1

  Among the three samples, SAC1 has the highest concen- tration of bridging acid sites (3610 cm

  (c) (a) (b) ~ ~ ~ ~ ~ ~ _{140 120 80 100} SAC2L ¹⁸⁰

Fig. 6. Adsorption isotherms of (a) reference samples and CS1, (b) carbon-templated samples, (c) caustic-treated samples.

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87 acid sites (1540 cm

  1

  20 AP4 (50% carbon)

  Absorbance (b)

  SAC1 HT1 CS1 _{1600 1550 1500 1400 1450} Wavenumber (cm

• ^-1 )

  Absorbance (a)

  1 We thank Professor Thomas Bein for this suggestion. ^{4000 3900 3800 3700 3600 3500 3400 3300 3200 3000 3100} Wavenumber (cm ^-1 )

  89

  22

  28 BP2 (33% carbon + TPABr)

  17

  84 BP1 (33% carbon)

  21

  37 AP5 (50% carbon + TPABr)

  16

  19

  ). In other words, SAC1 (L/B = 0.2) synthesised under the dry gel system has fewer structural defects than HT1 (L/B = 0.5) and CS1 (L/B = 0.9) made under traditional hydrothermal conditions. details the Si/Al values for the measured samples, all of which are higher than expected (reaction mixture Si/Al = 15). It is notable that AP5 and BP2 with reagent quantities of TPA in the syntheses had much higher Si/Al values than the others. Such reaction compositions crystallise MFI products in the absence of added aluminium. The presence of stoichiometric TPA has thus excluded much of the gel aluminium from the crystalline product.

  44 SAC1 (no carbon)

  15

  23 CS1 (no carbon)

  11

  HT1 (no carbon)

  EDAX (bulk analysis) FTIR (Brønsted site)

  Table 3 Values of Si/Al for selected samples (the Si/Al in the reaction mixture was 15) Sample Si/Al

  The post-synthesis treatment (alkaline leaching) proba- bly dissolved amorphous material and generated more mesoporosity, but it also led to slightly reduced crystallin- ity and micropore volume. Sample BP2 suffered a more severe impact from alkaline leaching than either AP4 or BP1, which tends to suggest a more open structure, allow- ing the caustic solution to attack its framework easily. It is also possible that the relatively more effective leaching of

  : the nanoparticulate carbon may coat the reactant surfaces at the drying stage, thus reducing reactivity during the synthesis step.

  

  The bulk Si:Al ratio for a number of products was ana- lysed by EDAX and the result for each sample was very close to the value in the synthesis gel (Si/Al = 15). How- ever, values from FTIR acidity measurements were higher than expected. Hence, it can be concluded that, although the majority of the aluminium in the reaction precursor was present in the final product, reduced levels were incor- porated into the ZSM-5 framework. As the carbon content in the synthesis was increased, the framework aluminium decreased ). Even less incorporation of aluminium was observed in the preparations with additional TPABr as the reaction passed from an essentially inorganic to a TPA- templated synthesis. The influence of the carbon appears also to derive from a real chemical effect in which the progression of the crystallisation is retarded. Possibly, the nanosized carbon is acting in a manner similar to that of a polymeric growth inhibitor. Mass transfer limitations could also exert some control

  ZSM-5 catalysts have been successfully synthesised under various conditions using carbon-templating. In terms of heating method, the SAC procedure was found to result in fewer framework defects (FTIR) than conventional hydrothermal synthesis. High aluminium ZSM-5 with a large crystal size (6–10 lm) was obtained by the SAC method using a greatly-reduced proportion of organic tem- plate compared to the quantities used by Jacobsen . The addition of carbon retarded the crystallisation rate and modified the crystal morphology. It was found that BP4, containing the highest level of carbon (100 wt.% with duration (504 h) of BP3 (50 wt.%) to show comparable crystallinity. With the increasing carbon content in BP1 (33 wt.%), BP3 (50 wt.%), and BP4 (100 wt.%) the crystal morphology became increasingly fragmented, the crystals finally becoming transmuted into irregular lath-like frag- ments at the highest carbon loading. Hysteresis loops in the nitrogen adsorption–desorption isotherms indicate the presence of both inter- and intra-crystalline mesopores in the carbon-templated ZSM-5 materials. However, incom- plete crystallisation or partial blockage of micropores leads to relatively low micropore volumes in some products. Although two different carbon sources were used, their behaviour in the syntheses appeared to be very similar.

  4. Conclusions This work reports low-cost ZSM-5 syntheses with mes- opores incorporated into the product crystals. A series of

  SAC1 HT1 CS1

Fig. 7. FTIR spectra for SAC1, HT1, and CS1 at (a) high frequency (prior to the titration of pyridine), (b) low frequency (coordinated pyridine bands).

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87

  

Y.H. Chou et al. / Microporous and Mesoporous Materials 89 (2006) 78–87

[12] Y. Whang, Y. Tang, A. Dong, X. Wang, N. Ren, W. Shan, Z. Gao,

  BP2 was due to its more siliceous framework which facili- Adv. Mater. 14 (2002) 994. tated an enhanced attack by the caustic solution.

  [13] J. Sun, Z. Shan, T. Maschmeyer, J.A. Moulijn, M.O. Coppens, Chem.

  Commun. (2001) 2670.

  Acknowledgements

  [14] F.A. Topsoe, C.J.H. Jacobsen, M. Brorson, C. Madsen, F. Schmidt, U.S. Patent 6,241,960, 1999.

  The authors are indebted to the late Mr. R.J. Plaisted [15] J.C. Groen, L.A.A. Peffer, J.A. Moulijn, J. Perez-Ramirez, Micropor.

  Mesopor. Mater. 69 (2004) 29.

  for his experimental guidance and helpful discussions, [16] T. Suzuki, T. Okuhara, Micropor. Mesopor. Mater. 43 (2001) 83. and to Dr. Patrick Hill for his assistance in the operation [17] J.C. Groen, J. Perez-Ramirez, L.A.A. Peffer, Chem. Lett. (2002) 94. of the electron microscope.

  [18] M. Matsukata, N. Nishiyama, N. Ueyama, Micropor. Mater. 1 (1993) 219.

  References

  [19] M. Matsukata, N. Nishiyama, K. Ueyama, Micropor. Mater. 7 (1996) 109.

[1] A. Corma, Chem. Rev. 97 (1997) 2373. [20] M. Matsukata, M. Ogura, T. Osaki, P. Rao, M. Nomura, E. Kikuchi,

[2] S. van Donk, A.H. Janssen, J.H. Bitter, K.P. de Jong, Catal. Rev. 45 Top. Catal. 9 (1999) 77.

  (2003) 297.

  [21] M. Matsukata, M. Ogura, T. Osaki, E. Kikuchi, A. Mitra, Micropor. [3] M.W. Anderson, S.M. Holmes, N. Hanif, C.S. Cundy, Angew. Chem. Mesopor. Mater. 48 (2001) 23.

  Int. Ed. 39 (2000) 2707. [22] M. Matsukata, T. Osaki, M. Ogura, E. Kikuchi, Micropor. Mesopor. [4] A.H. Janssen, I. Schmidt, C.J.H. Jacobsen, A.J. Koster, K.P. de Jong, Mater. 56 (2002) 1.

  

Micropor. Mesopor. Mater. 65 (2003) 59. [23] P. Rao, K. Ueyama, M. Matsukata, Appl. Catal. A 166 (1998) 97.

[5] C. Madsen, C.J.H. Jacobsen, Chem. Commun. (1999) 673. [24] P. Rao, C. Leon, K. Ueyama, M. Matsukata, Micropor. Mesopor.

[6] I. Schmidt, C. Madsen, C.J.H. Jacobsen, Inorg. Chem. 39 (2000) Mater. 21 (1998) 305.

  2279.

  [25] H. Robson, K.P. Lillerud (Eds.), Verified Syntheses of Zeolitic [7] C.J.H. Jacobsen, C. Madsen, T.V.W. Janssens, H.J. Jakobsen, J. Materials, second ed., Elsevier, London, 2001, p. 198. Skibsted, Micropor. Mesopor. Mater. 39 (2000) 393. [26] C.S. Cundy, J.O. Forrest, R.J. Plaisted, Micropor. Mesopor. Mater. [8] C.J.H. Jacobsen, C. Madsen, J. Houzvicka, I. Schmidt, A. Carlsson, 66 (2003) 143.

  J. Am. Chem. Soc. 122 (2000) 7116. [27] A.E. Persson, B.J. Schoeman, J. Sterte, J.-E. Otterstedt, Zeolites 14 [9] I. Schmidt, A. Boisen, E. Gustavsson, K. Stahl, S. Pehrson, S. Dahl, (1994) 557.

A. Carlsson, C.J.H. Jacobsen, Chem. Mater. 13 (2001) 4416.

  [28] F. Thibault-Starzyk, B. Gil, S. Aiello, T. Chevreau, J.-P. Gilson, [10] M.E. Davis, Nature 417 (2002) 813. Micropor. Mesopor. Mater. 67 (2004) 107. [11] P. Yang, T. Deng, D. Zhao, P. Feng, D. Pine, B.F. Chmelka, G.M. [29] R.W. Grose, E.M. Flanigen, U.S. Pat. 4,257,885, 1981.

  Whitesides, G.D. Stucky, Science 282 (1998) 2244. [30] B.M. Lowe, J.R.D. Nee, J.L. Casci, Zeolites 14 (1994) 610.