Pembuatan Komposit Biodegradabel dari α-Selulosa Ampas Tebu Bz 132 (Saccharum officinarum) dan Polipropilena dengan Menggunakan Polipropilena Tergrafting Maleat Anhidrida dan Divinil Benzena Sebagai Agen Pengikat Silang

  PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α-SELULOSA AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING

  MALEAT ANHIDRIDA DAN DIVINIL BENZENA

SEBAGAI AGEN PENGIKAT SILANG

TESIS Oleh Tengku Rachmi Hidayani

  107006002/KIM FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SUMATERA UTARA

MEDAN

  2012 PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α-SELULOSA AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING

  MALEAT ANHIDRIDA DAN DIVINIL BENZENA

SEBAGAI AGEN PENGIKAT SILANG

TESIS Diajukan Sebagai Salah Satu Syarat Untuk Memperoleh Gelar Magister Sains Dalam Program Studi Ilmu Kimia Pada Fakultas Matematika Dan Ilmu Pengetahuan Alam Universitas Sumatera Utara Oleh Tengku Rachmi Hidayani 107006002/KIM FAKULTAS MATEMATIKA DAN ILMU PENGETAHUAN ALAM UNIVERSITAS SUMATERA UTARA

  

MEDAN

2012

  Judul Tesis : PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α-SELULOSA AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING MALEAT ANHIDRIDA DAN DIVINIL BENZENA SEBAGAI AGEN PENGIKAT SILANG Nama Mahasiswa : Tengku Rachmi Hidayani Nomor Pokok : 107006002 Program Studi : Magister Ilmu Kimia

Menyetujui

Komisi Pembimbing

  (Dr. Darwin Yunus Nasution, MS) (Dr.Yugia Muis, MS) Ketua Anggota Ketua Program Studi Dekan (Prof. Basuki Wirjosentono, MS, Ph.D) (Dr. Sutarman, MSc) Tanggal Lulus : 4 Mei 2012

  

PERNYATAAN ORISINALITAS

PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α-SELULOSA AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA

  DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING MALEAT ANHIDRIDA DAN DIVINIL BENZENA

SEBAGAI AGEN PENGIKAT SILANG

  TESIS Dengan ini saya menyatakan bahwa saya mengakui semua karya Tesis ini adalah hasil kerja saya sendiri kecuali kutipan dan ringkasan yang tiap satunya telah dijelaskan sumbernya dengan benar.

  Medan, 4 Mei 2012 Tengku Rachmi Hidayani NIM. 107006002

  

PERNYATAAN PERSETUJUAN PUBLIKASI KARYA ILMIAH

UNTUK KEPENTINGAN AKADEMIS

  Sebagai Sivitas Akademika Universitas Sumatera Utara, saya yang bertanda tangan di bawah ini: Nama : Tengku Rachmi Hidayani Nomor Pokok : 107006002 Program Studi : Magister Ilmu Kimia Jenis Karya Ilmiah : Tesis

  Demi pengembangan ilmu pengetahuan, menyetujui untuk memberikan kepada Universitas Sumatera Utara Hak Bebas Royalti Non-Eksklusif (Non-Exclusif Royalty

  Free Right) atas Tesis saya yang berjudul: PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α-SELULOSA AMPAS TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA

  DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING MALEAT ANHIDRIDA DAN DIVINIL BENZENA

SEBAGAI AGEN PENGIKAT SILANG

  beserta perangkat yang ada (jika diperlukan). Dengan Hak Bebas Royalti Non- Eksklusif ini, Universitas Sumatera Utara berhak menyimpan, mengalih media, memformat, mengelola dalam bentuk data-base, merawat dan mempublikasikan Tesis saya tanpa meminta izin dari saya selama tetap mencantumkan nama saya sebagai penulis dan sebagai pemegang dan atau sebagai pemilik hak cipta.

  Demikian pernyataan ini dibuat dengan sebenarnya.

  Medan, 4 Mei 2012 Tengku Rachmi Hidayani NIM. 107006002

  Telah diuji pada

Tanggal : 4 Mei 2012

PANITIA PENGUJI TESIS KETUA : Dr. Darwin Yunus Nasution, MS Anggota : 1. Dr. Yugia Muis, MS

   2. Prof. Basuki Wirjosentono, MS, Ph.D

   3. Dr. Hamonangan Nainggolan, MSc

   4. Prof. Dr. Thamrin, MSc

RIWAYAT HIDUP

  Penulis lahir di Medan,Sumatera Utara pada tanggal 15 Maret 1988, anak pertama dan terakhir dari Bapak H.T.Syahril SH dan Ibu Hj.Dra.Nurtizar,Apt. Penulis menimba ilmu di TK Perwanis Medan pada tahun 1992-1994. Melanjutkan pendidikan di SD Percobaan negeri Medan pada Tahun 1994-2000, SLTP Negeri I Medan pada tahun 2000-2003, dan di SMA Negeri I Medan pada tahun 2003-2006. Kemudian melanjutkan jenjang perkuliahan dengan menjadi mahasiswa Departemen Kimia Fakultas Matematika Universitas Sumater Utara pada tahun 2006-2010. Lalu melanjutkan kembali pendidikan pada program Magister Ilmu Kimia di Universitas Sumatera Utara 2010-2012.

KATA PENGANTAR

  Puji syukur atas limpahan rezeki dan Rahmat dari Allah SWT. Salawat dan salam untuk Rasulullah Muhammad SAW karena jika bukan karena-Nya,saya tidak akan mampu mengerjakan penelitian serta tesis ini dengan baik. Tesi s berjudul “PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α- SELULOSA AMPAS TEBU Bz 132 (Saccharum officinarum ) DAN POLIPROPILENA DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING MALEAT ANHIDRIDA DAN DIVINIL BENZENA SEBAGAI AGEN PENGIKAT SILANG” ini dibuat sebagai salah satu syarat mendapatkan gelar Magister Sains pada bidang ilmu Kimia Fakultas Matematika Dan Ilmu Pengetahuan Alam Universitas Sumatera Utara. Pada kesempatan ini penulis ingin memberikan penghargaan yang setinggi-tingginya serta mengucapkan terima kasih yang tidak terhingga kepada berbagai pihak yang terlibat secara langsung maupun tidak langsung dan telah memberikan dukungan baik moril maupun materil. Dengan segala kerendahan hati dan rasa hormat yang mendalam penulis ingin menyampaikan terima kasih yang tulus kepada:

  Orang tua tercinta, Ayahanda H.T.Syahril SH dan Ibunda Hj.Dra.Nurtizar,Apt yang selalu memberikan limpahan kasih sayang,ketulusan dan keikhlasan dalam mendidik dan membesarkan penulis. Memberikan semangat terbesar yang tidak ada henti-hentinya kepada penulis. Semoga mama dan papa selalu dalam lindungan Allah SWT.

  Bapak Prof. Dr. dr. Syahril Pasaribu, DMTH, MSc, CTM SpA (K) dan Dr. Sutarman, MSc selaku Rektor Universitas Sumatera Utara dan Dekan Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Sumatera Utara.

  Bapak Dr.Darwin Yunus Nst, MS selaku dosen pembimbing I dan Ibu Dr.Yugia Muis, MS selaku dosen Pembimbing II yang telah dengan sabar meluangkan waktu,tenaga dan pikirannya serta memberikan masukan, saran, dan petunjuk kepada penulis dalam melakukan penelitian dan penyusunan tesis ini.

  Bapak Prof. Basuki Wirjosentono, MS, Ph.D dan Dr. Hamonangan Nainggolan, MSc selaku ketua program studi dan sekretaris Pascasarjana Ilmu Kimia. Bapak/Ibu dosen Pascasarjana Ilmu Kimia yang telah membimbing dan memotivasi serta memberi disiplin ilmu selama penulis menjalani studi. Seluruh staf laboratorium Kimia Polimer dan Laboratorium Ilmu Dasar

  FMIPA USU, kak Ayu, serta seluruh adik-adik assisten kimia fisika dan kimia polimer, terima kasih atas bantuannya dalam penelitian.

  Kak Leli selaku tata usaha Pascasarjana Ilmu Kimia dan bang Edi teknisi Laboratorium Kimia Polimer FMIPA-USU. Kakak tempat berbagi suka dan duka selama di Program Magister. Teman-teman Pascasarjana Ilmu Kimia USU Stambuk 2010 semester ganjil (kak Mawar, kak Efi, Kak Sari, Kak Angel, Bang Mulia, Bang Irwan, Bang Ridwan) dan juga stambuk 2010 semester genap.

  Sahabat terbaik yang pernah penulis miliki, Rizki FitriYani,Reni Silvia Nasution,Widia Susanti. Sahabat lama yang tak pernah tergantikan : Uli, Kiki, Lia, Diah, Putri, Nanda, Ramadhani, Leila. Teman berbagi cerita dan melepas lelah : adik Dwi Ramadhani dan Wendy Syahfitri. Seluruh keluarga besar (sepupu,ponakan,om dan tante) yang selalu mendoakan yang terbaik kepada penulis. Seluruh teman-teman baik dari dunia maya,maupun dunia nyata yang tidak dapat disebutkan satu persatu. Semangat dari kalian semua sangat berharga.

  Hanya Allah yang dapat membalas segala kebaikan,ketulusan dan keikhlasan yang telah kalian berikan kepada penulis. Penulis berharap limpahan Rahmat Allah selalu mengalir untuk kita semua. Terima kasih.

  Penulis menyadari bahwa tesis ini tidak terlepas dari kekurangan. Oleh karena itu penulis mengharapkan kritik dan saran yang dapat membangun dan menyempurnakan skripsi ini agar lebih baik lagi.

  Akhirnya penulis berharap tesis ini memberikan manfaat bagi setiap pembaca maupun kemajuan penelitian dan ilmu pengetahuan yang akan datang.

  Medan, Mei 2012 Hormat Penulis

  Tengku Rachmi Hidayani PEMBUATAN KOMPOSIT BIODEGRADABEL DARI α-SELULOSA AMPAS

  TEBU Bz 132 (Saccharum officinarum) DAN POLIPROPILENA DENGAN MENGGUNAKAN POLIPROPILENA TERGRAFTING MALEAT ANHIDRIDA DAN DIVINIL BENZENA SEBAGAI AGEN PENGIKAT SILANG

  

ABSTRAK

  Telah dilakukan penelitian tentang penggunaan polipropilena tergrafting maleat anhidrida dan divinil benzene sebagai agen pengikat silang dalam pembuatan komposit biodegradabel dari

  α-selulosa yang bersumber dari ampas tebu dan polipropilena. Penelitian ini terdiri dari tiga tahapan. Tahap pertama yaitu pembuatan PP-g-MA dari polipropilena murni. Tahap kedua yaitu pemisahan

  α-selulosa dari ampas tebu yang dilakukan dengan metode Okhamafe. Tahapan yang terakhir adalah pencampuran antara polipropilena dan

  α-selulosa dari ampas tebu dengan agen pengikat silang dengan berbagai variasi massa. Proses pembuatan PP-g-MA dilakukan dengan mendegradasi polipropilena terlebih dahulu dengan BPO dalam internal mixer dengan perbandingan 90:10 (%berat/berat). Kemudian digrafting dengan maleat anhidrida dengan perbandingan PPd:MA:BPO 92:6:2 (%berat/berat). Hasil PP-g-Ma yang diperoleh dimurnikan dengan cara direfluks dengan pelarut xilena. Proses pemisahan

  α-selulosa dilakukan dengan metode Okhamafe yaitu dilakukan dengan perendaman dalam asam HNO 3,5%, pemutihan dengan Natrium Hipoklorit 1,75% dan pemurnian dengan NaOH 17,5%. Proses pencampuran

  α- selulosa dengan polipropilena dan agen pengikat silangnya dilakukan dengan metode

  o

  kempa tekan pada suhu 160

  C. Variasi komposisi dan massa dalam pembentukan komposit biodegradabel adalah PP: α-Selulosa (95:5), PP:α-Selulosa:PP-g-MA

  (95:5:1), PP: (95:5:1:1), PP: α-Selulosa:PP-g-MA:BPO α-Selulosa:PP-g-

  MA:BPO:DVB (95:5:1:1:1), PP: α-Selulosa:PP-g-MA:BPO:DVB (95:5:0,5:0,5:1), dan PP:

  α-Selulosa:BPO:DVB (95:5:1:1). Karakterisasi hasil komposit yang diperoleh dianalisa gugus fungsi dengan uji FTIR, analisa sifat morfologi dengan uji SEM, analisa sifat thermal dengan uji DTA, analisa sifat mekanis dengan uji tarik, analisa ketahanan terhadap air dengan uji daya serap air dan analisa kemampuannya terurai di alam dengan uji biodegradabel. Hasil penelitian menunjukan bahwa komposit biodegradabel yang memiliki sifat terbaik dan sesuai dengan SNI 7188.7:2011 adalah dengan perbandingan PP:

  α-Selulosa:PP-g-MA:BPO:DVB (95:5:0,5:0,5:1) dengan

  2

  nilai tegangan hasil uji tarik yaitu 50,031N/m , daya serap air yang rendah yaitu 0,791%, hasil foto permukaan yang rata dan interaksi gugus yang kuat serta memiliki sifat biodegradabel yang baik.

  Kata kunci: α-Cellulose; Packaging; Composite Polymer; Biodegradable

  ABSTRACT PREPARATION OF COMPOSITE BIODEGRADABLE FROM BAGGASE α-

CELLULOSE Bz 132 (Saccharum officinarum) AND POLYPROPYLENE

  

USING POLYPROPYLENE GRAFTED MALEIC ANHYDRADE

AND DIVINIL BENZENE AS CROSSLINKING AGENTS

Research about use of polypropylene grafted maleic anhydride and divinyl benzene as a crosslinking agent in the manufacture of composite biodegradable and

α-cellulose from bagasse and polypropylene. The study consisted of three stages. The

first stage of the manufacture of PP-g-MA of pure polypropylene. The second stage of the separation of α-cellulose from bagasse is performed by the Okhamafe methode.

The last stage of the mixing between the polypropylene and α-cellulose from bagasse

by crosslinking with various binding agents of mass variation. The process of making PP-g-MA polypropylene degrades done by BPO in advance in an internal mixer with

a ratio of 90:10 (% w / w). Then PPd grafted with maleic anhydride in the ratio PPd

: MA: BPO 92:6:2 (% w / w). The results of PP-g-ma obtained was purified by solvent refluxed with xylene. α-cellulose separation process performed by the Okhamafe methode that is done by immersion in 3.5% HNO 3 acid, bleaching with sodium hypochlorite 1

  .75% and 17.5%, purification with NaOH. Α-mixing process

with polypropylene and cellulose binding agents is done by cross-clamp method at a

temperature of 150 C press. Variations in composition and mass of the formation of

polymer composites is a PP: α-Cellulose (95:5), PP: α-Cellulose: PP-g-MA (95:5:1),

PP:α-Cellulose:PP-g-MA:BPO (95:5:1:1), PP:α-Cellulose:PP-g-MA: BPO:DVB

(95:5:1:1:1), PP:α-Cellulose:PP-g-MA:BPO:DVB (95:5:0,5:0,5:1), PP:α- Cellulose:BPO:DVB (95:5:1:1).

Characterization of the composites obtained were analyzed with a functional group

FTIR testing, analysis of morphology by SEM, analysis of thermal properties by DTA

test, analysis of mechanical properties with tensile stress test, analysis of resistance

to water with a water absorption test and analysis of its ability to decompose in

nature to the test biodegradable.

The results showed that the polymer composite that has the best properties and in

accordance with ISO 7188.7:2011 is the ratio of PP:

  α-Cellulose: PP-g-MA: BPO:

DVB (95:5:0,5:0,5:1) with the test results of tensile stress is 50.031 N/m2, low water

absorption, namely 0.791%, the images on a flat surface and a strong group

. interactions as well as having good biodegradable properties

   : Keywords

α-Cellulose; Packaging; Composite Polymer; Biodegradable

DAFTAR ISI KATA PENGANTAR

  i ABSTRAK iv

  ABSTRACT v DAFTAR ISI vi DAFTAR TABEL x DAFTAR GAMBAR xi DAFTAR LAMPIRAN xiii DAFTAR SINGKATAN xiv

BAB 1 PENDAHULUAN

  1

  2.1.2 Komposit biodegradabel dengan bahan dasar selulosa

  1

  13

  2.3.2 Ampas Tebu

  12

  2.3.1 Botani Tebu (Saccharum Officinarum)

  12

  2.3 Tebu

  10

  2.2.2 Kemasan Biodegradabel

  10

  2.2.1 Fungsi kemasan

  9

  2.2 Kemasan

  8

  8

  1.2 Permasalahan

  5

  4

  1.3 Pembatasan Masalah

  4

  1.4. Tujuan Pelitian

  4

  1.5 Manfaat Penelitian

  1.6 Lokasi Penelitian

  2.1.1 Biokomposit

  5

  1.7 Metodologi Penelitian

  5 BAB 2 TINJAUAN PUSTAKA

  7

  2.1 Komposit

  1.1 Latar Belakang

  7

  2.4 Selulosa

  3.2.1 Proses Degradasi Polipropilena dengan Benzoil Peroksida

  29

  2.8.6 Analisa Kemampuan Terurai dialam dengan uji biodegradabel

  30 Reaksi Penelitian

  34 BAB 3 METODE PENELITIAN

  37

  3.1 Alat dan Bahan

  37

  3.1.1 Alat

  37

  3.1.2 Bahan

  37

  3.2 Prosedur Penelitian

  38

  38

  29

  3.2.2 Proses Grafting MA kedalam PP Terdegradasi

  38

  3.2.3 Pemurnian PP-g-MA

  39

  3.2.4 Preparasi Pembentukan Serbuk Polipropilena

  39

  3.2.5 Preparasi Serbuk Ampas Tebu

  39

  3.2.6 Ekstraksi α-Selulosa Dari Serbuk Ampas Tebu

  39

  3.2.7 Pembentukan komposit biodegradabel PP Murni dan

  40 α-Selulosa

  3.2.8 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa 40

  2.8.5 Analisa Ketahanannya Terhadap Air dengan Uji serapan air

  2.8.4 Analisa Sifat Mekanik dengan uji kekuatan tarik dan kemulura

  14

  20

  2.4.1 Sifat-Sifat Selulosa

  14

  2.4.2 Pembagian Selulosa

  16

  2.4.3 α-Selulosa

  16

  2.4.4 Selulosa dari serat alam

  17

  2.4.5 Metode Pemisahan Selulosa

  18

  2.5 Polipropilena

  19

  2.5.1 Struktur Polipropilena

  2.5.2 Pembentukan Radikal Bebas Pada Bahan Polimer

  28

  21

  2.5.2.1 Radikal Bebas pada Polimerisasi

  21

  2.6 Degradasi dengan Inisiator Peroksida

  23

  2.7 Proses Grafting

  23

  2.8 Karakterisasi Komposit Biodegradabel

  24

  2.8.1 Analisa Sifat Thermal Komposit Biodegradabel

  25

  2.8.2 Spektofotometer FT-IR

  27

  2.8.3 Analisa Sifat Permukaan dengan Pengujian SEM

  Dan PP-g-MA

  3.2.9 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 41

  PP-g-MA, BPO dan DVB

  47

  3.3.6 Ekstraksi α-Selulosa Dari Serbuk Ampas Tebu

  48

  3.3.7 Pembentukan komposit biodegradabel PP Murni dan

  49 α-Selulosa

  3.3.8 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa 49 dan PP-g-MA

  3.3.9 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 50

  PP-g-MA dan BPO

  3.3.10 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 50

  BPO dan DVB

  3.3.11 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 51

  3.3.12 Uji Serap Air

  47

  51

  3.3.13 Uji Biodegradabel

  52 BAB 4 HASIL DAN PEMBAHASAN

  53

  4.1 Karakterisasi Berdasarkan Analisa Sifat Mekanik dengan Uji Traik

  53

  4.2 Analisa Sifat Thermal dengan Uji DTA

  55

  4.3 Analisa Sifat Morfologi dengan Uji SEM

  57

  4.4 Analisa Ketahanannya Terhadap Air dengan Uji Serapan Air

  3.3.5 Preparasi Serbuk Ampas Tebu

  3.3.4 Preparasi Pembentukan Serbuk Polipropilena

  PP-g-MA dan BPO

  42

  3.2.10 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 41

  BPO dan DVB

  3.2.11 Pembentukan Komposit biodegradabel PP Murni, α-Selulosa, 41

  PP-g-MA, BPO dan DVB

  3.2.12 Karakterisasi Komposit Biodegradabel

  42

  3.2.12.1 Analisa Gugus Fungsi Dengan FTIR

  42

  3.2.12.2 Analisa Sifat Thermal dengan Uji DTA

  42

  3.2.12.3 Analisa Sifat Mekanik dengan Uji Tarik

  3.2.12.4 Analisa Sifat Morfologi dengan uji SEM

  46

  43

  3.2.12.5 Analisa Sifat Ketahanan Terhadap Air dengan

  43 Uji Serap Air

  3.2.12.6 Analisa Kemampuan Terurai di Alam dengan

  44 Uji Biodegradabel

  3.3 Bagan Penelitian

  44

  3.3.1 Proses Degradasi Polipropilena dengan Benzoil Peroksida

  44

  3.3.2 Proses Grafting MA kedalam PP Terdegradasi

  45

  3.3.3 Pemurnian PP-g-MA

  60

  4.5 Analisa Gugus Fungsi dengan Uji FTIR

  61

  4.5.1 Komposit biodegradabel PP:

  64 α-Selulosa:PP-g-MA (95:5:1)

  4.5.2 Komposit biodegradabel PP: α-Selulosa:BPO:DVB (95:5:1:1) 64

  4.5.3 Komposit biodegradabel PP: α-Selulosa:PP-g-MA:BPO:DVB 64

  (95:5:0,5:0,5:1)

  4.6 Analisa Kemampuan Terurai di Alam dengan Uji Biodegradasi

  65 BAB 5 KESIMPULAN DAN SARAN

  71

  5.1 Kesimpulan

  71

  5.2 Saran

  72 DAFTAR PUSTAKA

  73 LAMPIRAN

  77

  

DAFTAR TABEL

  Nomor Judul Halaman

  2.1 Persyaratan Kemasan Biodegradabel menurut SNI 7188.7:2011

  11

  2.2 Komposisi Kimia Ampas Tebu

  13

  3.1 Perbandingan Pembentukan Komposit Biodegradabel PP murni,

  42 α-selulosa, PP-g-MA, BPO dan DVB

  4.1 Hasil Perhitungan Kekuatan Tarik dan kemuluran Komposit

  53 Biodegradabel

  4.2 Hasil Uji DTA Polipropilena Murni dan Komposit Biodegradabel

  56

  4.3 Data Hasil Uji Serapan Air

  61

  4.4 Bilangan Gelombang Polipropilena Murni

  62

  4.5 Bilangan Gelombang PP:

  62 α-selulosa:PP-g-MA (95:5:1)

  4.6 Bilangan Gelombang PP:

  63 α-selulosa:BPO:DVB (95:5:1:1)

  4.7 Bilangan Gelombang PP:

  63 α-selulosa:

  PP-g-MA:BPO:DVB (95:5:0,5:0,5:1)

  4.8 Data Hasil Penurunan Massa (%) Spesimen Komposit Biodegradebel

  65 setelah Penguburan dalam Tanah

  4.9 Bilangan Gelombang PP:

  66 α-selulosa:PP-g-MA (95:5:1) setelah Penguburan

  4.10 Bilangan Gelombang PP:

  67 α-selulosa:BPO:DVB (95:5:1:1) setelah Penguburan

  4.11 Bilangan Gelombang PP:

  67 α-selulosa:

  PP-g-MA:BPO:DVB (95:5:0,5:0,5:1) setelah Penguburan

  DAFTAR GAMBAR

  Nomor Judul Halaman

  2.1 Rumus Bangun Selulosa

  15

  2.2 Struktur Polipropilena

  19

  2.3 Polipropilena Isotatik, Sindiotaktik, Ataktik

  21

  2.4 Grafik (b) hasil dari set up yang diperlihatkan pada gambar

  27 (a), Grafik (d) merupakan jejak DTA yang umum yang merupakan dari pengaturan yang diperlihatkan pada Gambar (c)

  2.5 Reaksi Penelitian

  36

  3.1 Spesimen Uji Kekuatan Tarik Berdasarkan ASTM D-638-72 TypeIV

  42

  3.2 Proses Degradasi Polipropilena dengan Benzoil Peroksida

  44

  3.3 Proses Grafting Maleat Anhidrida kedalam Polipropilena Terdegradasi

  45

  3.4 Pemurnian Polipropilena Tergrafting Maleat Anhidrida

  46

  3.5 Preparasi Pembentukan Serbuk Polipropilena

  47

  3.6 Preparasi Serbuk Ampas Tebu

  47

  3.7 Ekstraksi

  48 α-Selulosa Dari Serbuk Ampas Tebu

  3.8 Pembentukan Komposit biodegradabel Polipropilena Murni

  49 dan α-Selulosa

  3.9 Pembentukan Komposit biodegradabel Polipropilena Murni,

  49 α-Selulosa, dan PP-g-MA

  3.10 Pembentukan Komposit biodegradabel PP murni,

  50 α-Selulosa,

  PP-g-MA, dan BPO

  3.11 Pembentukan Komposit biodegradabel PP murni,

  50 α-Selulosa, BPO, dan DVB

  3.12 Pembentukan Komposit biodegradabel PP murni, PP-g-MA, BPO,

  51 DVB, dan α-Selulosa

  3.13 Uji Serapan Air

  51

  3.14 Uji Biodegradabel

  4.5 Hasil Uji Komposit biodegradabel PP: α-Selulosa: BPO:DVB (95:5:1:1) 59

  4.10 Permukaan Komposit biodegradabel PP: α-Selulosa:

  4.9 Permukaan Komposit biodegradabel PP: α-selulosa:BPO:DVB (95:5:1:1) 70

  69

  4.8 Permukaan Komposit biodegradabel PP: α-Selulosa:PP-g-MA (95:5:1)

  69

  4.7 Mekanisme Reaksi Penguraian di Alam

  60 PP-g-MA:BPO:DVB (95:5:0,5:0,5:1) Pembesaran 1000 kali

  4.6 Hasil Uji Komposit biodegradabel PP: α-Selulosa:

  Pembesaran 1000 kali

  58

  52

  4.4 Hasil Uji PP: α-Selulosa:PP-g-MA (95:5:1) Pembesaran 1000 kali

  57

  4.3 Hasil Uji SEM dari Polipropilen Murni Pembesaran 1000 kali

  54

  4.2 Grafik Kemuluran (%) Dari Komposit Biodegradabel

  54

  ) dari Komposit Biodegradabel

  2

  4.1 Grafik Kekuatan Tarik (N/m

  70 PP-g-MA:BPO:DVB (95:5:0,5:0,5:1)