ISO Standards Related to
23.4.2 ISO Standards Related to
• SP0188-2007: Discontinuity (Holi-
Protective Coatings
day) Testing of New Protective Coat- ings on Conductive Substrates
• ISO 2409:1992 , Paints and varnishes
— Cross-cut test
• SP0298-2007: Sheet Rubber Lini n gs
for Abrasion and Corrosion Service • ISO 2431:1993 , Paints and varnishes
— Determination of flow time by use of
• SP0487-2007: Considerations in the
flow cups (Corr.2:1999)
Selection and Evaluation of Rust Pre- • ISO 2808:2007 , Paints and varnishes ventives and Vapor Corrosion Inhibi-
— Determination of film thickness
tors for Interim (Temporary) Corrosion Protection
• ISO 3668:1998 , Paints and varnishes
— Visual comparison of the color of
• SP0490-2007: Holiday Detection of
paints
Fusion-Bonded Epoxy External Pipe- line Coatings of 250 to 760 m (10 to
• ISO 4617:2000 , Paints and varnishes
30 mils)
— List of equivalent terms (withdrawn)
• SP0892-2007: Linings over Con- • ISO 4618:2006 , Paints and varnishes crete for Immersion Service
— Terms and definitions
• SSPC-PA2: Measurement of Dry • ISO 4624:2002 , Paints and varnishes Coating Thickness with Magnetic — Pull-off test for adhesion
Gauges • ISO 4628, Paints and varnishes —
• TM0102-2002: Measurement of Pro-
Evaluation of degradation of coatings —
Designation of quantity and size of
tective Coating Electrical Conduc-
defects, and of intensity of uniform
tance on Underground Pipelines
changes in appearance
• TM0104-2004: Offshore Platform — ISO 4628-1:2003 , Part 1: Ballast Water Tank Coating System
General introduction and desig-
Evaluation
nation system
• TM0174-2002: Laboratory Methods — ISO 4628-2:2003 , Part 2: for the Evaluation of Protective Coat-
Assessment of degree of blister-
ings and Lining Materials in Immer-
ing
sion Service — ISO 4628-3:2003 , Part 3:
23-6 Standards
Assessment of degree of rusting • ISO 8502, Preparation of steel substrates
— ISO 4628-4:2003 , Part 4:
before application of paints and related Assessment of degree of crack-
products — Tests for the assessment of ing
surface cleanliness
— ISO 4628-5:2003 , Part 5:
— ISO/TR 8502-1:1991 ,
Assessment of degree of flaking (Withdrawn Standard) Part 1:
— ISO 4628-6:200 7, Part 6:
Field test for soluble iron corro- Rating of degree of chalking by
sion products tape method
— ISO 8502-2:2005 , Part 2: — ISO 4628-7:2003 , Part 7:
Laboratory determination of Assessment of degree of chalk-
chloride on cleaned surfaces ing by velvet method
— ISO 8502-3:1992 , Part 3: — ISO 4628-8:2005 , Part 8:
Assessment of dust on steel sur- Assessment of degree of delami-
faces prepared for painting nation and corrosion around a
(pressure-sensitive tape method) scribe
— ISO 8502-4:1993 , Part 4: — ISO 4628-10:2003 , Part 10:
Guidance on the estimation of Assessment of degree of filiform
the probability of condensation corrosion
prior to paint application • ISO 8501, Preparation of steel substrates
— ISO 8502-5:1998 , Part 5:
before application of paints and related Measurement of chloride on products — Visual assessment of surface
steel surfaces prepared for cleanliness
painting (ion detection tube method)
— ISO 8501-1:2007 , Part 1: — ISO 8502-6:2006 , Part 6:
Rust grades and preparation Extraction of soluble contami- grades of uncoated steel sub- nants for analysis — The Bresle strates and of steel substrates
method
after overall removal of previ-
ISO 8502-8:2001 , Part 8: Field method for the refracto-
ous coatings
— ISO 8501-2:1994 , Part 2:
metric determination of mois- Representative photographic
ture
examples of the change of
, Part 9: appearance imparted to steel
ISO 8502-9:1998
when blast-cleaned with differ- Field method for the conducto- ent abrasives
metric determination of water- soluble salts
— ISO 8501-3:2006 , Part 3:
ISO 8502-10:1999 , Part 10:
Preparation grades of welds, cut
edges and other areas with sur- Field method for the titrimetric face imperfections
determination of water-soluble chloride
— ISO 8501-4:2006 , Part 4:
ISO 8502-11:2006 , Part 11:
Initial surface conditions, prep-
aration grades and flash rust Field method for the turbidimet- grades in connection with high-
ric determination of water-solu- pressure water jetting
ble sulfate
— ISO 8502-12:2003 , Part 12:
Field method for the titrimetric
Standards 23-7
determination of water-soluble
— ISO 11124-1:1993 , Part 1:
ferrous ions General introduction and classi- • ISO 8503, Preparation of steel substrates
fication
before application of paints and related
— ISO 11124-2:1993 , Part 2:
products — Surface roughness character- Chilled-iron grit istics of blast-cleaned steel substrates
— ISO 11124-3:1993 , Part 3:
ISO 8503-1:1988 High-carbon cast-steel shot and
, Part 1:
grit
Specifications and definitions for ISO surface profile compar-
— ISO 11124-4:1993 , Part 4:
ators for the assessment of abra- Low-carbon cast-steel shot sive blast-cleaned surfaces
• ISO 11125, Preparation of steel substrates
— ISO 8503-2:1988 , Part 2:
before application of paints and related Method for the grading of sur-
products — Test methods for metallic face profile of abrasive blast-
blast-cleaning abrasives cleaned steel — Comparator
— ISO 11125-1:1993 , Part 1:
procedure
Sampling
— ISO 8503-3:1988 , Part 3: — ISO 11125-2:1993 , Part 2:
Method for the calibration of Determination of particle size ISO surface profile comparators distribution and for the determination of sur-
— ISO 11125-3:1993 , Part 3:
face profile — Focusing micro- scope procedure
Determination of hardness
— ISO 8503-4:1988 , Part 4: — ISO 11125-4:1993 , Part 4:
Method for the calibration of Determination of apparent den- ISO surface profile comparators
sity
and for the determination of sur-
— ISO 11125-5:1993 , Part 5:
face profile — Stylus instrument Determination of percentage procedure
defective particles and of micro-
— ISO 8503-5:2003 , Part 5:
structure
Replica tape method for the
— ISO 11125-6:1993 , Part 6:
determination of the surface Determination of foreign matter profile
— ISO 11125-7:1993 , Part 7:
Determination of moisture • ISO 8504, Preparation of steel substrates
before application of paints and related • ISO 11126, Preparation of steel substrates products — Surface preparation methods
before application of paints and related products — Specifications for non-metal-
— ISO 8504-1:2000 , Part 1:
lic blast-cleaning abrasives General principles
— ISO 8504-2:2000 , Part 2: — ISO 11126-1:1993 , Part 1:
Abrasive blast-cleaning General introduction and classi-
— ISO 8504-3:1993 , Part 3:
fication (Corr. 2: 1997) Hand- and power-tool cleaning
— ISO 11126-3:1993 , Part 3:
Copper refinery slag • ISO 11124, Preparation of steel substrates
— ISO 11126-4:1993 , Part 4:
before application of paints and related Coal furnace slag products — Specifications for metallic
— ISO 11126-5:1993 , Part 5:
blast-cleaning abrasives
23-8 Standards
Nickel refinery slag Design considerations
— ISO 11126-6:1993 , Part 6: — ISO 12944-4:1998 , Part 4:
Iron furnace slag Types of surface and surface
— ISO 11126-7:1995 , Part 7:
preparation Fused aluminum oxide
— ISO 12944-5:2007 , Part 5:
(Corr.1:1999) Protective paint systems
— ISO 11126-8:1993 , Part 8: — ISO 12944-6:1998 , Part 6:
Olivine sand Laboratory performance test
— ISO 11126-9:1999 , Part 9:
methods
— ISO 12944-7:1998 , Part 7: — ISO 11126-10:2000 , Part
Staurolite
Execution and supervision of 10: Almandite garnet
paint work
, Part 8: • ISO 11127, Preparation of steel substrates
ISO 12944-8:1998
before application of paints and related Development of specifications products — Test methods for non-metal-
for new work and maintenance lic blast-cleaning abrasives
• ISO/TR 15235:2001 , Preparation of — ISO 1127-1:1993 , Part 1:
steel substrates before application of Sampling
paints and related products — Collected information on the effect of levels of
— ISO 11127-2:1993 , Part 2:
water-soluble salt contamination Determination of particle size
• ISO 15741:2001 , Paints and var- — ISO 11127-3:1993 , Part 3:
distribution
nishes -- Friction-reduction coatings for Determination of apparent den-
the interior of on- and offshore steel pipe- sity
lines for non-corrosive gases
— ISO 11127-4:1993 , Part 4:
• ISO 16276, Corrosion protection of steel Assessment of hardness by a
structures by protective paint systems — glass slide test
Assessment of, and acceptance criteria
— ISO 11127-5:1993 , Part 5:
for, the adhesion/cohesion (fracture Determination of moisture
strength) of a coating
— ISO 11127-6:1993 , Part 6: — ISO 16276-1:2007 , Part 1:
Determination of water-soluble Pull-off testing contaminants by conductivity
— ISO 16276-2:2007 , Part 2:
measurement Cross-cut testing and X-cut test-
— ISO 11127-7:1993 , Part 7:
ing
Determination of water-soluble chlorides
• ISO 19840:2004 , Paints and varnishes
— Corrosion protection of steel structures • ISO 12944, Paints and varnishes — by protective paint systems — Measure- Corrosion protection of steel structures by ment of, and acceptance criteria for, the protective paint systems thickness of dry films on rough surfaces
— ISO 12944-1:1998 , Part 1: • ISO 20340:2009 , Paints and varnishes
General introduction — Performance requirements for protec-
— ISO 12944-2:1998 , Part 2:
tive paint systems for offshore and related Classification of environments
structures
— ISO 12944-3:1998 , Part 3:
Standards 23-9
• ISO 14877:2002 , Protective clothing between Australia and New Zealand for new
for abrasive blasting operations using
projects commenced after July 1992.
granular abrasives
In the following table are joint standards
23.4.3 Australia/New Zealand
(except for Part 10) which form part of a
Standards
series of product standards for industrial Standards prepared by the Joint Australia/
paints referred to in AS/NZS 2312: New Zealand Standards (AS/NZS) Commit-
tee, CH/3 on Paints and Related Materials are listed below. These are issued under the terms of the Active Cooperation Agreement
Table 1: Joint Standards
AS/NZS 3750 Paints for steel structures Supersedes PRN
Part 0: Introduction and list of Stan-
Part 1: Epoxy mastic (two-pack) for
AS3750.1-1994 C32
rusted steel
AS3750.2-1994 C34 3750.3:2008
Part 2: Ultra high-build paint
Part 3: Heat resisting, Exterior
3750.3:1994 C27, C28, C31,
C35 3750.4:1994
C22 3750.5:2008
Part 4: Bitumen paint
3750.5 1994 C33 3750.6:2009
Part 5: Acrylic full gloss (two pack)
Part 6: Full gloss polyurethane
AS 2692-1983 C26,
C28 3750.7:2009
(two pack)
Part 7: Aluminum paint
Part 8: Vinyl paints – Primer, high
AS 3886-1991 C16
build and gloss
C2 AS 3750.10:2008 Part 10: Full gloss epoxy (two pack)
Part 9: Organic zinc-rich primer
AS 2204-1978
3750.10:1994 C24 3750.11:2009
Part 11: Chlorinated rubber, high
AS 2672-1983 C14,
C25 3750.12:1996
build and gloss
Part 12: Alkyd/micaceous iron oxide AS 2673-1983 C17
23-10 Standards
Table 1: Joint Standards
C6 3750.14:1997
Part 13: Epoxy primer (two pack)
AS 2674-1983
Part 14: High build epoxy (two pack) AS 2364-1990 C13 3750.15:1998
C1 3750.16:1998
Part 15: Inorganic zinc silicate paint
AS 2105-1992
Part 16: Waterborne primer and paint AS 3885-1991 C11
for galvanized, zinc/aluminum alloy coated and zinc primed steel
Part 17: Etch primers
AS 3884-1991 C10
(single pack and two pack)
AS 3750.18:2002 Part 18: Moisture cure urethane (sin-
gle-pack) systems
3750.19:2008 Part 19: Metal primer – General pur- AS 4089-1993 C4 &
C5 3750.20:2008
pose
Part 20: Anticorrosive metal primer – AS 4025.4-1994 Solvent borne – Lead and chromate free
AS 4025.2-1993 3750.22:2008
Part 21: Undercoat – Solvent borne
Part 22: Full gloss enamel – Solvent
AS 4025.1-1993 C20
borne
3750.23:2008 Part 23: Semi-gloss enamel – Solvent AS 4025.3-1993 borne
(Note: Paint Reference Number (PRN) used
— 3894.2-2002, Method 2: Non-
is AS/NZS 2312)
conductive coatings – Continu- ity testing – Wet sponge method
The following standards have been devel-
— 3894.3-2002, Method 3: Deter-
oped for use by coatings inspectors and may mination of dry film thickness
— 3894.4-2002, Method 4:
be referenced in technical specifications for
Assessment of degree of cure
protective coating contracts.
— 3894.5-2002, Method 5: Deter- mination of surface profile
• AS 3894, Site testing of protective coat- — 3894.6-2002, Method 6: Deter- ings
mination of residual contami- — 3894.0-2002, Introduction and
nants:
list of test methods • Method A: Chlorides — 3894.1-2002, Method 1: Non-
• Method B: Oil or water drop- conductive coatings – Continu-
lets
ity testing – High voltage (brush • Method C: Surface dust
Standards 23-11
iron • AS 1940-2004 (Amdt.2 2006) The storage • Method E: Mill scale
and handling of flammable and combusti- — 3894.7-2002, Method 7: Deter-
ble liquids)
mination of surface temperature • AS/NZS 2310:2002 Glossary of paint and — 3894.8-2002, Method 8: Visual
painting terms (Under revision as determination of gloss
DR07334)
— 3894.9:2003, Method 9: Deter- mination of adhesion
• AS/NZS 2311:2009 Guide to the painting — 3894.10-2002, Method 10:
of buildings
Inspection report – Daily surface • AS/NZS 2312:2002 (Amdt.1-2004)Guide and ambient conditions
to the protection of structural steel against — 3894.11-2002, Method 11:
atmospheric corrosion by the use of pro- Equipment report
tective coatings
— 3894.12-2002, Method 12: • AS 700-1996 Colour standards for general Inspection report – Coating
purposes
— 3894.13-2002, Method 13: Inspection report – Daily (blast
• AS/NZS 4114:2003 Spray painting and paint)
booths:
— 3894.14-2002, Method 14: — Part 1: Design, construction and Inspection report – Daily paint-
testing
ing — Part 2: Installation and mainte-
Other coating related Standards include:
nance
• AS 1627 Metal finishing-Preparation and • AS/NZS 4233:1999 High pressure water pretreatment of surfaces (under review):
(hydro) jetting systems: — 1627.0-1997 Method selection
— Part 1: Guidelines for safe oper- guide
ation and maintenance — 1627.1-2003 Cleaning using liq-
— Part 2: Construction and perfor- uid solvents and alkaline solu-
mance
tions • AS 4361 Guide to lead paint management: — 1627.2-2002 Power tool clean-
ing — Part.1: 1995 Industrial applica- — 1627.3-1988 Flame descaling
tions
(withdrawn in 2002) — Part.2: 1998 Residential and — 1627.4-2005 Abrasive blast
commercial buildings cleaning
Other common standards for coatings
— 1627.5-2003 Pickling, descal-
inspection work may also come from
ing and oxide removal
ASTM, ANSI, SSPC and other prominent
— 1627.6-2003 Chemical conver-
organizations. These standards can be
sion treatment of metals — 1627.9-2002 Pictorial surface
obtained by or all of the following ways:
preparation standards for paint- • Purchase via website ing steel surfaces (ISO 8501-1)
• Purchase by phone
• DR 00083-2001 The storage and handling
• Purchase by mail
of flammable paints and paint related material (terminated in 2000. Instead refer
Regardless of the specified standard, the job
to:
of the coatings inspector remains the same;
23-12 Standards
obtain, read, understand and verify per the specification.