f. Komposisi SKJ 5
Beban sampel = 46,05 kgf
Tebal sampel = 3 mm
Lebar sampel = 15 mm
Sehingga : Luas A = b x d
= 15 mm x 3 mm = 45 mm
2
Loadbeban P = 46,05 x 9,8 ms
2
= 451,29 N
σ =
= 10,02 MPa
5 Menghitung Kekuatan Lentur Sampel Komposit SKJE
Kekuatan lentur dihitung dengan menggunakan persamaan berikut :
UFS =
Dimana : P = Load atau beban N
L = Jarak Span 10 cm = 0,1 m b = Lebar sampel mm
h = Tebal sampel mm
a. Komposisi SKJ 0
Load beban = 2,63 kgf Lebar sampel = 15 mm
Tebal sampel = 3 mm
Universitas Sumatera Utara
Jarak Span = 0,1 m
Sehingga : Load beban P
= 2,63 kgf = 2,63 kgf x 9,8 ms
2
= 25,77 N 3PL
= 3 x 25,77 N x 0,1 m = 7,73 Nm
2bh
2
= 2 x 15 mm 3 mm
2
= 270 mm
3
= 0,27 x 10
-6
m
3
UFS = =
=
28,62 MPa
b Komposisi SKJ 1
Load beban = 4,21 kgf Lebar sampel = 15 mm
Tebal sampel = 3 mm Jarak Span = 0,1 m
Sehingga : Load beban P
= 4,21 kgf = 4,21 kgf x 9,8 ms
2
= 41,25 N 3PL = 3 x 41,25 N x 0,1 m
= 12,37 Nm 2bh
2
= 2 x 15 mm 3 mm
2
= 270 mm
3
= 0,27 x 10
-6
m
3
UFS =
Universitas Sumatera Utara
= = 45,81 MPa
b. Komposisi SKJ 2
Load beban = 5,06 kgf Lebar sampel = 15 mm
Tebal sampel = 3 mm Jarak Span = 0,1 m
Sehingga : Load beban P
= 5,06 kgf = 5,06 kgf x 9,8 ms
2
= 49,58 N
3PL = 3 x 49,58 N x 0,1 m = 14,87 Nm
2bh
2
= 2 x 15 mm 3 mm
2
= 270 mm
3
= 0,27 x 10
-6
m
3
UFS =
= 55,07 MPa
c. Komposisi SKJ 3
Load beban = 4,65 kgf Lebar sampel = 15 mm
Tebal sampel = 3 mm Jarak Span = 0,1 m
Sehingga : Load beban P
= 4,65 kgf = 4,65 kgf x 9,8 ms
2
= 45,57 N
Universitas Sumatera Utara
3PL = 3 x 45,57 N x 0,1 m = 13,67 Nm
2bh
2
= 2 x 15 mm 3 mm
2
= 270 mm
3
= 0,27 x 10
-6
m
3
UFS =
= 50,62 MPa
d. Komposisi SKJ 4
Load beban = 4,21 kgf Lebar sampel = 15 mm
Tebal sampel = 3 mm Jarak Span = 0,1 m
Sehingga : Load beban P
= 4,21 kgf = 4,21 kgf x 9,8 ms
2
= 41,25 N 3PL = 3 x 41,25 N x 0,1 m
= 12,37 2bh
2
= 2 x 15 mm 3 mm
2
= 270 mm
3
= 0,27 x 10
-6
m
3
UFS =
= 45,81 MPa
e. Komposisi SKJ 5
Load beban = 4,15 kgf Lebar sampel = 15 mm
Tebal sampel = 3 mm Jarak Span = 0,1 m
Sehingga : Load beban P
= 4,15 kgf
Universitas Sumatera Utara
= 4,1 5kgf x 9,8 ms
2
= 40,67 N
3PL = 3 x 40,67N x 0,1 m = 12,20 Nm
2bh
2
= 2 x 15 mm 3 mm
2
= 270 mm
3
= 0,27 x 10
-6
m
3
UFS =
= 45,18 MPa
6 Menghitung Kekuatan Impak Sampel Komposit SKJP
Nilai kekuatan Impak dapat dihitung dengan persamaan berikut :
Is
=
Dimana : Is = Kekuatan Impak
Es = Energi serap J A = Luas permukaan mm
2
a. Komposisi 0