DAFTAR ISI
Halaman HALAMAN JUDUL
i HALAMAN PENGESAHAN
ii HALAMAN PERSETUJUAN
iii PERNYATAAN
iv PENGHARGAAN
v ABSTRAK
vi ABSTRACT
vii DAFTAR ISI
viii DAFTAR GAMBAR
ix BAB I PENDAHULUAN
1.1 Latar Belakang
1 1.2
Rumusan Masalah 3
1.3 Batasan Masalah
3 1.4
Tujuan penelitian 4
1.5 Manfaat Penelitian
4 1.6
Sistematika Penulisan 4
BAB II TINJAUAN PUSTAKA 2.1 Gigi Tiruan
6 2.2 Basis Protesa
7 2.3 Elemen Gigi Resin Akrilik
8 2.4 Karakterisasi Resin Akrilik Polimerisasi Panas
15
2.5 Serat Kaca 18
BAB III METODOLOGI PENELITIAN 3.1.
Rancangan Penelitian 22
3.2. Tempat Penelitian
22 3.3.
Variabel Penelitian 22
3.4. Peralatan dan Bahan-Bahan
24 3.5
Tempat dan Waktu Penelitian 25
3.6 Diagram Alir
26
Universitas Sumatera Utara
3.7 Prosedur Penelitian
28 BAB IV HASIL DAN PEMBAHASAN
4.1 Densitas Density
34 4.2
Porositas Porosity 36
4.3 Kekuatan Tekan Compressive Strength
37 4.4
Kekerasan Vickers Vickers Hardness 38
4.5 Kekuatan Tarik Tensile Strength
40
BAB V KESIMPULAN DAN SARAN
5.1 Kesimpulan
42 5.2
Saran 43
DAFTAR PUSTAKA LAMPIRAN A
LAMPIRAN B
Universitas Sumatera Utara
DAFTAR GAMBAR
Halaman Gambar 2.1
Gigi Tiruan Lepasan 7
Gambar 2.2 Resin Akrilik
12 Gambar 2.3
Serat kaca potongan panjang akan dipotong menjadi 19
serta kaca potongan pendek. Gambar 4.1
Grafik hubungan densitas terhadap komposisi resin akrilik 35 polimerisasi panas
Gambar 4.2 Grafik hubungan porositas terhadap komposisi resin akrilik 37
polimerisasi panas. Gambar 4.3
Grafik hubungan Kekuatan tekan terhadap komposisi 38
Gambar 4.4 Grafik hubungan kekerasan Vickers terhadap Komposisi
40 Gambar 4.5
Grafik hubungaan antara kekuatan tarik terhadap komposisi 41
Universitas Sumatera Utara
PEMBUATAN DAN KARAKTERISASI GIGI TIRUAN BERBAHAN DASAR KOMPOSIT RESIN AKRILIK
NO.3 DENGAN PENAMBAHAN SERAT KACA
ABSTRAK
Resin akrilik biasanya digunakan sebagai bahan dasar pembuatan gigi tiruan, karena bersifat biocompatibel, flexibel, dan bahannya mudah diperoleh dan harganya murah.
Bahan ini mudah patah dan dapat menimbulkan pori akibat adanya penguapan monomer yang tidak bereaksi dengan polimer. Kelebihan bahan ini menyerupai gigi asli, sesuai
estetika dan dapat diperkuat dengan penambahan serat kaca. Pada penelitian ini dilakukan pembuatan gigi tiruan yang berbahan dasar resin akrilik polimerisasi panas
no.3 dengan penambahan variasi serat kaca. Resin akrilik yang dipilih no.3 karena warna dari resin ini sesuai dengan warna gigi asli manusia. Serat kaca fiberglass
adalah serat yang dapat ditambahkan ke dalam resin akrilik untuk memperbaiki sifat fisis dan mekanis resin akrilik. Penambahan serat kaca pada gigi tiruan ini berfungsi
meningkatkan sifat fisis dan mekanisnya serta dapat beradhesi dengan matriks polimer didalam resin akrilik sehingga memiliki kekuatan ikatan yang baik dengan resin akrilik,
oleh karena itu serat kaca menjadi pilihan untuk ditambahkan ke dalam resin akrilik sebagai bahan penguat. Komposisi resin akrilik, minyak gigi dan serat kaca dibuat
dengan perbandingan 10 gr : 4,5 mL : 0,13 gr yang merupakan perbandingan yang paling tepat untuk mendapatkan 3 buah sampel yang sesuai dengan model induk.
Ukuran panjang serat kaca yang digunakan adalah 4 mm, 6 mm, dan 8 mm sebagai variable bebas dari penelitian ini. Pengujian yang dilakukan yaitu, pengujian fisis yang
terdiri dari pengujian porositas dan densitas yang gunanya untuk mengetahui apakah gigi itu memiliki struktur yang baik yang mencakup susunan atom yang rapat atau
renggang ataupun kristal dan amorf. Pengujian mekanik yaitu, kuat tekan, kuat tarik dan kekerasan Vickers gunanya untuk mengetahui bagaimana kekuatan dari gigi tiruan
tersebut.. Dari hasil penelitian menunjukkan bahwa resin akrilik dengan penambahan serat kaca ukuran 6 mm merupakan kondisi optimum, dimana gigi tiruan merupakan
gigi yang baik untuk digunakan, dimana diperoleh : densitas 1,2256 gcm
3
, porositas 1,846 , kekuatan tekan 76,623 MPa, kekuatan tarik 71,207 MPa, dan kekerasan
Vickers 16,997 kgmm
2
. Kata kunci : Resin Akrilik, serat kaca, sifat fisis, sifat mekanis.
Universitas Sumatera Utara
MANUFACTURE AND CHARACTERIZATION OF A DENTURE MATERIALS BASED ON ACRYLIC RESIN COMPOSITE NO.3
WITH THE ADDITION OF GLASS FIBERS
ABSTRACT
Acrylic resins usually used as a base for the manufacture of artificial teeth, because it is biocompatibel, flexible, and easily available material and cheap. This material is brittle
and can cause pores due to evaporation of unreacted monomers to polymers. The advantages of this material resembles the original tooth, fit and aesthetics can be
strengthened with the addition of glass fibers. In this research, the manufacture of denture acrylic resin-based thermal polymerization no.3 with the addition of glass fiber
variation. Acrylic resin selected no.3 because of the color of the resin is in accordance with the color of human teeth. Glass fiber fiberglass is a fiber that can be added to the
acrylic resin to improve the physical and mechanical properties of acrylic resin. The addition of glass fibers in denture serves enchance physical and mechanical properties
and can adhesi with acrylic resin in the polymer matrix that has the power of a good bond with acrylic resin, glass fiber therefore be an option to be added to the acrylic resin
as reinforcing material. Acrylic resin composition, gear oil and fiber glass is made with a ratio of 10 g: 4.5 mL: 0.13 g which is the most appropriate comparison to get 3 pieces
of samples according to the model parent. Length of the glass fiber used was 4 mm, 6 mm, and 8 mm as the independent variable of the study. Tests were carried out ,
physical examination consisting of tests is density and porosity testing point to see if the tooth has a good structure that includes the arrangement of atoms or loose or dense
crystalline and amorphous. Namely mechanical testing, compressive strength, tensile strength and Vickers hardness point to know how the power of the denture . The results
showed that the addition of acrylic resin with glass fiber size 6 mm is the optimum condition, which is an artificial tooth gear to good use, which is obtained: density
1.2256 gcm
3
, porosity 1.846, compressive strength 76.623 MPa, tensile strength 71.207 MPa and Vickers hardness 16.997 kgmm
2
. Keywords: Acrylic resins, fiber glass, physical properties, mechanical properties.
Universitas Sumatera Utara
PEMBUATAN DAN KARAKTERISASI GIGI TIRUAN BERBAHAN DASAR KOMPOSIT RESIN AKRILIK
NO.3 DENGAN PENAMBAHAN SERAT KACA
ABSTRAK
Resin akrilik biasanya digunakan sebagai bahan dasar pembuatan gigi tiruan, karena bersifat biocompatibel, flexibel, dan bahannya mudah diperoleh dan harganya murah.
Bahan ini mudah patah dan dapat menimbulkan pori akibat adanya penguapan monomer yang tidak bereaksi dengan polimer. Kelebihan bahan ini menyerupai gigi asli, sesuai
estetika dan dapat diperkuat dengan penambahan serat kaca. Pada penelitian ini dilakukan pembuatan gigi tiruan yang berbahan dasar resin akrilik polimerisasi panas
no.3 dengan penambahan variasi serat kaca. Resin akrilik yang dipilih no.3 karena warna dari resin ini sesuai dengan warna gigi asli manusia. Serat kaca fiberglass
adalah serat yang dapat ditambahkan ke dalam resin akrilik untuk memperbaiki sifat fisis dan mekanis resin akrilik. Penambahan serat kaca pada gigi tiruan ini berfungsi
meningkatkan sifat fisis dan mekanisnya serta dapat beradhesi dengan matriks polimer didalam resin akrilik sehingga memiliki kekuatan ikatan yang baik dengan resin akrilik,
oleh karena itu serat kaca menjadi pilihan untuk ditambahkan ke dalam resin akrilik sebagai bahan penguat. Komposisi resin akrilik, minyak gigi dan serat kaca dibuat
dengan perbandingan 10 gr : 4,5 mL : 0,13 gr yang merupakan perbandingan yang paling tepat untuk mendapatkan 3 buah sampel yang sesuai dengan model induk.
Ukuran panjang serat kaca yang digunakan adalah 4 mm, 6 mm, dan 8 mm sebagai variable bebas dari penelitian ini. Pengujian yang dilakukan yaitu, pengujian fisis yang
terdiri dari pengujian porositas dan densitas yang gunanya untuk mengetahui apakah gigi itu memiliki struktur yang baik yang mencakup susunan atom yang rapat atau
renggang ataupun kristal dan amorf. Pengujian mekanik yaitu, kuat tekan, kuat tarik dan kekerasan Vickers gunanya untuk mengetahui bagaimana kekuatan dari gigi tiruan
tersebut.. Dari hasil penelitian menunjukkan bahwa resin akrilik dengan penambahan serat kaca ukuran 6 mm merupakan kondisi optimum, dimana gigi tiruan merupakan
gigi yang baik untuk digunakan, dimana diperoleh : densitas 1,2256 gcm
3
, porositas 1,846 , kekuatan tekan 76,623 MPa, kekuatan tarik 71,207 MPa, dan kekerasan
Vickers 16,997 kgmm
2
. Kata kunci : Resin Akrilik, serat kaca, sifat fisis, sifat mekanis.
Universitas Sumatera Utara
MANUFACTURE AND CHARACTERIZATION OF A DENTURE MATERIALS BASED ON ACRYLIC RESIN COMPOSITE NO.3
WITH THE ADDITION OF GLASS FIBERS
ABSTRACT
Acrylic resins usually used as a base for the manufacture of artificial teeth, because it is biocompatibel, flexible, and easily available material and cheap. This material is brittle
and can cause pores due to evaporation of unreacted monomers to polymers. The advantages of this material resembles the original tooth, fit and aesthetics can be
strengthened with the addition of glass fibers. In this research, the manufacture of denture acrylic resin-based thermal polymerization no.3 with the addition of glass fiber
variation. Acrylic resin selected no.3 because of the color of the resin is in accordance with the color of human teeth. Glass fiber fiberglass is a fiber that can be added to the
acrylic resin to improve the physical and mechanical properties of acrylic resin. The addition of glass fibers in denture serves enchance physical and mechanical properties
and can adhesi with acrylic resin in the polymer matrix that has the power of a good bond with acrylic resin, glass fiber therefore be an option to be added to the acrylic resin
as reinforcing material. Acrylic resin composition, gear oil and fiber glass is made with a ratio of 10 g: 4.5 mL: 0.13 g which is the most appropriate comparison to get 3 pieces
of samples according to the model parent. Length of the glass fiber used was 4 mm, 6 mm, and 8 mm as the independent variable of the study. Tests were carried out ,
physical examination consisting of tests is density and porosity testing point to see if the tooth has a good structure that includes the arrangement of atoms or loose or dense
crystalline and amorphous. Namely mechanical testing, compressive strength, tensile strength and Vickers hardness point to know how the power of the denture . The results
showed that the addition of acrylic resin with glass fiber size 6 mm is the optimum condition, which is an artificial tooth gear to good use, which is obtained: density
1.2256 gcm
3
, porosity 1.846, compressive strength 76.623 MPa, tensile strength 71.207 MPa and Vickers hardness 16.997 kgmm
2
. Keywords: Acrylic resins, fiber glass, physical properties, mechanical properties.